Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Polymer Property : Specific Heat Capacity = 0.120 BTU/lb-°F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Specific Heat Capacity 0.502 J/g-°C

@Temperature 650 °C
 0.120 BTU/lb-°F

@Temperature 1200 °F
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 4000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Specific Heat Capacity 0.502 J/g-°C

@Temperature 650 °C
 0.120 BTU/lb-°F

@Temperature 1200 °F
Haynes Hastelloy® S alloy, gas tungsten arc welded, aged at 538°C (1000°F) for 4000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Specific Heat Capacity 0.502 J/g-°C

@Temperature 650 °C
 0.120 BTU/lb-°F

@Temperature 1200 °F
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 4000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Specific Heat Capacity 0.502 J/g-°C

@Temperature 650 °C
 0.120 BTU/lb-°F

@Temperature 1200 °F
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 8000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Specific Heat Capacity 0.502 J/g-°C

@Temperature 650 °C
 0.120 BTU/lb-°F

@Temperature 1200 °F
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 8000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Specific Heat Capacity 0.504 J/g-°C

@Temperature 300 °C
 0.120 BTU/lb-°F

@Temperature 572 °F
Haynes Ultimet® alloy, 1.6 mm sheet
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Specific Heat Capacity 0.504 J/g-°C

@Temperature 300 °C
 0.120 BTU/lb-°F

@Temperature 572 °F
Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, SMAW weld
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Specific Heat Capacity 0.504 J/g-°C

@Temperature 300 °C
 0.120 BTU/lb-°F

@Temperature 572 °F
Haynes Ultimet® alloy, 12.7-50.8 mm bar
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Specific Heat Capacity 0.504 J/g-°C

@Temperature 300 °C
 0.120 BTU/lb-°F

@Temperature 572 °F
Haynes Ultimet® alloy, aged 1000 hours at 538°C (1000°F)
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Specific Heat Capacity 0.504 J/g-°C

@Temperature 300 °C
 0.120 BTU/lb-°F

@Temperature 572 °F
Haynes Ultimet® alloy, aged 1000 hours at 871°C (1600°F)
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Specific Heat Capacity 0.504 J/g-°C

@Temperature 300 °C
 0.120 BTU/lb-°F

@Temperature 572 °F
Haynes Ultimet® alloy, all-weld metal, GMAW weld (spray)
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Specific Heat Capacity 0.504 J/g-°C

@Temperature 300 °C
 0.120 BTU/lb-°F

@Temperature 572 °F
Haynes Ultimet® alloy, all-weld metal, SMAW weld
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Specific Heat Capacity 0.504 J/g-°C

@Temperature 300 °C
 0.120 BTU/lb-°F

@Temperature 572 °F
Haynes Ultimet® alloy, mill annealed
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Specific Heat Capacity 0.504 J/g-°C

@Temperature 600 °C
 0.120 BTU/lb-°F

@Temperature 1110 °F
Haynes Hastelloy® C-22HS™ Nickel Alloy Plate and Bar, Hot-rolled, Solution Annealed
Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Specific Heat Capacity 0.502 J/g-°C

@Temperature 400 °C
 0.120 BTU/lb-°F

@Temperature 752 °F
 hardened and tempered condition
Assab Steels ASP 30 Cold Work Steel
ASP 30 is a W-Mo-v-Co alloyed PM high speed steel characterized by:High wear resistanceHigh compressive strength at high hardnessGood through hardening propertiesGood toughnessGood dimensional stabi..
Specific Heat Capacity 0.502 J/g-°C

@Temperature 200 °C
 0.120 BTU/lb-°F

@Temperature 392 °F
QuesTek® Innovations Ferrium® S53® Corrosion Resistant High Strength Steel for Aerospace Structural Applications
Description: Ferrium® S53® is a corrosion resistant ultra high-strength steel for structural aerospace applications. Ferrium® S53® was designed to provide mechanical properties equal to, or bett..
Specific Heat Capacity 0.502 J/g-°C

@Temperature 650 °C
 0.120 BTU/lb-°F

@Temperature 1200 °F
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 1000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications ..
Copyright © lookpolymers.com All Rights Reserved