| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 18.5 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Outokumpu 353MA® High Temperature Austenitic Stainless Steel Alloy with higher nickel content than the other steels. Has increased silicon and nitrogen contents and is microalloyed with rare earth metals (REM). Max service temperature in air is 1150°C, but.. |
|||
| Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 214® alloy, 0% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 214® alloy, 10% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 214® alloy, 10% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 214® alloy, 10% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 214® alloy, 20% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 214® alloy, 30% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 214® alloy, 40% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 214® alloy, 40% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 214® alloy, 50% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 214® alloy, sheet, 100 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 214® alloy, sheet, 100 hours exposure at 870°C (1600°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 214® alloy, sheet, 100 hours exposure at 980°C (1800°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 214® alloy, sheet, 1000 hours exposure at 980°C (1800°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 214® alloy, sheet, 32 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 214® alloy, sheet, 32 hours exposure at 980°C (1800°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 230® alloy plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 230® alloy plate, 1000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 230® alloy, 10% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 230® alloy, 30% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 230® alloy, 40% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 230® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 230® alloy, plate, 1000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 18.4 W/m-K @Temperature 400 °C |
128 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 214® alloy, 30% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Thermal Conductivity | 18.5 - 20.2 W/m-K | 128 - 140 BTU-in/hr-ft²-°F | |
| China-Yixing Longly Refractories Tube SiC SiC tube made by our company have lots of superior performance, such as high refractoriness, good wear and corrosion resistance, hardness, strength, thermal conductivity, thermal shock stability, as.. |
|||
| Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 230® alloy, plate, 16000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Thermal Conductivity | 18.5 - 43.7 W/m-K @Temperature 85.0 - 85.0 °C |
128 - 303 BTU-in/hr-ft²-°F @Temperature 185 - 185 °F |
Average value: 31.1 W/m-K Grade Count:1 |
| Overview of materials for Vinyl Ester Sheet Molding Compound This property data is a summary of similar materials in the MatWeb database for the category "Vinyl Ester Sheet Molding Compound". Each property range of values reported is minimum and maximum value.. |
|||
| Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 230® alloy plate, 16000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 230® alloy plate, 8000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Thermal Conductivity | 18.4 W/m-K @Temperature 500 °C |
128 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 230® alloy, plate, 4000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||