Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 48.6 µm/m-°C @Temperature -40.0 - 149 °C |
27.0 µin/in-°F @Temperature -40.0 - 300 °F |
ASTM E831 |
Quadrant EPP Ketron® CM HPV PEEK Polyetheretherketone; PTFE, Graphite, and Carbon Fiber Filled Bearing Grade, compression molded (ASTM Product Data Sheet) Excellent chemical resistance Very low moisture absorption Inherently good wear and abrasion resistance Unaffected by continuous exposure to hot water or steam |
|||
CTE, linear | 48.6 µm/m-°C @Temperature 20.0 °C |
27.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Ravago Manufacturing Americas Hylon® N1040MHL Nylon 6/6 (DAM) Information provided by Ravago. |
|||
CTE, linear | 48.6 - 100 µm/m-°C | 27.0 - 55.6 µin/in-°F | Average value: 77.2 µm/m-°C Grade Count:10 |
Overview of materials for Polypropylene with 30% Talc Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Talc Filler". Specific grades with primary filler content between 25% and 34% are.. |
|||
CTE, linear | 48.6 µm/m-°C | 27.0 µin/in-°F | ASTM D696 |
Ensinger Sintimid™ V-HPHT high purity high temp Polyimide (PI)
(discontinued **) SINTIMID™ V polyimide stock shapes provide a superior combination of high temperature and bearing and wear, properties that make it an idea choice for the most demanding applications. SINTIMID™ V.. |
|||
CTE, linear | 48.6 µm/m-°C @Temperature 20.0 °C |
27.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Ravago Manufacturing Americas Hylon® N1040ML Nylon 6/6 (DAM)
(discontinued **) Information provided by Ravago. |
|||
CTE, linear | 48.6 µm/m-°C @Temperature 20.0 °C |
27.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Techmer ES Plaslube® J-4/30/TF/13/SI/2 BK223 PA6/12 |
|||
CTE, linear | 48.6 µm/m-°C @Temperature 20.0 °C |
27.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Techmer ES Plaslube® J-4/30/TF/13/SI/2 NAT PA6/12 |
|||
CTE, linear | 48.6 µm/m-°C @Temperature 20.0 °C |
27.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Techmer ES Plaslube® J-4/35/TF/15 NAT PA6/12 |
|||
CTE, linear | 48.6 µm/m-°C @Temperature 23.9 - 260 °C |
27.0 µin/in-°F @Temperature 75.0 - 500 °F |
ASTM E831 |
Saint-Gobain Meldin® 7001 CM Compression Molded Polyimide Meldin® 7001 CM unfilled polyimide base resin, compression moldedSpecification Qualifications:Satisfies Type I P for ASTM D 6456-99: Standard Specification for Finished Parts Made from Polyimide .. |
|||
CTE, linear | 48.6 µm/m-°C @Temperature 20.0 °C |
27.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Westlake Plastics Polyethersulfone High resistance to heat and combustibility, low smoke emission, and transparency are the combination of properties possessed by stock shapes extruded from PES. These, coupled with light weight, good.. |
|||
CTE, linear | 48.6 µm/m-°C | 27.0 µin/in-°F | |
Trelleborg Emerson & Cuming EP551 Adhesive Clear unfilled adhesive for use with complete range.All information provided by Trelleborg Emerson & Cuming |
|||
CTE, linear | 48.6 µm/m-°C @Temperature 20.0 °C |
27.0 µin/in-°F @Temperature 68.0 °F |
|
Aremco Aremco-Bond™ 631 High Performance Epoxide Clear-Amber, 1:1, Good Bond Strength and Corrosion Resistance.Also available filled with aluminum oxide (Alumina) or pigments. |
|||
CTE, linear | 48.6 µm/m-°C @Temperature 20.0 °C |
27.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Asahi Kasei Thermylene® P-15FG-0860 15% Glass Fiber Reinforced, UV Stabilized Information provided by Asahi Thermofil |
|||
CTE, linear | 48.6 µm/m-°C @Temperature 20.0 °C |
27.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
PolyOne Lubri-Tech™ NI-30GF/15T Nylon 6/10 - 30% Glass Fiber Reinforced - 15% PTFE Lubricated
(discontinued * Data provided by PolyOne. |
|||
CTE, linear | 48.6 µm/m-°C @Temperature 20.0 °C |
27.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Asahi Kasei Thermofil N3-13FG-1626 13% Glass Fiber Reinforced, Heat Stabilized Information provided by Asahi Thermofil |