Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 24.1 W/m-K @Temperature 816 °C |
167 BTU-in/hr-ft²-°F @Temperature 1500 °F |
|
Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Thermal Conductivity | 24.1 W/m-K @Temperature 816 °C |
167 BTU-in/hr-ft²-°F @Temperature 1500 °F |
|
Haynes R-41 alloy, 0.635 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Thermal Conductivity | 24.1 W/m-K @Temperature 816 °C |
167 BTU-in/hr-ft²-°F @Temperature 1500 °F |
|
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Thermal Conductivity | 24.1 W/m-K @Temperature 816 °C |
167 BTU-in/hr-ft²-°F @Temperature 1500 °F |
|
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F) Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Thermal Conductivity | 24.1 W/m-K @Temperature 816 °C |
167 BTU-in/hr-ft²-°F @Temperature 1500 °F |
|
Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F) Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Thermal Conductivity | 24.0 W/m-K @Temperature 900 °C |
167 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
Haynes X-750 Nickel Alloy Sheet and Strip (AMS 5598, UNS N07750) Haynes X-750 (UNS No. N07750) alloy is an age-hardenable, nickel-base superalloy with very good strength at temperatures up to about 1600°F (870°C). It is widely used as a wrought material for.. |
|||
Thermal Conductivity | 24.0 W/m-K @Temperature 399 °C |
167 BTU-in/hr-ft²-°F @Temperature 750 °F |
hardened to 52 HRC |
Bohler-Uddeholm POLMAX® 420 Modified - Stainless Mold Steel Polmax is an excellent choice for extreme surface finish requirements. This high performance grade achieves surface finishes that go well beyond conventional tool steels. Polmax is specifically eng.. |
|||
Thermal Conductivity | 24.0 W/m-K @Temperature 200 °C |
167 BTU-in/hr-ft²-°F @Temperature 392 °F |
Hardened and tempered to 60-62 HRC |
Bohler-Uddeholm UDDEHOLM Caldie Plastic Mold Tool Steel Description: Uddeholm Caldie is a chromium-molybdenumvanadium alloyed tool steel.Uddeholm Caldie which is characterized by:Very good chipping and cracking resistanceGood wear resistanceHigh hardness.. |
|||
Thermal Conductivity | 24.0 W/m-K @Temperature 400 °C |
167 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Bohler-Uddeholm UDDEHOLM MIRRAX ESR Plastic Mold Steel Uddeholm Mirrax ESR is specially developed and adapted for larger molds that require corrosion resistance and/or high surface finish.It is characterized by:High hardenability for consistent properti.. |
|||
Thermal Conductivity | 24.0 W/m-K @Temperature 399 °C |
167 BTU-in/hr-ft²-°F @Temperature 750 °F |
hardened to 50 HRC |
Bohler-Uddeholm UDDEHOLM STAVAX® ESR Modified 420 Premium grade stainless tool steelStavax® ESR is characterized by: Good corrosion resistance Good polishability Good wear resistance Good machinability Good stability in hardeningApplications: Udd.. |
|||
Thermal Conductivity | 24.0 W/m-K @Temperature 600.0 °C |
167 BTU-in/hr-ft²-°F @Temperature 1112 °F |
hardened and tempered |
Bohler-Uddeholm UDDEHOLM VANADIS 60 Powder Metallurgically Produced Tool Steel Uddeholm Vanadis 60 is a high alloyed powder metallurgical high speed steel suitable for very demanding cold work applications and for cutting tools. The high carbon and alloying content, Co, Mo, W .. |
|||
Thermal Conductivity | 24.0 W/m-K @Temperature 800.0 °C |
167 BTU-in/hr-ft²-°F @Temperature 1472 °F |
|
AK Steel 13-4 SR® Ferritic Stainless Steel AK Steel 13-4 SR Stainless Steel is a ductile weldable ferritic with 13% Cr and 3.75% Al. The high aluminum content results in a base alloy with high electrical resistivity. It is intended for use w.. |
|||
Thermal Conductivity | 24.0 W/m-K @Temperature 600 °C |
167 BTU-in/hr-ft²-°F @Temperature 1110 °F |
hardened and tempered condition |
Assab Steels ASP 60 Cold Work Steel ASP 60 is a W-Mo-V-Co alloyed PM high speed steel characterized by:Highest wear resistanceMaximum compressive strengthGood through hardening propertiesGood toughnessGood dimensional stability on hea.. |
|||
Thermal Conductivity | 24.0 W/m-K @Temperature 20.0 °C |
167 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
|
Assab Steels ASP 23 Cold Work Steel ASP 23 is a chromium-molybdenum-tungsten-vanadium alloyed high speed steel which is characterized by:High wear resistance (abrasive profile)High compressive strengthVery good through-hardening prope.. |
|||
Thermal Conductivity | 24.1 W/m-K @Temperature 816 °C |
167 BTU-in/hr-ft²-°F @Temperature 1500 °F |
|
Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications include .. |
|||
Thermal Conductivity | 24.1 W/m-K @Temperature 400 °C |
167 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Schmolz + Bickenbach Formadur® 2316/2316 ESR Plastic Mold Steel Increased corrosion resistance in comparison to Formadur 2083, good polishability. Usually this grade is supplied quenched and tempered to 300 HBApplications: Molds for processing plastics with corr.. |