Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 18.0 µm/m-°C @Temperature -40.0 - 149 °C |
10.0 µin/in-°F @Temperature -40.0 - 300 °F |
ASTM E831 |
Quadrant EPP Ketron® CA30 LSG PEEK, Extruded 30% Carbon Fiber Reinforced Polyetherether Ketone (ASTM Product Data Sheet) |
|||
CTE, linear | 18.0 µm/m-°C @Temperature 20.0 °C |
10.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Covestro Petlon® 7530 Semi-Crystalline PET, 35% Mineral/Glass Fiber
(discontinued **) Characteristics: Excellent Electrical Properties, High Heat and Chemical ResistanceApplications: Automotive (Under Hood), Appliances, Casings and HousingsProcessing: Injection Molding (Melt Temperat.. |
|||
CTE, linear | 18.0 µm/m-°C @Temperature 100 °C |
10.0 µin/in-°F @Temperature 212 °F |
ASTM E-831 (TMA) |
Technetics Group Amicon™ PEEK 30% Carbon
(Unverified Data**) Information provided by Technetics Group (formerly Plastomer Technologies) |
|||
CTE, linear | 18.0 - 18.0 µm/m-°C @Temperature 100 - 100 °C |
10.0 - 10.0 µin/in-°F @Temperature 212 - 212 °F |
Average value: 18.0 µm/m-°C Grade Count:1 |
Overview of materials for Syndiotactic Polystyrene (SPS) with Glass or Carbon Fiber This property data is a summary of similar materials in the MatWeb database for the category "Syndiotactic Polystyrene (SPS) with Glass or Carbon Fiber". Each property range of values reported is mi.. |
|||
CTE, linear | 18.0 µm/m-°C | 10.0 µin/in-°F | ISO 11359-2 |
Solvay Specialty Polymers Ixef® 1002 Polyarylamide (PARA)
(Unverified Data**) Ixef 1002 is a 30% glass-fiber reinforced, general purpose polyarylamide compound which exhibits high strength and rigidity, outstanding surface finish, and excellent creep resistance. - Black: Ixef.. |
|||
CTE, linear | 18.0 - 140 µm/m-°C | 10.0 - 77.8 µin/in-°F | Average value: 63.7 µm/m-°C Grade Count:163 |
Overview of materials for PVC, Rigid Grade This property data is a summary of similar materials in the MatWeb database for the category "PVC, Rigid Grade". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
CTE, linear | 18.0 µm/m-°C @Temperature 20.0 - 200 °C |
10.0 µin/in-°F @Temperature 68.0 - 392 °F |
|
Materion Beryllium Copper Alloy 10 Rod and Bar; A (TB00) Temper; All Sizes (UNS C17500) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |
|||
CTE, linear | 18.0 µm/m-°C @Temperature 20.0 - 200 °C |
10.0 µin/in-°F @Temperature 68.0 - 392 °F |
|
Materion Beryllium Copper Alloy 10 Wire; H (TD04) Temper; 1.3-12.7 mm Diameter (UNS C17500) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |
|||
CTE, linear | 18.0 µm/m-°C @Temperature 20.0 - 200 °C |
10.0 µin/in-°F @Temperature 68.0 - 392 °F |
|
Materion Beryllium Copper Alloy 3 Forgings & Extrusions; A (TB00) Temper (UNS C17510) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |
|||
CTE, linear | 18.0 µm/m-°C @Temperature 20.0 - 200 °C |
10.0 µin/in-°F @Temperature 68.0 - 392 °F |
|
Materion Beryllium Copper Alloy 3 Plate & Rolled Bar; A (TB00) Temper; All Thicknesses (UNS C17510) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |
|||
CTE, linear | 18.0 µm/m-°C @Temperature 20.0 - 200 °C |
10.0 µin/in-°F @Temperature 68.0 - 392 °F |
|
Materion Beryllium Copper Alloy 3 Rod and Bar; H (TD04) Temper; up to 76 mm (UNS C17510) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |
|||
CTE, linear | 18.0 µm/m-°C @Temperature 21.1 - 204 °C |
10.0 µin/in-°F @Temperature 70.0 - 400 °F |
|
Materion BrushCAST® 165C High Strength Casting Alloy (As Cast) Pouring Temperature: 1010-1120°CHeat treatment required for max strength (Annealing): 760-790°C/water quenchHeat treatment required for max strength (Hardening): 760-790°C/water quenchDescr.. |
|||
CTE, linear | 18.0 µm/m-°C @Temperature 21.1 - 204 °C |
10.0 µin/in-°F @Temperature 70.0 - 400 °F |
|
Materion BrushCAST® 20C High Strength Casting Alloy (As Cast) Pouring Temperature: 1010-1120°CHeat treatment required for max strength (Annealing): 760-790°C/water quenchHeat treatment required for max strength (Hardening): 760-790°C/water quenchDescr.. |
|||
CTE, linear | 18.0 µm/m-°C @Temperature 21.1 - 204 °C |
10.0 µin/in-°F @Temperature 70.0 - 400 °F |
|
Materion BrushCAST® 3C High Conductivity Casting Alloy (As Cast) Pouring Temperature: 1095-1175°CHeat treatment required for max strength (Annealing): 870-900°C/water quenchHeat treatment required for max strength (Hardening): 870-900°C/water quenchDescr.. |
|||
CTE, linear | 18.0 µm/m-°C @Thickness 1.57 mm, Temperature 20.0 °C |
10.0 µin/in-°F @Thickness 0.0620 in, Temperature 68.0 °F |
x-axis; IPC-TM 650-2.4.24 |
Industrial Laminates/Norplex NP313 Cotton Fabric Description: Canvas phenolic laminate with molybdenum disulfide lubricant. Mechanical properties slightly lower than NP310.Thickness Tested: 0.062", 0.125" & 0.500" |
|||
CTE, linear | 18.0 µm/m-°C @Thickness 1.57 mm, Temperature 20.0 °C |
10.0 µin/in-°F @Thickness 0.0620 in, Temperature 68.0 °F |
x-axis; IPC-TM 650-2.4.24 |
Industrial Laminates/Norplex NP320E Cotton Fabric Description: Similar to NP320 with improved moisture resistance. Suitable for electrical applications in moderate humidity conditions.Thickness Tested: 0.062", 0.125", and 0.500†|
|||
CTE, linear | 18.0 µm/m-°C | 10.0 µin/in-°F | DIN 53752 |
Lehmann & Voss LUVOCOM® 1/CF/20/TF/5 Polyamide 66, with carbon fiber and PTFE, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Improved friction and wear beh.. |
|||
CTE, linear | 18.0 µm/m-°C @Temperature 20.0 - 200 °C |
10.0 µin/in-°F @Temperature 68.0 - 392 °F |
|
Materion Brush 1915™ AT Temper Wire Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: 3.5 hrs @ 370°CBrush 1915™ is Brush Wellman's new heat-treatable leaded copper alloy. Enginee.. |
|||
CTE, linear | 18.0 - 58.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
10.0 - 32.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
SABIC Innovative Plastics NORYL GTX APS430 PPE+PPS (Asia Pacific) PPE + PPS GF 30%, FR V-0 |
|||
CTE, linear | 18.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
10.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM E831 |
A. Schulman POLYPUR™ FPU 1156 Thermoplastic Polyurethane Information provided by A. Schulman. |
|||
CTE, linear | 18.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
10.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM E831 |
A. Schulman POLYPUR™ FPU 1156 Thermoplastic Polyurethane Information provided by A. Schulman. |
|||
CTE, linear | 18.0 µm/m-°C @Temperature 20.0 °C |
10.0 µin/in-°F @Temperature 68.0 °F |
|
Cotronics Resbond™ 954 High Temperature Ceramic Adhesive, Stainless Steel Composition |
|||
CTE, linear | 18.0 µm/m-°C | 10.0 µin/in-°F | |
Epoxyset Epoxibond EB-309 Low Expansion Epoxy Adhesive EB-309 is a highly filled, extremely low expansion, epoxy adhesive. This low out-gassing adhesive exhibits excellent wettability without preheating metal bonding surfaces and has a good dimensional .. |
|||
CTE, linear | 18.0 µm/m-°C @Temperature 20.0 - 50.0 °C |
10.0 µin/in-°F @Temperature 68.0 - 122 °F |
|
DuPont Teijin Films Melinex® ST505 Polyester Film, 700 Gauge Melinex® ST505 is a crystal clear, high gloss, heat stabilized polyester film. It is pretreated on both sides for improved adhesion. It can be overprinted with a wide range of solvent-based graphic.. |
|||
CTE, linear | 18.0 µm/m-°C @Temperature 100 °C |
10.0 µin/in-°F @Temperature 212 °F |
|
CMW® ELKALOY D130 Copper Alloy, Aluminum Bronze ELKALOY® D alloys are aluminum bronze type casting alloys. The sequence, ELKALOY® D, D110, D120, D130 materials represents increasing hardness and abrasion resistance but reduced electrical and th.. |
|||
CTE, linear | 18.0 µm/m-°C @Temperature 20.0 °C |
10.0 µin/in-°F @Temperature 68.0 °F |
DIN 53 752 |
Brandenburger S 5000 Ablation Material for Aeronautics and Space Aviation Information provided by Brandenburger Isoliertechnik GmbH&Co. |
|||
CTE, linear | 18.0 µm/m-°C @Temperature 20.0 - 200 °C |
10.0 µin/in-°F @Temperature 68.0 - 392 °F |
|
Materion Beryllium Copper Alloy 3 Wire; HT (TH04) Temper; 1.3-12.7 mm Diameter (UNS C17510) Treatment required for max strength: 2 hrs @ 480-495°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials .. |
|||
CTE, linear | 18.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
10.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM E831 |
A. Schulman POLYPUR™ FPU 1156 Thermoplastic Polyurethane Information provided by A. Schulman. |
|||
CTE, linear | 18.0 - 37.8 µm/m-°C | 10.0 - 21.0 µin/in-°F | Average value: 27.0 µm/m-°C Grade Count:5 |
Overview of materials for Polyphthalamide (PPA), Glass/PTFE This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide + Glass/PTFE". Each property range of values reported is minimum and maximum values of a.. |
|||
CTE, linear | 18.0 µm/m-°C @Temperature 20.0 - 200 °C |
10.0 µin/in-°F @Temperature 68.0 - 392 °F |
|
Materion Beryllium Copper Alloy 10 Forgings & Extrusions; AT (TF00) Temper (UNS C17500) Treatment required for max strength: 3 hrs @ 480°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc... |