Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 12.9 W/m-K @Temperature 200 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 25 alloy, cold worked sheet, 15% cold reduction, aged at 370°C (700°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 12.9 W/m-K @Temperature 200 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 370°C (700°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 12.9 W/m-K @Temperature 200 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 595°C (1100°F) for 2 hours Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 12.9 W/m-K @Temperature 200 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 25 alloy, cold rolled and 1205°C (2200°F) solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 12.9 W/m-K @Temperature 200 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 25 alloy, cold worked sheet, 15 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 12.9 W/m-K @Temperature 200 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 25 alloy, room temperature after 20% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 12.9 W/m-K @Temperature 200 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 25 alloy, room temperature after 25% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 12.9 W/m-K @Temperature 200 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 25 alloy, room temperature after 25% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 12.9 W/m-K @Temperature 200 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 25 alloy, room temperature after 25% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 12.9 W/m-K @Temperature 200 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 25 alloy, room temperature sheet after 100 hours of 760°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 12.9 W/m-K @Temperature 200 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 25 alloy, room temperature sheet after 100 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 12.9 W/m-K @Temperature 200 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 25 alloy, room temperature sheet after 1000 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 12.9 W/m-K @Temperature 200 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 25 alloy, room temperature sheet after 1000 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 12.9 W/m-K @Temperature 200 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 25 alloy, room temperature sheet after 2500 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 12.9 W/m-K @Temperature 200 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 25 alloy, room temperature sheet after 500 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 12.9 W/m-K @Temperature 200 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 25 alloy, sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 12.9 W/m-K @Temperature 200 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 25 alloy, vacuum investment castings, solution treated Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Thermal Conductivity | 12.9 - 14.5 W/m-K | 89.5 - 101 BTU-in/hr-ft²-°F | Z (vertical) direction, as manufactured |
EOS PH1 Precipitation Hardening Stainless Steel for DMLS 3D Printing EOS Stainless Steel PH1 is a stainless steel powder which has been optimized especially for processing on EOSINT M 270 systems. This stainless steel prototyping material is tough and resistant to .. |
|||
Thermal Conductivity | 12.9 W/m-K @Temperature 20.0 - 50.0 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 68.0 - 122 °F |
|
ATI Allegheny Ludlum Stainless Steel 334 (UNS S33400) Allegheny Ludlum Type 334 is a titanium- and aluminum-bearing austenitic stainless steel offering superior elevated temperature scaling resistance compared to the conventional chromium-nickel stainl.. |
|||
Thermal Conductivity | 12.9 W/m-K @Temperature 200 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 25 alloy, room temperature after 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Thermal Conductivity | 12.9 W/m-K @Temperature 200 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 25 alloy, room temperature after 10% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Thermal Conductivity | 12.9 W/m-K @Temperature 200 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 25 alloy, room temperature after 10% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Thermal Conductivity | 12.9 W/m-K @Temperature 200 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 25 alloy, room temperature after 15% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Thermal Conductivity | 12.9 W/m-K @Temperature 200 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 25 alloy, room temperature after 15% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Thermal Conductivity | 12.9 W/m-K @Temperature 200 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 25 alloy, room temperature after 15% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Thermal Conductivity | 12.9 W/m-K @Temperature 200 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 25 alloy, room temperature after 20% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Thermal Conductivity | 12.9 W/m-K @Temperature 200 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 25 alloy, room temperature after 20% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Thermal Conductivity | 12.9 W/m-K @Temperature 200 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 25 alloy, room temperature after 20% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Thermal Conductivity | 12.9 W/m-K @Temperature 200 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 25 alloy, room temperature after 10% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Thermal Conductivity | 12.9 W/m-K @Temperature 200 °C |
89.5 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
Haynes 25 alloy, room temperature after 15% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |