Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 24.2 W/m-K @Temperature 800 °C |
168 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed, 20% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Thermal Conductivity | 24.2 W/m-K @Temperature 800 °C |
168 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 242® alloy Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Thermal Conductivity | 24.2 W/m-K @Temperature 800 °C |
168 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 242® alloy, after 1000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Thermal Conductivity | 24.2 W/m-K @Temperature 800 °C |
168 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 242® alloy, after 4000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Thermal Conductivity | 24.2 W/m-K @Temperature 800 °C |
168 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 242® alloy, after 8000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Thermal Conductivity | 24.2 W/m-K @Temperature 800 °C |
168 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Thermal Conductivity | 24.2 W/m-K @Temperature 800 °C |
168 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed and 20% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Thermal Conductivity | 24.2 W/m-K @Temperature 800 °C |
168 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed and 40% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Thermal Conductivity | 24.2 W/m-K @Temperature 800 °C |
168 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Thermal Conductivity | 24.2 W/m-K @Temperature 392 °C |
168 BTU-in/hr-ft²-°F @Temperature 738 °F |
|
Latrobe 14-4CrMo Stainless Tool Steel 14-4CrMo is a wear resistant, martensitic stainless tool steel that exhibits better corrosion resistance than Type 440C stainless steel. The molybdenum in the steel provides superior corrosion resis.. |
|||
Thermal Conductivity | 24.2 W/m-K | 168 BTU-in/hr-ft²-°F | |
SGL Carbon Group EK 40 Graphite Good mechanical strength, good sliding properties, high temperature resistance, high thermal shock resistance, low wettability, high corrosion resistance, high thermal conductivity, high purity, and.. |
|||
Thermal Conductivity | 24.2 W/m-K @Temperature 95.0 °C |
168 BTU-in/hr-ft²-°F @Temperature 203 °F |
|
Crucible Steel 154 CM Martensitic Steel Crucible 154 CM is a modification of 440C martensitic stainless steel to which molybdenum has been added. 154 CM has better corrosion resistance, better wear resistance and better hot-hardness than .. |
|||
Thermal Conductivity | 24.2 W/m-K @Temperature 93.3 °C |
168 BTU-in/hr-ft²-°F @Temperature 200 °F |
|
Crucible Steel 440A Chromium Steel Crucible 440A is a hardenable chromium steel which is the toughest of the high chromium cutlery grades. This grade is magnetic at all times. Information provided by Crucible Specialty Metals. |
|||
Thermal Conductivity | 24.2 W/m-K @Temperature 93.3 °C |
168 BTU-in/hr-ft²-°F @Temperature 200 °F |
|
Crucible Steel 440B Chromium Steel Crucible 440B Is a hardenable chromium steel which is cutlery grade having high attainable hardness and toughness. This grade is magnetic at all times. Information provided by Crucible Specialty Me.. |
|||
Thermal Conductivity | 24.2 W/m-K @Temperature 200 °C |
168 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Crucible Steel CPM® 3V® Tool Steel CPM 3V is a new tool steel made by the Crucible Particle Metallurgy process, designed to provide maximum resistance to breakage and chipping in a highly wear-resistant steel. CPM 3V offers impact to.. |
|||
Thermal Conductivity | 24.2 W/m-K | 168 BTU-in/hr-ft²-°F | |
Dura-Bar 80-55-06 Continuously Cast Ductile Iron Bar Stock ASTM A536 Continuously cast ductile iron bar stock is produced in a wide variety of sizes and shapes, including rounds, rectangles and special shape cross sections.It often is used as a direct replacement for.. |
|||
Thermal Conductivity | 24.2 W/m-K @Temperature 100 °C |
168 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
ATI Allegheny Ludlum 420 Martensitic Stainless Steel Characteristics: superior wear resistance, hardenable, excellent corrosion resistance. Applications:cutlery, dental and surgical instruments, nozzles, valve parts, hardened steel ball and seats for.. |
|||
Thermal Conductivity | 24.2 W/m-K @Temperature 100 °C |
168 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
ATI Allegheny Ludlum 425 Mod Martensitic Stainless Steel Characteristics: superior wear resistance, hardenable, excellent corrosion resistance. Applications:cutlery, dental and surgical instruments, nozzles, valve parts, hardened steel ball and seats for.. |
|||
Thermal Conductivity | 24.2 W/m-K @Temperature 100 °C |
168 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
ATI Allegheny Ludlum 440A Martensitic Stainless Steel Characteristics: superior wear resistance, hardenable, excellent corrosion resistance. Applications:cutlery, dental and surgical instruments, nozzles, valve parts, hardened steel ball and seats for.. |
|||
Thermal Conductivity | 24.2 W/m-K | 168 BTU-in/hr-ft²-°F | |
ATI Allegheny Ludlum Stainless Steel Type 439/AL 439HP™ (ASTM XM-8; UNS S43035) Allegheny Ludlum Stainless Steel Type 439, a titanium stabilized, 18 percent chromium alloy, also known as ASTM XM-8 and by the UNS designation S43035, is a ferritic stainless steel designed to resi.. |
|||
Thermal Conductivity | 24.2 W/m-K @Temperature 20.0 - 100 °C |
168 BTU-in/hr-ft²-°F @Temperature 68.0 - 212 °F |
|
ATI Allegheny Ludlum Stainless Steel Type 439/AL 439HP™ (ASTM XM-8; UNS S43035) Allegheny Ludlum Stainless Steel Type 439, a titanium stabilized, 18 percent chromium alloy, also known as ASTM XM-8 and by the UNS designation S43035, is a ferritic stainless steel designed to resi.. |
|||
Thermal Conductivity | 24.2 W/m-K | 168 BTU-in/hr-ft²-°F | |
ATI Allegheny Ludlum Stainless Steel Type 439/AL 439HP™, 10% cold work (ASTM XM-8; UNS S43035) Allegheny Ludlum Stainless Steel Type 439, a titanium stabilized, 18 percent chromium alloy, also known as ASTM XM-8 and by the UNS designation S43035, is a ferritic stainless steel designed to resi.. |
|||
Thermal Conductivity | 24.2 W/m-K @Temperature 20.0 - 100 °C |
168 BTU-in/hr-ft²-°F @Temperature 68.0 - 212 °F |
|
ATI Allegheny Ludlum Stainless Steel Type 439/AL 439HP™, 10% cold work (ASTM XM-8; UNS S43035) Allegheny Ludlum Stainless Steel Type 439, a titanium stabilized, 18 percent chromium alloy, also known as ASTM XM-8 and by the UNS designation S43035, is a ferritic stainless steel designed to resi.. |
|||
Thermal Conductivity | 24.2 W/m-K | 168 BTU-in/hr-ft²-°F | |
ATI Allegheny Ludlum Stainless Steel Type 439/AL 439HP™, 30% cold work (ASTM XM-8; UNS S43035) Allegheny Ludlum Stainless Steel Type 439, a titanium stabilized, 18 percent chromium alloy, also known as ASTM XM-8 and by the UNS designation S43035, is a ferritic stainless steel designed to resi.. |
|||
Thermal Conductivity | 24.2 W/m-K @Temperature 20.0 - 100 °C |
168 BTU-in/hr-ft²-°F @Temperature 68.0 - 212 °F |
|
ATI Allegheny Ludlum Stainless Steel Type 439/AL 439HP™, 30% cold work (ASTM XM-8; UNS S43035) Allegheny Ludlum Stainless Steel Type 439, a titanium stabilized, 18 percent chromium alloy, also known as ASTM XM-8 and by the UNS designation S43035, is a ferritic stainless steel designed to resi.. |
|||
Thermal Conductivity | 24.2 W/m-K | 168 BTU-in/hr-ft²-°F | |
ATI Allegheny Ludlum Stainless Steel Type 439/AL 439HP™, 70% cold work (ASTM XM-8; UNS S43035) Allegheny Ludlum Stainless Steel Type 439, a titanium stabilized, 18 percent chromium alloy, also known as ASTM XM-8 and by the UNS designation S43035, is a ferritic stainless steel designed to resi.. |
|||
Thermal Conductivity | 24.2 W/m-K @Temperature 20.0 - 100 °C |
168 BTU-in/hr-ft²-°F @Temperature 68.0 - 212 °F |
|
ATI Allegheny Ludlum Stainless Steel Type 439/AL 439HP™, 70% cold work (ASTM XM-8; UNS S43035) Allegheny Ludlum Stainless Steel Type 439, a titanium stabilized, 18 percent chromium alloy, also known as ASTM XM-8 and by the UNS designation S43035, is a ferritic stainless steel designed to resi.. |
|||
Thermal Conductivity | 24.2 W/m-K @Temperature 100 °C |
168 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
Latrobe LSS™ 440C Stainless Steel Knife (ASTM A276) TLS 440C Stainless Knife Steel is a high-carbon martensitic stainless steel which exhibits an attainable hardness of approximately 60 HRC. The high carbon content results in a hard matrix and numero.. |
|||
Thermal Conductivity | 24.2 W/m-K | 168 BTU-in/hr-ft²-°F | |
ATI Allegheny Ludlum Stainless Steel Type 439/AL 439HP™, 50% cold work (ASTM XM-8; UNS S43035) Allegheny Ludlum Stainless Steel Type 439, a titanium stabilized, 18 percent chromium alloy, also known as ASTM XM-8 and by the UNS designation S43035, is a ferritic stainless steel designed to resi.. |
|||
Thermal Conductivity | 24.2 W/m-K @Temperature 20.0 - 100 °C |
168 BTU-in/hr-ft²-°F @Temperature 68.0 - 212 °F |
|
ATI Allegheny Ludlum Stainless Steel Type 439/AL 439HP™, 50% cold work (ASTM XM-8; UNS S43035) Allegheny Ludlum Stainless Steel Type 439, a titanium stabilized, 18 percent chromium alloy, also known as ASTM XM-8 and by the UNS designation S43035, is a ferritic stainless steel designed to resi.. |