Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 22.2 W/m-K @Temperature 700 °C |
154 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
Haynes HR-120® alloy, solution heat-treated Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
Thermal Conductivity | 22.2 W/m-K @Temperature 700 °C |
154 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
Haynes HR-120® alloy, solution heat-treated aged at 1200°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
Thermal Conductivity | 22.2 W/m-K @Temperature 700 °C |
154 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
Haynes HR-120® alloy, solution heat-treated aged at 1400°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
Thermal Conductivity | 22.2 W/m-K @Temperature 700 °C |
154 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
Haynes HR-120® alloy, solution heat-treated aged at 1600°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
Thermal Conductivity | 22.2 W/m-K @Temperature 700 °C |
154 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
Haynes HR-120® alloy, solution heat-treated aged at 1800°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
Thermal Conductivity | 22.2 W/m-K @Temperature 700 °C |
154 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
Haynes 718 alloy, cold rolled, solution-treated and aged sheet Cb and Ta content combined weight percentage of 5. Excellent high-temperature strength up to 650°C, good ductility, formability, and weldability. Very good welding characteristics. Applications i.. |