Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 16.5 W/m-K @Temperature 400 °C |
115 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 538°C (1000°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
Thermal Conductivity | 16.5 W/m-K @Temperature 400 °C |
115 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 704°C (1300°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
Thermal Conductivity | 16.5 W/m-K @Temperature 400 °C |
115 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, welded and tested as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
Thermal Conductivity | 16.5 W/m-K @Temperature 400 °C |
115 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Hastelloy® N, weld metal as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
Thermal Conductivity | 16.5 W/m-K @Temperature 400 °C |
115 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Hastelloy® N, weld metal, aged 500 hours at 649°C (1200°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
Thermal Conductivity | 16.6 W/m-K @Temperature 20.0 °C |
115 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
|
Schmolz + Bickenbach LeanDupâ„¢ 35N Stainless Steel Bar Description: LeanDupâ„¢ 35N also known as (Uranus 35 N) is a dual phase austentic-ferritic stainless steel that has the ability to become as important as 316L. It offers better corrosion resistan.. |
|||
Thermal Conductivity | 16.6 - 17.8 W/m-K | 115 - 124 BTU-in/hr-ft²-°F | |
China-Yixing Longly Refractories Seggar SiC SiC series products of SiC shelf boards, SiC pillars, SiC slab, SiC seggar kiln furniture, are formed using high-quality silicon carbide materials and high temperature binders by tons of high-vibrat.. |
|||
Thermal Conductivity | 16.5 - 17.5 W/m-K | 115 - 121 BTU-in/hr-ft²-°F | |
China-Yixing Longly Refractories Slab SiC SiC series products of SiC shelf boards, SiC pillars, SiC slab, SiC seggar kiln furniture, are formed using high-quality silicon carbide materials and high temperature binders by tons of high-vibrat.. |
|||
Thermal Conductivity | 16.5 W/m-K @Temperature 400 °C |
115 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 593°C (1100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
Thermal Conductivity | 16.5 W/m-K @Temperature 400 °C |
115 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
Thermal Conductivity | 16.5 W/m-K @Temperature 400 °C |
115 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Hastelloy® N, 1.6 mm sheet, aged 128 hours at 815°C (1500°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
Thermal Conductivity | 16.5 W/m-K @Temperature 400 °C |
115 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, rapid air cooled Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
Thermal Conductivity | 16.5 W/m-K @Temperature 20.0 - 100 °C |
115 BTU-in/hr-ft²-°F @Temperature 68.0 - 212 °F |
DIN EN 821-2 |
CeramTec Rubalit® IS 95 Brown Alumina Rubalit® IS 95 brown is a high-performance alumina ceramic. Aluminas exhibit good mechanical properties such as hardness, compressive and tensile strength, and elastic modulus. They perform well at.. |
|||
Thermal Conductivity | 16.5 W/m-K @Temperature 400 °C |
115 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 649°C (1200°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
Thermal Conductivity | 16.5 W/m-K @Temperature 400 °C |
115 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, heat treated at 1149°C (2100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |