Thermal Properties | Metric | English | Comments |
---|---|---|---|
Maximum Service Temperature, Air | 649 °C | 1200 °F | |
Palm Labs Adhesives Turbo Anti-Seize Aluminum Paste TURBO ANTI-SEIZE – ALUMINUM is a gray, viscous metallic paste which may be used on all bolts, studs, value shafts, value assemblies, transmission shafts, and other types of assembly work where prot.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | |
Palm Labs Adhesives Turbo Anti-Seize Copper Paste TURBO ANTI-SEIZE – COPPER is a copper, viscous metallic paste which may be used on all bolts, studs, value shafts, value assemblies, transmission shafts, and other types of assembly work where prot.. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | |
Pyrotek G-1 Low-Temperature Felt An inexpensive, tough material. Will not support combustion.Rolls:610 mm x 30.5 m 13 & 25 mm thickApplicationsHigh-temperature gasketsInformation provided by Pyrotek. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | |
Pyrotek G-2 Low-Temperature Felt An inexpensive tough material.Dimensions610 mm x 30.5 m 25 mm thickApplicationsHigh-temperature gasketsInformation provided by Pyrotek. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | Continuous |
Pyrotek IR-3 Fiber Seal Pre-cut Gasket A felt-like material which expands between 350°C and 540°C.Information provided by Pyrotek. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | |
Pyrotek IR-3 Low-Temperature Felt Felt-like material which expands between 350°C and 540°C.Custom Rolls:3 & 6 mm thickApplicationsCompressible gasketing Collector bar seals Siphon gaskets Flange gaskets Information provided by Pyr.. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | for Continuous use with standard cloth exterior |
Pyrotek MT-29P Microporous Panel Insulation MT-29P is a unique panel insulation which offers exceptionally low thermal conductivity. The exterior of the panel is a glass fabric which maximizes the strength of the rigid interior panel.Applica.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | Continuous use |
Pyrotek S-679 Dense Graphite Material Treated for Oxidation Resistance S-679 is an isostatically pressed graphite material that is treated to provide oxidation resistance at elevated temperatures. This material performs well in glass contact applications where heat an.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | Steam |
Garlock GRAPH-LOCK® 3123/3125 Graphite Sheet Gasketing A pure graphite sheet. Thicknesses |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | Steam |
Garlock GRAPH-LOCK® 3125SS Graphite Sheet Gasketing, Steel Foil Insert A laminated graphite sheet with a 316SS foil insert.Pure exfoliated graphite flake material excels in extreme conditions, withstanding heat, pressure, and aggressive chemicalsProven fire-safeSeals e.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | Steam |
Garlock GRAPH-LOCK® 3128 HOCHDRUCK® Graphite Sheet Gasketing, Steel Reinforced High performance multi-layer graphite with 316SS inserts provides high compressive strength, blow-out resistance, excellent handling properties and improved tightness.Pure exfoliated graphite flake .. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | for long term exposure |
Microtherm Group MT Thermosphere® Moldable Insulation Paste MT Thermosphere® is a low density temperature resistant paste with excellent thermal insulation properties from cryogenic to high temperature exposure. It is a perfectly seamless insulation syste.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | Upper limit of working range |
Heatbath/Park Alu-Braze 860 Aluminum Brazing Salt This is our premium aluminum dip braze salt. By proper chemical balance the lowest practical melt point has been developed with no sacrifices in fluidity or braze characteristics. Because of its sig.. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | resistance to low cycle and thermal fatigue |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 15% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 9.0. Other property values are typical of t.. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | resistance to low cycle and thermal fatigue |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 1950°F (1070°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 1950°F (1070°C)/5 minutes/AC. This produces ASTM grain size 9.5. Other property values are ty.. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | resistance to low cycle and thermal fatigue |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 1950°F (1070°C) + Aged 1400°F (760°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 1950°F (1070°C)/5 minutes/AC + Aged 1400°F (760°C)/100h/AC. This produces ASTM grain siz.. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | resistance to low cycle and thermal fatigue |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 2150°F (1180°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 2150°F (1180°C)/5 minutes/AC. This produces ASTM grain size 5.5. Other property values are ty.. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | resistance to low cycle and thermal fatigue |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 2150°F (1180°C) + Aged 1200°F (650°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 2150°F (1180°C)/5 minutes/AC + Aged 1200°F (650°C)/100h/AC. This produces ASTM grain siz.. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | |
Zircar Refractory Composites ZIRCAL-45 Refractory Board Type ZIRCAL-45 Refractory Board is a self supporting, high strength, rigid refractory product fabricated from calcium silicate, inert fillers and reinforcing agents. Its high structural strength com.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | |
Cotronics Resbond™ 950 High Temperature Ceramic Adhesive, Aluminum Composition |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | |
Dura-Bar 120-90-02 Continuously Cast Ductile Iron Bar Stock ASTM A536 Continuously cast ductile iron bar stock is produced in a wide variety of sizes and shapes, including rounds, rectangles and special shape cross sections.It often is used as a direct replacement for.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | |
Dura-Bar 65-45-12 Continuously Cast Ductile Iron Bar Stock ASTM A536 Continuously cast ductile iron bar stock is produced in a wide variety of sizes and shapes, including rounds, rectangles and special shape cross sections.It often is used as a direct replacement for.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | |
Dura-Bar 80-55-06 Continuously Cast Ductile Iron Bar Stock ASTM A536 Continuously cast ductile iron bar stock is produced in a wide variety of sizes and shapes, including rounds, rectangles and special shape cross sections.It often is used as a direct replacement for.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | |
Aremco Ceramabind™ 880 High Temperature Inorganic Binder High Temperature, water-dispersible silicone resin for producing corrosion and moisture resistant coatings and sealing porous ceramics. Cures at 450 °F in one hour. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | |
Aremco AREMCOLOX™ 502-1800 Machinable Aluminum Nitride Hot-pressed boron nitride – aluminum nitride composite that demonstrates high thermal conductivity, dielectric strength, and abrasion resistance. Readily machined and available in rods from 1/4” t.. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | |
Pyrotek O-1 Low-Temperature Felt Excellent resistance to vibration. Not effected by 1.55 MPa steam.Dimensions1524 mm x 22.9 m 6, 13, 25 mm thickApplicationsHigh-density gaskets at elevated temperatures Initial systems, high pressu.. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | |
Pyrotek S-1 Fabric Excellent mechanical strength and abrasion resistance. Low air permeability.Information provided by Pyrotek. |