Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 27.6 W/m-K @Temperature 1000 °C |
192 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes 188 alloy, 0% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 27.6 W/m-K @Temperature 1000 °C |
192 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 27.6 W/m-K @Temperature 1000 °C |
192 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 27.6 W/m-K @Temperature 1000 °C |
192 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 27.6 W/m-K @Temperature 1000 °C |
192 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 27.6 W/m-K @Temperature 1000 °C |
192 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 27.6 W/m-K @Temperature 1000 °C |
192 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 27.6 W/m-K @Temperature 1000 °C |
192 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 27.6 W/m-K @Temperature 1000 °C |
192 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 27.6 W/m-K @Temperature 1000 °C |
192 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 27.6 W/m-K @Temperature 1000 °C |
192 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 27.6 W/m-K @Temperature 1000 °C |
192 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 27.6 W/m-K @Temperature 1000 °C |
192 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 27.6 W/m-K @Temperature 1000 °C |
192 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 27.6 W/m-K @Temperature 1000 °C |
192 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 27.6 W/m-K @Temperature 1000 °C |
192 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes 188 alloy, plate at RT after 0 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 27.6 W/m-K @Temperature 1000 °C |
192 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes 188 alloy, plate at RT after 1000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 27.6 W/m-K @Temperature 1000 °C |
192 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes 188 alloy, plate at RT after 16000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 27.6 W/m-K @Temperature 1000 °C |
192 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes 188 alloy, plate at RT after 4000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 27.6 W/m-K @Temperature 1000 °C |
192 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes 188 alloy, plate at RT after 8000 hours at 650°C (1200°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 27.6 W/m-K @Temperature 1000 °C |
192 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes 188 alloy, plate at RT after 8000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 27.6 W/m-K @Temperature 1000 °C |
192 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 27.6 W/m-K @Temperature 1000 °C |
192 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 27.6 W/m-K @Temperature 1000 °C |
192 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
Haynes 188 alloy, plate at RT after 8000 hours at 760°C (1400°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 27.7 W/m-K | 192 BTU-in/hr-ft²-°F | |
SGL Carbon Group EK 204 Graphite Good mechanical strength, good sliding properties, high temperature resistance, high thermal shock resistance, low wettability, high corrosion resistance, high thermal conductivity, high purity, and.. |
|||
Thermal Conductivity | 27.7 W/m-K | 192 BTU-in/hr-ft²-°F | |
CeramTec 771 94% Alumina (Al2O3) Te value is 840°C. Hasselman Thermal Shock value is 200 K.Data provided by CeramTec North America. |