Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 2.20 W/m-K @Pressure 2.07 MPa |
15.3 BTU-in/hr-ft²-°F @Pressure 300 psi |
ASTM D5470 |
Parker Chomerics CHO-SEAL 1285 Conductive Elastomer Conductive Elastomer with Improved Corrosion Resistance. This conductive silicone elastomer features significantly improved corrosion resistance in salt spray environments over silver-plated copper-.. |
|||
Thermal Conductivity | 2.20 W/m-K | 15.3 BTU-in/hr-ft²-°F | ASTM E 1530 |
SABIC Innovative Plastics LNP KONDUIT OTF2AXXP PPS (Asia Pacific) LNP* Konduit* OTF2AXXP is a compound based on Polyphenylene Sulfide resin containing Glass Fiber, Thermal Carbon Fiber. Added features of this material include: Thermally Conductive, Electrically C.. |
|||
Thermal Conductivity | 2.20 W/m-K | 15.3 BTU-in/hr-ft²-°F | Along flow; ISO 22007-4 |
Victrex® WG101™ Polyaryletherketone Product Description: High performance thermoplastic material, PolyArylEtherKetone (PAEK), semi crystalline, black, granules for injection moulding, easy flow with wear additivesWG101 does not contai.. |
|||
Thermal Conductivity | 2.20 W/m-K | 15.3 BTU-in/hr-ft²-°F | Along flow; ISO 22007-4 |
Victrex® WG102™ Polyaryletherketone Product Description: High performance thermoplastic material, PolyArylEtherKetone (PAEK), semi crystalline, granules for injection moulding, standard flow, FDA food contact compliantWG102 does not c.. |
|||
Thermal Conductivity | 2.20 W/m-K | 15.3 BTU-in/hr-ft²-°F | ASTM C177 |
SABIC Innovative Plastics LNP KONDUIT PX11422 PA 6 LNP* KONDUIT* is a compound based on Nylon 6 resin containing thermally conductive fillers. Added feature of this material is Electrically Conductive. |
|||
Thermal Conductivity | 2.20 W/m-K | 15.3 BTU-in/hr-ft²-°F | |
MarkeTech Zirconium Oxide Ceramic - Zirconia, Y2O3 Stabilized Data provided by the supplier, MarkeTech International.Zirconium oxide is widely used and has superior high temperature properties. When combined with yttria the strength and fracture toughness is .. |
|||
Thermal Conductivity | 2.20 W/m-K | 15.3 BTU-in/hr-ft²-°F | |
MarkeTech Zirconium Oxide Ceramic, Zirconia MgO Stabilized Data provided by the supplier, MarkeTech International.Zirconium oxide is widely used and has superior high temperature properties. When combined with yttria the strength and fracture toughness is .. |
|||
Thermal Conductivity | 2.20 W/m-K | 15.3 BTU-in/hr-ft²-°F | |
ICE ZrO Data provided by the manufacturer, International Ceramic Engineering. |
|||
Thermal Conductivity | 2.20 W/m-K | 15.3 BTU-in/hr-ft²-°F | HOT-DISK || 60x60x3 mm |
Lehmann & Voss LUVOCOM® 1301-0825 PPS, linear, with carbon fiber Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.High-strength and stiff parts with low creep.Electrically conductive, suitable for continuous disc.. |
|||
Thermal Conductivity | 2.20 W/m-K | 15.3 BTU-in/hr-ft²-°F | ISO 22007-4 |
Sichuan Deyang Haton® hFR31 PPS / AR Polyphenylene Sulfide Injection molding, conductiveInformation provided by Sichuan Deyang Chemical Co., LTD |
|||
Thermal Conductivity | 2.20 W/m-K | 15.3 BTU-in/hr-ft²-°F | ribbon direction |
Ultracor® UCF-51-3/8-2.0 Honeycomb Core Material Construction: ±45° XN50. Fiber: Carbon XN50. Ultracor® is a very low density honeycomb core material designed for use in highly weight-sensitive structures. It is expected that it will be use.. |
|||
Thermal Conductivity | 2.20 W/m-K | 15.3 BTU-in/hr-ft²-°F | DIN EN 821-2 / ASTM-C408 |
CeramTec Sikor® S Cordierite Cordierites have low coefficients of thermal expansion and excellent resistance to thermal shock. They offer a range of thermal expansion, mechanical strength, and porosity criteria. They excel as c.. |
|||
Thermal Conductivity | 2.20 W/m-K | 15.3 BTU-in/hr-ft²-°F | ASTM C408 |
CoorsTek Dura-Z™ MgO Partially Stabilized Zirconia Thermal Shock Delta Tc = 350°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |
|||
Thermal Conductivity | 2.20 W/m-K | 15.3 BTU-in/hr-ft²-°F | ASTM C408 |
CoorsTek TTZ (Dura-Z™) MgO Partially Stabilized Zirconia Thermal Shock Delta Tc = 350°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |
|||
Thermal Conductivity | 2.20 W/m-K | 15.3 BTU-in/hr-ft²-°F | ASTM C408 |
CoorsTek Yttria Partially Stabilized Zirconia, YZTP, Sintered Thermal Shock Delta Tc = 350°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |
|||
Thermal Conductivity | 2.20 W/m-K | 15.3 BTU-in/hr-ft²-°F | ASTM C408 |
CoorsTek YZTP Yttria Partially Stabilized Zirconia, Hipped Thermal Shock Delta Tc = 350°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar.. |
|||
Thermal Conductivity | 2.20 W/m-K | 15.3 BTU-in/hr-ft²-°F | ASTM-C408 |
CoorsTek ZDY Yttria Fully Stabilized Zirconia Oxygen ionic conductor for high-stress and high-thermal-shock environments |
|||
Thermal Conductivity | 2.20 W/m-K | 15.3 BTU-in/hr-ft²-°F | |
Dow Corning SE 4448 CV KIT PARTS A&B Excellent thermal conductivity, low volatility (D4-D10 0.03% wt), heat cure, high viscosity.Information provided by Dow Corning |
|||
Thermal Conductivity | 2.20 - 2.50 W/m-K @Temperature 25.0 - 300 °C |
15.3 - 17.4 BTU-in/hr-ft²-°F @Temperature 77.0 - 572 °F |
|
China-Yixing Longly Refractories Steatite Ceramics (High Frequency Porcelain) LONGLY's steatite ceramics (namely high frequency porcelain, strengthened porcelain, magnesia porcelain), molecular formula as MgO-SiO2, is pure white. Steatite is the appropriate option when good .. |
|||
Thermal Conductivity | 2.20 W/m-K @Temperature 20.0 - 100 °C |
15.3 BTU-in/hr-ft²-°F @Temperature 68.0 - 212 °F |
|
Anderman Ceramics EZY 94 Zirconia, 94%, Yttria-Stabilized Dense impervious zirconia for high wear and aggressive engineering applications. Available in many shapes and sizes.Information provided by Anderman Ceramics. |
|||
Thermal Conductivity | 2.20 W/m-K | 15.3 BTU-in/hr-ft²-°F | |
Aremco AREMCOLOX™ 502-1900-MTTZ Dense MgO Partially Stabilized Zirconium Oxide This grade offers a high level of fracture toughness for a zirconia material. Features include excellent fracture, corrosion, thermal shock, and wear resistance. Used for pump parts, valve component.. |
|||
Thermal Conductivity | 2.20 W/m-K | 15.3 BTU-in/hr-ft²-°F | |
Aremco AREMCOLOX™ 502-1900-YTZP Dense Yttria Stabilized Zirconium Oxide This grade offers a high flexural strength for a zirconia. The fine grain size lends itself to be used in cutting tools where a very sharp edge can be achieved and maintained due to its high wear re.. |
|||
Thermal Conductivity | 2.20 W/m-K @Temperature 20.0 - 100 °C |
15.3 BTU-in/hr-ft²-°F @Temperature 68.0 - 212 °F |
|
Anderman Ceramics EZM 96 Zirconia, 96.5%, Magnesia-Stabilized Zirconia materials offer high temperature capability as well as excellent performance in areas of high wear and corrosion. Available in many shapes and sizes. |
|||
Thermal Conductivity | 2.20 W/m-K | 15.3 BTU-in/hr-ft²-°F | Tested in accordance with ASTM F433; ASTM C177 |
LNP Konduit® OTF-202-10 Polyphenylene Sulfide, Carbon Fiber Reinforcement
(discontinued **) Features: Electrically Conductive, Thermally ConductiveForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; h.. |