Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 20.3 W/m-K @Temperature 600 °C |
141 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 538°C (1000°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
Thermal Conductivity | 20.3 W/m-K @Temperature 600 °C |
141 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 704°C (1300°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
Thermal Conductivity | 20.3 W/m-K @Temperature 600 °C |
141 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, welded and tested as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
Thermal Conductivity | 20.3 W/m-K @Temperature 600 °C |
141 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes Hastelloy® N, weld metal as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
Thermal Conductivity | 20.3 W/m-K @Temperature 600 °C |
141 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes Hastelloy® N, weld metal, aged 500 hours at 649°C (1200°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
Thermal Conductivity | 20.3 W/m-K | 141 BTU-in/hr-ft²-°F | |
Special Metals UDIMET® Alloy 250 Maraging Steel A high-strength, maraging steel of iron and nickel with additions of molybdenum and titanium. It has the strength of standard 18Ni (250) maraging steel but the advantages of containing less molybde.. |
|||
Thermal Conductivity | 20.3 W/m-K @Temperature 600 °C |
141 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 593°C (1100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
Thermal Conductivity | 20.3 W/m-K @Temperature 600 °C |
141 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
Thermal Conductivity | 20.3 W/m-K @Temperature 600 °C |
141 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes Hastelloy® N, 1.6 mm sheet, aged 128 hours at 815°C (1500°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
Thermal Conductivity | 20.3 W/m-K @Temperature 600 °C |
141 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, rapid air cooled Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
Thermal Conductivity | 20.3 W/m-K @Temperature 600 °C |
141 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 649°C (1200°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
Thermal Conductivity | 20.3 W/m-K @Temperature 600 °C |
141 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes Hastelloy® N, 1.14 mm sheet, heat treated at 1149°C (2100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
Thermal Conductivity | 20.3 W/m-K @Temperature 500 °C |
141 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Special Metals INCOLOY® Alloy 903 A nickel-iron-cobalt alloy with additions of niobium, titanium, and aluminum for precipitation hardening. The alloy combines high strength with a low and constant coefficient of thermal expansion a.. |