Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 0.900 W/m-K @Pressure 2.07 MPa |
6.25 BTU-in/hr-ft²-°F @Pressure 300 psi |
ASTM D5470 |
Parker Chomerics CHO-SEAL 1401 Conductive Elastomer High performance for non-corrosive environments; soft(45 Shore A) for low closure force where gasket geometry cannot be exploited; low tear strength; no fluid resistance. Molded and ExtrudedRoHS Com.. |
|||
Thermal Conductivity | 0.900 W/m-K @Pressure 2.07 MPa |
6.25 BTU-in/hr-ft²-°F @Pressure 300 psi |
ASTM D5470 |
Parker Chomerics CHO-SEAL 6370 Conductive Elastomer Commercial Grade Conductive Elastomer Extrusions. These materials offer excellent cost/performance characteristics for commercial EMI gasket applications. These silicone and fluorosilicone based con.. |
|||
Thermal Conductivity | 0.900 W/m-K @Pressure 2.07 MPa |
6.25 BTU-in/hr-ft²-°F @Pressure 300 psi |
ASTM D5470 |
Parker Chomerics CHO-SEAL® 6503 Conductive Elastomer Description: Highest performance in harsh environments; excellent shielding; best choice for corrosion requirements against aluminum.Molded and ExtrudedRoHS CompliantInformation provided by Chomeric.. |
|||
Thermal Conductivity | 0.900 - 1.10 W/m-K | 6.25 - 7.63 BTU-in/hr-ft²-°F | ASTM E1461 |
Raschig Group 2567 AMC Glass fiber-reinforced and inorganically filled polyester molding compound (UP) in various colors. Outstanding mechanical strength similar to BMC/SMC, very good electrical isolation properties and .. |
|||
Thermal Conductivity | 0.900 - 1.10 W/m-K | 6.25 - 7.63 BTU-in/hr-ft²-°F | ASTM E1461 |
Raschig Group 2568 AMC Glass fiber-reinforced polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, heat resistant up to 500°C for short time - usable for s.. |
|||
Thermal Conductivity | 0.900 - 1.10 W/m-K | 6.25 - 7.63 BTU-in/hr-ft²-°F | ASTM E1461 |
Raschig Group 5553 DAP Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona.. |
|||
Thermal Conductivity | 0.900 - 1.10 W/m-K | 6.25 - 7.63 BTU-in/hr-ft²-°F | ASTM E1461 |
Raschig Group 5562 DAP Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona.. |
|||
Thermal Conductivity | 0.900 - 1.10 W/m-K | 6.25 - 7.63 BTU-in/hr-ft²-°F | ASTM E1461 |
Raschig Group 5563 DAP Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona.. |
|||
Thermal Conductivity | 0.900 - 1.00 W/m-K | 6.25 - 6.94 BTU-in/hr-ft²-°F | ASTM E1461 |
Raschig Group RALUPOL® 2100 UP Polyester Organically and inorganically filled polyester molding compound. Low post-shrinkage, very good electrical values, good mechanical strength. This product meets the allowed upper limits for heavy meta.. |
|||
Thermal Conductivity | 0.900 - 1.10 W/m-K | 6.25 - 7.63 BTU-in/hr-ft²-°F | DIN 52 612 |
Raschig Group RALUPOL® 4385 UP Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, very high arc resistance, very high mechanical values. This product meets the allowed upper limits for heavy.. |
|||
Thermal Conductivity | 0.900 - 1.10 W/m-K | 6.25 - 7.63 BTU-in/hr-ft²-°F | ASTM E1461 |
Raschig Group RALUPOL® 4802 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, good electrical values, excellent heat resistance, outstanding pourability. This product meets the allowed u.. |
|||
Thermal Conductivity | 0.900 - 1.10 W/m-K | 6.25 - 7.63 BTU-in/hr-ft²-°F | DIN 52 612 |
Raschig Group RALUPOL® 4806 UP Glass-fiber reinforced polyester molding compound. Very low mold shrinkage and post-shrinkage, very good mechanical strength, very good electrical values, better performance values compared to UP 80.. |
|||
Thermal Conductivity | 0.900 W/m-K | 6.25 BTU-in/hr-ft²-°F | through-plane, ø80*3mm discs; ISO 22007-2 |
SABIC Innovative Plastics LNP KONDUIT OX11314 PPS (Asia Pacific) Thermally conductive mineral filled PPS FR compound |
|||
Thermal Conductivity | 0.900 W/m-K | 6.25 BTU-in/hr-ft²-°F | ASTM D5470 |
Parker Chomerics THERM-A-FORM T646 Cure-in-Place Potting and Underfill Material Description: THERM-A-FORM™ thermally conductive silicone elastomer products are dispensable form-in-place compounds designed for heat transfer without excessive compressive force in electronics co.. |
|||
Thermal Conductivity | 0.900 - 1.10 W/m-K | 6.25 - 7.63 BTU-in/hr-ft²-°F | ASTM E1461 |
Raschig Group RALUPOL® 802 UP Polyester Glass-fiber reinforced polyester molding compound. Low molding shrinkage and post-shrinkage, good electrical values, good mechanical strength, good heat resistance. This product meets the allowed up.. |
|||
Thermal Conductivity | 0.900 - 1.10 W/m-K | 6.25 - 7.63 BTU-in/hr-ft²-°F | ASTM E1461 |
Raschig Group RALUPOL® 804 UP Polyester Glass-fiber reinforced polyester molding compound. Low molding shrinkage and post-shrinkage, good electrical values, good mechanical strength. This product meets the allowed upper limits for heavy m.. |
|||
Thermal Conductivity | 0.900 W/m-K | 6.25 BTU-in/hr-ft²-°F | Longitudinal |
LATI Kelon® B FR H2 CEG/500-V0CT3 PA 6, Glass/Mineral Reinforced, Flame Retardant, Heat Stabilized Polyamide 6 (PA6) based compound. Heat stabilized. Glass fibers / Mineral filler. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE and antimony trioxide free. Low thermal expansion co.. |
|||
Thermal Conductivity | 0.900 W/m-K | 6.25 BTU-in/hr-ft²-°F | Longitudinal |
LATI Laticonther 80 GCE/650 PPS, Glass/Mineral Reinforced High thermal conductivity product based on Polyphenylene Sulfide (PPS). Glass fibers / Mineral filler.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformatio.. |
|||
Thermal Conductivity | 0.900 W/m-K @Temperature 90.0 °C |
6.25 BTU-in/hr-ft²-°F @Temperature 194 °F |
|
Schott Glass 8652 Sealing Glass Tungsten sealing glass, lower sealing temperature than glass 8651 Power diodesInformation provided by SCHOTT AG. |
|||
Thermal Conductivity | 0.900 W/m-K | 6.25 BTU-in/hr-ft²-°F | silicone property; Arlon SQA-TMS-022 |
Arlon Thermabond® 99180T010 Silicone Rubber/Fiberglass Laminate Low outgassing, thermally conductive, electrically insulating, Thermabond®. Bonds with primer. Liner: 1 mil FEP; Product: uncured silicone rubber; Carrier: 3 mil PTFE coated fiberglass. |
|||
Thermal Conductivity | 0.900 - 1.10 W/m-K | 6.25 - 7.63 BTU-in/hr-ft²-°F | ASTM E1461 |
Raschig Group 5567 DAP Diallyl Phthalate (DAP), Cast, Mineral Filler Glass-fiber reinforced diallyl phthalate molding compound free from halogens. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exc.. |
|||
Thermal Conductivity | 0.900 - 1.10 W/m-K | 6.25 - 7.63 BTU-in/hr-ft²-°F | ASTM E1461 |
Raschig Group RALUPOL® 8605 UP Polyester Glass fiber reinforced polyester molding compound. Resistant to hydrolysis. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU dire.. |