Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 31.1 W/m-K @Temperature 1100 °C |
216 BTU-in/hr-ft²-°F @Temperature 2010 °F |
|
Haynes HR-160® alloy plate, aged 1000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Thermal Conductivity | 31.1 W/m-K @Temperature 1100 °C |
216 BTU-in/hr-ft²-°F @Temperature 2010 °F |
|
Haynes HR-160® alloy plate, aged 4000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Thermal Conductivity | 31.1 W/m-K @Temperature 1100 °C |
216 BTU-in/hr-ft²-°F @Temperature 2010 °F |
|
Haynes HR-160® alloy, annealed plate Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Thermal Conductivity | 31.1 W/m-K @Temperature 1100 °C |
216 BTU-in/hr-ft²-°F @Temperature 2010 °F |
|
Haynes HR-160® alloy, plate, aged 1000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Thermal Conductivity | 31.1 W/m-K @Temperature 1100 °C |
216 BTU-in/hr-ft²-°F @Temperature 2010 °F |
|
Haynes HR-160® alloy, plate, aged 1000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Thermal Conductivity | 31.1 W/m-K @Temperature 1100 °C |
216 BTU-in/hr-ft²-°F @Temperature 2010 °F |
|
Haynes HR-160® alloy, plate, aged 4000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Thermal Conductivity | 31.1 W/m-K @Temperature 1100 °C |
216 BTU-in/hr-ft²-°F @Temperature 2010 °F |
|
Haynes HR-160® alloy, plate, aged 4000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Thermal Conductivity | 31.1 W/m-K @Temperature 1100 °C |
216 BTU-in/hr-ft²-°F @Temperature 2010 °F |
|
Haynes HR-160® alloy, plate, aged 8000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Thermal Conductivity | 31.1 W/m-K @Temperature 1100 °C |
216 BTU-in/hr-ft²-°F @Temperature 2010 °F |
|
Haynes HR-160® alloy, plate, aged 8000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Thermal Conductivity | 31.1 W/m-K @Temperature 1100 °C |
216 BTU-in/hr-ft²-°F @Temperature 2010 °F |
|
Haynes HR-160® alloy plate, aged 8000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Thermal Conductivity | 31.1 W/m-K | 216 BTU-in/hr-ft²-°F | |
Chicago Extruded Metals BioBrass® CXM10 Lead-Free Alloy Finished product available in rods.Chicago Extruded Metal temper code: H02This alloy is registered with the U.S. EPA as Antimicrobial.Information provided by Chicago Extruded Metals |