Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 11.4 W/m-K @Temperature 100 °C |
79.1 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes Hastelloy® C-4 alloy, all-weld metal, as welded, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang.. |
|||
Thermal Conductivity | 11.4 W/m-K @Temperature 100 °C |
79.1 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, aged 1000 hours at 649°C (1200°F) Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang.. |
|||
Thermal Conductivity | 11.4 W/m-K @Temperature 93.0 °C |
79.1 BTU-in/hr-ft²-°F @Temperature 199 °F |
Annealed |
Special Metals INCONEL® alloy 783 Ni-Co-Fe Alloy The newest of the high-performance superalloys invented by Special Metals Corporation, INCONEL® alloy 783 (UNS R30783/US Patent 5,478,417), is an oxidation-resistant, low expansion, nickel-cobalt.. |
|||
Thermal Conductivity | 11.4 W/m-K @Temperature 100 °C |
79.1 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, aged 10 hours at 649°C (1200°F) Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |
|||
Thermal Conductivity | 11.4 W/m-K @Temperature 100 °C |
79.1 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |