Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged at 649°C (1200°F) for 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes Hastelloy® S alloy, gas tungsten arc welded, aged at 538°C (1000°F) for 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes Hastelloy® S alloy, weld metal, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes Hastelloy® S alloy, weld metal, aged at 649°C (1200°F) for 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Thermal Conductivity | 28.0 W/m-K @Temperature 500 °C |
194 BTU-in/hr-ft²-°F @Temperature 932 °F |
Hot strip, Mean temp.; SINTEF |
Skamol Group SICAL 78 Silicon Nitride-Bonded Silicon Carbide Brick Silicon nitride-bonded silicon carbide brick has the following characteristics: Max. service temperature 1580°C (2876°F)For sidewall lining of aluminum reduction cellsHigh thermal conductivity.. |
|||
Thermal Conductivity | 28.0 W/m-K @Temperature 700 °C |
194 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
Bohler-Uddeholm BÖHLER M268 VMR® Plastic Mold Steel Description: HBÖHLER M268 VMR is a hardened and tempered plastic mould steel with excellent cleanliness for best polishability. The hardness is constant over the entire cross-section of the steel b.. |
|||
Thermal Conductivity | 28.0 W/m-K @Temperature 400 °C |
194 BTU-in/hr-ft²-°F @Temperature 752 °F |
Hardened and tempered to 60-62 HRC |
Bohler-Uddeholm UDDEHOLM Caldie Plastic Mold Tool Steel Description: Uddeholm Caldie is a chromium-molybdenumvanadium alloyed tool steel.Uddeholm Caldie which is characterized by:Very good chipping and cracking resistanceGood wear resistanceHigh hardness.. |
|||
Thermal Conductivity | 28.0 W/m-K @Temperature 400 °C |
194 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Assab Steels ASP 23 Cold Work Steel ASP 23 is a chromium-molybdenum-tungsten-vanadium alloyed high speed steel which is characterized by:High wear resistance (abrasive profile)High compressive strengthVery good through-hardening prope.. |
|||
Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
Thermal Conductivity | 28.0 W/m-K @Temperature 1000 °C |
194 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |