Thermal Properties | Metric | English | Comments |
---|---|---|---|
Vicat Softening Point | 185 °C @Load 1.00 kg |
365 °F @Load 2.21 lb |
50°C/h; ISO 306 |
Polykemi AB SCANLON A 5005 PA/ABS-Blend Information provided by Polykemi AB |
|||
Vicat Softening Point | 185 °C @Load 1.00 kg |
365 °F @Load 2.21 lb |
50°C/h; ISO 306 |
Polykemi AB SCANLON A 5005B PA/ABS-Blend Information provided by Polykemi AB |
|||
Vicat Softening Point | 185 °C @Load 1.00 kg |
365 °F @Load 2.21 lb |
50°C/h; ISO 306 |
Polykemi AB SCANLON A 5005B UV PA/ABS-Blend Information provided by Polykemi AB |
|||
Vicat Softening Point | 185 °C @Load 0.999 kg |
365 °F @Load 2.20 lb |
50°C/hr; ISO 306 |
Cossa Polimeri ESTABLEND PA 1424 GF HI ABS / Nylon 6 Blend, 12% Glass Filled ESTABLEND PA is a blend of acrylonitrile butadiene styrene and polyamide 6.12% glass fiber reinforcedHigh impact strength, high chemical resistance, excellent heat resistance, high dimensional stabi.. |
|||
Vicat Softening Point | 185 °C @Load 5.10 kg |
365 °F @Load 11.2 lb |
cond.; ISO 306 |
Azoty Tarnow™ Tarnamid® T-27 MCS V0 Polyamide 6 - Flame Retarded, Unreinforced Flame retarded (class V0), bromine and red phosphorus free, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has th.. |
|||
Vicat Softening Point | 185 °C @Load 5.10 kg |
365 °F @Load 11.2 lb |
cond.; ISO 306 |
Azoty Tarnow™ Tarnamid® T-27 MCS V2 Polyamide 6 - Flame Retarded, Unreinforced Flame retarded (class V2), bromine and red phosphorus free, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has th.. |
|||
Vicat Softening Point | 185 °C @Load 5.10 kg |
365 °F @Load 11.2 lb |
cond.; ISO 306 |
Azoty Tarnow™ Tarnamid® T-27 MX6 Polyamide 6 - Flame Retarded, Reinforced Flame retarded grade, reinforced with 10% hybrid mineral-glass fibers, without addition of any halogen compounds, red phosphorus and asbestos, doesn't release any toxic gases during burning, good su.. |