- Polymer Property : Thermal Conductivity = 26.1 W/m-K
Polymer Property : Thermal Conductivity = 26.1 W/m-K Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 26.1 W/m-K @Temperature 800 °C |
181 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 700 °C |
181 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 900 °C |
181 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 900 °C |
181 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 800 °C |
181 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 700 °C |
181 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 900 °C |
181 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 900 °C |
181 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 800 °C |
181 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 700 °C |
181 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 700 °C |
181 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged at 649°C (1200°F) for 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 700 °C |
181 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded, aged 1300 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 800 °C |
181 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded, aged 1300 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 900 °C |
181 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded, aged 1300 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 700 °C |
181 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded, aged at 538°C (1000°F) for 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 800 °C |
181 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded, aged at 538°C (1000°F) for 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 700 °C |
181 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 800 °C |
181 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 700 °C |
181 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 900 °C |
181 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 800 °C |
181 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 800 °C |
181 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 900 °C |
181 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes Hastelloy® S alloy, weld metal, aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 900 °C |
181 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes Hastelloy® S alloy, weld metal, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 20.0 °C |
181 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
|
| Latrobe LSSâ„¢ Chipper Knife Tool Steel (ASTM A8 Mod.) TLS Chipper Knife tool steel is an air-hardening, 8% chromium tool steel which exhibits very good wear resistance and toughness. TLS Chipper Knife exhibits wear resistance which is better than that.. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 800 °C |
181 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 700 °C |
181 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 900 °C |
181 BTU-in/hr-ft²-°F @Temperature 1650 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 700 °C |
181 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| Thermal Conductivity | 26.1 W/m-K @Temperature 700 °C |
181 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||