Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 16.8 W/m-K @Temperature 400 °C |
117 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 25 alloy, cold worked sheet, 15% cold reduction, aged at 370°C (700°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 16.8 W/m-K @Temperature 400 °C |
117 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 370°C (700°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 16.8 W/m-K @Temperature 400 °C |
117 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 25 alloy, cold rolled and 1205°C (2200°F) solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 16.8 W/m-K @Temperature 400 °C |
117 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 25 alloy, cold worked sheet, 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 16.8 W/m-K @Temperature 400 °C |
117 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 25 alloy, cold worked sheet, 15 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 16.8 W/m-K @Temperature 400 °C |
117 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 25 alloy, room temperature after 20% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 16.8 W/m-K @Temperature 400 °C |
117 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 25 alloy, room temperature after 25% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 16.8 W/m-K @Temperature 400 °C |
117 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 25 alloy, room temperature after 25% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 16.8 W/m-K @Temperature 400 °C |
117 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 25 alloy, room temperature sheet after 2500 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 16.8 W/m-K @Temperature 400 °C |
117 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 25 alloy, room temperature sheet after 500 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 16.8 W/m-K @Temperature 400 °C |
117 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 25 alloy, vacuum investment castings, solution treated Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 625 alloy, 10% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 625 alloy, 20% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 625 alloy, 30% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 625 alloy, 40% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 625 alloy, 40% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 625 alloy, 50% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 625 alloy, plate after 16000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 625 alloy, plate after 4000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 625 alloy, plate after 8000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 625 alloy, plate after 8000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Thermal Conductivity | 16.8 W/m-K @Temperature 400 °C |
117 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 25 alloy, room temperature after 10% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Thermal Conductivity | 16.8 W/m-K @Temperature 400 °C |
117 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 25 alloy, room temperature after 10% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Thermal Conductivity | 16.8 W/m-K @Temperature 400 °C |
117 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 25 alloy, room temperature after 15% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Thermal Conductivity | 16.8 W/m-K @Temperature 400 °C |
117 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 25 alloy, room temperature after 20% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 625 alloy, 40% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
Thermal Conductivity | 16.8 W/m-K @Temperature 400 °C |
117 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes 25 alloy, room temperature after 15% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 625 alloy, 10% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
Thermal Conductivity | 16.9 W/m-K @Temperature 500 °C |
117 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Haynes 625 alloy, 40% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
Thermal Conductivity | 16.9 W/m-K @Temperature 50.0 °C |
117 BTU-in/hr-ft²-°F @Temperature 122 °F |
|
Special Metals INCOLOY® Alloy 903 A nickel-iron-cobalt alloy with additions of niobium, titanium, and aluminum for precipitation hardening. The alloy combines high strength with a low and constant coefficient of thermal expansion a.. |