Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes Hastelloy® C-4 alloy, all-weld metal, as welded, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang.. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, aged 1000 hours at 649°C (1200°F) Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang.. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 25.0 °C |
128 BTU-in/hr-ft²-°F @Temperature 77.0 °F |
|
COI Ceramics Nicalon™ HI Type S SiC Ceramic Fiber Description: A stoichiometric beta-SiC fiber manufactured near-oxygen-free using decarbonization pyrolysis and electron-beam curing. It has higher modulus, creep resistance and oxidation resistance .. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, aged 10 hours at 649°C (1200°F) Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |
|||
Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |