Thermal Properties | Metric | English | Comments |
---|---|---|---|
Maximum Service Temperature, Air | 649 °C | 1200 °F | |
Palm Labs Adhesives Turbo Anti-Seize Copper Paste TURBO ANTI-SEIZE – COPPER is a copper, viscous metallic paste which may be used on all bolts, studs, value shafts, value assemblies, transmission shafts, and other types of assembly work where prot.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | |
Palm Labs Adhesives Turbo Anti-Seize Nickel Paste TURBO ANTI-SEIZE – NICKEL is a gray, viscous metallic paste which may be used on all bolts, studs, value shafts, value assemblies, transmission shafts, and other types of assembly work where protec.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | Continuous use |
Pyrotek S-679 Dense Graphite Material Treated for Oxidation Resistance S-679 is an isostatically pressed graphite material that is treated to provide oxidation resistance at elevated temperatures. This material performs well in glass contact applications where heat an.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | Steam |
Garlock GRAPH-LOCK® 3123/3125 Graphite Sheet Gasketing A pure graphite sheet. Thicknesses |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | Steam |
Garlock GRAPH-LOCK® 3124/3126 Graphite Sheet Gasketing, Steel Wire Insert A laminated graphite sheet with a 316SS wire mesh insert.Pure exfoliated graphite flake material excels in extreme conditions, withstanding heat, pressure, and aggressive chemicalsProven fire-safeSe.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | Steam |
Garlock GRAPH-LOCK® 3125SS Graphite Sheet Gasketing, Steel Foil Insert A laminated graphite sheet with a 316SS foil insert.Pure exfoliated graphite flake material excels in extreme conditions, withstanding heat, pressure, and aggressive chemicalsProven fire-safeSeals e.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | Steam |
Garlock GRAPH-LOCK® 3125TC Graphite Sheet Gasketing, Steel Insert A laminated graphite sheet with a 316SS tang insert.Pure exfoliated graphite flake material excels in extreme conditions, withstanding heat, pressure, and aggressive chemicalsProven fire-safeSeals e.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | Steam |
Garlock GRAPH-LOCK® 3128 HOCHDRUCK® Graphite Sheet Gasketing, Steel Reinforced High performance multi-layer graphite with 316SS inserts provides high compressive strength, blow-out resistance, excellent handling properties and improved tightness.Pure exfoliated graphite flake .. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | Upper limit of working range |
Heatbath/Park #90 Casing Salt for Liquid Nitriding An economical cyanide base salt which produces hard wear resistance properties for high speed tool steels in low dragout and/or low production use. It will maintain optimum operating characteristic.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | Upper limit of working range |
Heatbath/Park Alu-Braze 860 Aluminum Brazing Salt This is our premium aluminum dip braze salt. By proper chemical balance the lowest practical melt point has been developed with no sacrifices in fluidity or braze characteristics. Because of its sig.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | Upper limit of working range |
Heatbath/Park Alu-Braze 930 Aluminum Brazing Salt An improved salt having similar compositions but improved braze characteristics compared to Alu-Braze 960. The lower melt point offers good fluidity over a wider temperature and is ideally suited fo.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | |
Cotronics Resbond™ 950 High Temperature Ceramic Adhesive, Aluminum Composition |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | |
Dura-Bar 100-70-03 Continuously Cast Ductile Iron Bar Stock ASTM A536 Continuously cast ductile iron bar stock is produced in a wide variety of sizes and shapes, including rounds, rectangles and special shape cross sections.It often is used as a direct replacement for.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | |
Dura-Bar 60-40-18 Continuously Cast Ductile Iron Bar Stock ASTM A536, 4018 Continuously cast ductile iron bar stock is produced in a wide variety of sizes and shapes, including rounds, rectangles and special shape cross sections.It often is used as a direct replacement for.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | |
Dura-Bar 65-45-12 Continuously Cast Ductile Iron Bar Stock ASTM A536 Continuously cast ductile iron bar stock is produced in a wide variety of sizes and shapes, including rounds, rectangles and special shape cross sections.It often is used as a direct replacement for.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | Brittle behavior throughout temperature range |
Dura-Bar G2 Continuously Cast Gray Iron Bar Stock ASTM A48 Continuously cast ductile iron bar stock is produced in a wide variety of sizes and shapes, including rounds, rectangles and special shape cross sections.It often is used as an alternative to gray i.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | |
Aremco Ceramabind™ 880 High Temperature Inorganic Binder High Temperature, water-dispersible silicone resin for producing corrosion and moisture resistant coatings and sealing porous ceramics. Cures at 450 °F in one hour. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | |
Aremco AREMCOLOX™ 502-1800 Machinable Aluminum Nitride Hot-pressed boron nitride – aluminum nitride composite that demonstrates high thermal conductivity, dielectric strength, and abrasion resistance. Readily machined and available in rods from 1/4” t.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | |
Aremco Corr-Paint™ CP3015-AL High Temperature Protective Coating Inorganic, Mixed Oxides Filled These inorganic-ceramic, aqueous-based coatings provide outstanding resistance to thermal shock, oxidation and chemical corrosion in 1500°F. Aluminum-ceramic filled coating to 1200°F. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | Continuous |
Aremco Lamp-Coat™ LC4040-SG High Temperature Coating, Silicone White reflective coating for use on mercury vapor lamps and other high temperature glass and quartz components to 1200 ºF (649 ºC). |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | Upper limit of working range |
Heatbath/Park #90 Casing High Speed Hardening Salt An economical cyanide base salt which produces hard wear resistance properties for high speed tool steels in low dragout and/or low production use. It will maintain optimum operating characteristic.. |