Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 24.8 W/m-K @Temperature 800 °C |
172 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 188 alloy, 0% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 24.8 W/m-K @Temperature 800 °C |
172 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 24.8 W/m-K @Temperature 800 °C |
172 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 24.8 W/m-K @Temperature 800 °C |
172 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 24.8 W/m-K @Temperature 800 °C |
172 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 24.8 W/m-K @Temperature 800 °C |
172 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 24.8 W/m-K @Temperature 800 °C |
172 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 24.8 W/m-K @Temperature 800 °C |
172 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 24.8 W/m-K @Temperature 800 °C |
172 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 24.8 W/m-K @Temperature 800 °C |
172 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 24.8 W/m-K @Temperature 800 °C |
172 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 24.8 W/m-K @Temperature 800 °C |
172 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 24.8 W/m-K @Temperature 800 °C |
172 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 24.8 W/m-K @Temperature 800 °C |
172 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 24.8 W/m-K @Temperature 800 °C |
172 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 24.8 W/m-K @Temperature 800 °C |
172 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 188 alloy, plate at RT after 0 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 24.8 W/m-K @Temperature 800 °C |
172 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 188 alloy, plate at RT after 1000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 24.8 W/m-K @Temperature 800 °C |
172 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 188 alloy, plate at RT after 16000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 24.8 W/m-K @Temperature 800 °C |
172 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 188 alloy, plate at RT after 4000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 24.8 W/m-K @Temperature 800 °C |
172 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 188 alloy, plate at RT after 8000 hours at 650°C (1200°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 24.8 W/m-K @Temperature 800 °C |
172 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 188 alloy, plate at RT after 8000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 24.8 W/m-K @Temperature 800 °C |
172 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 24.8 W/m-K @Temperature 800 °C |
172 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 24.8 W/m-K @Temperature 800 °C |
172 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 188 alloy, plate at RT after 8000 hours at 760°C (1400°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Thermal Conductivity | 24.8 W/m-K @Temperature 700 °C |
172 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
Haynes Hastelloy® C-2000® alloy, flat products Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |