- Polymer Property : Thermal Conductivity = 12.5 W/m-K
Polymer Property : Thermal Conductivity = 12.5 W/m-K Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 12.5 W/m-K @Temperature 200 °C |
86.8 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 625 alloy, 0% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 12.5 W/m-K @Temperature 200 °C |
86.8 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 12.5 W/m-K @Temperature 200 °C |
86.8 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 12.5 W/m-K @Temperature 200 °C |
86.8 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 12.5 W/m-K @Temperature 200 °C |
86.8 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 12.5 W/m-K @Temperature 200 °C |
86.8 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 625 alloy, hot rolled and 1050°C mill-annealed plate Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 12.5 W/m-K @Temperature 200 °C |
86.8 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 12.5 W/m-K @Temperature 200 °C |
86.8 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 12.5 W/m-K @Temperature 200 °C |
86.8 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
| Special Metals INCONEL® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, 3 Part Heat Treatment, 0.062 inch (1.57 mm) Thickness Tensile and bearing strengths (ultimate and yield) and elongation values reported here are typical for Cold Rolled Sheet, 3 Part Heat Treatment, 0.062 inch (1.57 mm) Thickness samples. Density and m.. |
|||
| Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
| Special Metals INCONEL® 706 Precipitation Hardening Alloy, Forged Disc, 2 Part Heat Treatment Tensile strength (ultimate and yield), reduction of area, and elongation values reported here are typical for Forged Disc, 2 Part Heat Treatment samples. Density and magnetic permeability are typica.. |
|||
| Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
| Special Metals INCONEL® 706 Precipitation Hardening Alloy, Hot Finished Flat, 2 Part Heat Treatment, 1.250 inch (31.8 mm) Thickness Tensile strength (ultimate and yield), shear strength, compressive strength, reduction of area, and elongation values reported here are typical for Hot Finished Flat, 2 Part Heat Treatment, 1.250 in.. |
|||
| Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
| Special Metals INCONEL® 706 Precipitation Hardening Alloy, Hot Finished Rod, 3 Part Heat Treatment, 0.562 inch (14.3 mm) Diameter Tensile strength (ultimate and yield), shear strength, reduction of area, and elongation values reported here are typical for Hot Finished Rod, 3 Part Heat Treatment, 0.562 inch (14.3 mm) Diameter s.. |
|||
| Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
| Special Metals INCONEL® 706 Precipitation Hardening Alloy, Hot Finished Rod, 3 Part Heat Treatment, 8.0 inch (203 mm) Diameter Tensile strength (ultimate and yield), compressive strength, reduction of area, and elongation values reported here are typical for Hot Finished Rod, 3 Part Heat Treatment, 8.0 inch (203 mm) Diamete.. |
|||
| Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
| Elgiloy® Co-Cr-Ni Alloy, Strip, 20% Cold Reduction The strength, elongation, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, fati.. |
|||
| Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
| Elgiloy® Co-Cr-Ni Alloy, Strip, 50% Cold Reduction The strength, elongation, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, fati.. |
|||
| Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
| Elgiloy® Co-Cr-Ni Alloy, Strip, 50% Cold Reduction, Heat Treated Heat Treatment 5 hours at 482°C. The strength, elongation, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High .. |
|||
| Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
| Elgiloy® Co-Cr-Ni Alloy, Strip, 65% Cold Reduction The strength, elongation, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, fati.. |
|||
| Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
| Elgiloy® Co-Cr-Ni Alloy, Strip, 85% Cold Reduction The strength, elongation, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, fati.. |
|||
| Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
| Elgiloy® Co-Cr-Ni Alloy, Strip, 85% Cold Reduction, Heat Treated Heat Treatment 5 hours at 482°C. The strength, elongation, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High .. |
|||
| Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
| Elgiloy® Co-Cr-Ni Alloy, Wire, 30% Cold Reduction The strength, shear modulus, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, f.. |
|||
| Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
| Elgiloy® Co-Cr-Ni Alloy, Wire, 40% Cold Reduction The strength, shear modulus, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, f.. |
|||
| Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
| Elgiloy® Co-Cr-Ni Alloy, Wire, 65% Cold Reduction The strength, shear modulus, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, f.. |
|||
| Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
| Elgiloy® Co-Cr-Ni Alloy, Wire, Heat Treated Heat Treatment 5 hours at 527°C. The strength and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, duc.. |
|||
| Thermal Conductivity | 12.5 W/m-K @Temperature 200 °C |
86.8 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
| Carpenter Glass Sealing "42-6" Alloy A nickel-chromium-iron which has been developed to match the thermal expansion characteristics of 0120 glass. An additional advantage of this alloy for glass-to-metals seals is the tight dark green.. |
|||
| Thermal Conductivity | 12.5 W/m-K @Temperature 200 °C |
86.8 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 625 alloy, 10% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Thermal Conductivity | 12.5 W/m-K @Temperature 200 °C |
86.8 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Thermal Conductivity | 12.5 W/m-K @Temperature 200 °C |
86.8 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 625 alloy, 40% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
| Special Metals INCONEL® 706 Precipitation Hardening Alloy, Hot Finished Rod, 2 Part Heat Treatment, 0.562 inch (14.3 mm) Diameter Tensile strength (ultimate and yield), shear strength, reduction of area, and elongation values reported here are typical for Hot Finished Rod, 2 Part Heat Treatment, 0.562 inch (14.3 mm) Diameter s.. |
|||