Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 10.0 - 20.0 µm/m-°C @Temperature 50.0 - 100 °C |
5.56 - 11.1 µin/in-°F @Temperature 122 - 212 °F |
ISO 11359-2 |
Raschig Group 2567 AMC Glass fiber-reinforced and inorganically filled polyester molding compound (UP) in various colors. Outstanding mechanical strength similar to BMC/SMC, very good electrical isolation properties and .. |
|||
CTE, linear | 10.0 - 20.0 µm/m-°C @Temperature 50.0 - 100 °C |
5.56 - 11.1 µin/in-°F @Temperature 122 - 212 °F |
ISO 11359-2 |
Raschig Group 2568 AMC Glass fiber-reinforced polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, heat resistant up to 500°C for short time - usable for s.. |
|||
CTE, linear | 10.0 - 20.0 µm/m-°C @Temperature 50.0 - 100 °C |
5.56 - 11.1 µin/in-°F @Temperature 122 - 212 °F |
Injection; ISO 11359-2 |
Raschig Group 2572 AMC Glass fiber reinforced Polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, good abrasion stability, high flame retardance in combin.. |
|||
CTE, linear | 15.0 - 20.0 µm/m-°C @Temperature 50.0 - 150 °C |
8.33 - 11.1 µin/in-°F @Temperature 122 - 302 °F |
ISO 11359-2 |
Raschig Group 3505 Epoxy Glass-fiber reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. This product meets the allowed.. |
|||
CTE, linear | 15.0 - 20.0 µm/m-°C @Temperature 50.0 - 150 °C |
8.33 - 11.1 µin/in-°F @Temperature 122 - 302 °F |
ISO 11359-2 |
Raschig Group 3535 Epoxy Glass fiber-reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties adn dimensional stability even at high temperatures. Form: Low dust granulate pack.. |
|||
CTE, linear | 15.0 - 20.0 µm/m-°C @Temperature 50.0 - 150 °C |
8.33 - 11.1 µin/in-°F @Temperature 122 - 302 °F |
ISO 11359-2 |
Raschig Group 3536 Epoxy Glass-fiber reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. This product meets the allowed.. |
|||
CTE, linear | 15.0 - 20.0 µm/m-°C @Temperature 50.0 - 150 °C |
8.33 - 11.1 µin/in-°F @Temperature 122 - 302 °F |
ISO 11359-2 |
Raschig Group EPOXIDUR® 3582 EP Epoxy Glass-fiber reinforced and inorganically filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. Moldi.. |
|||
CTE, linear | 10.0 - 20.0 µm/m-°C @Temperature 50.0 - 100 °C |
5.56 - 11.1 µin/in-°F @Temperature 122 - 212 °F |
ISO 11359-2 |
Raschig Group RALUPOL® 4385 UP Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, very high arc resistance, very high mechanical values. This product meets the allowed upper limits for heavy.. |
|||
CTE, linear | 10.0 - 20.0 µm/m-°C @Temperature 50.0 - 100 °C |
5.56 - 11.1 µin/in-°F @Temperature 122 - 212 °F |
ISO 11359-2 |
Raschig Group RALUPOL® 4806 UP Glass-fiber reinforced polyester molding compound. Very low mold shrinkage and post-shrinkage, very good mechanical strength, very good electrical values, better performance values compared to UP 80.. |
|||
CTE, linear | 10.0 - 20.0 µm/m-°C @Temperature 50.0 - 100 °C |
5.56 - 11.1 µin/in-°F @Temperature 122 - 212 °F |
ISO 11359-2 |
Raschig Group RALUPOL® 8602 UP Glass-fiber reinforced polyester molding compound. Mold shrinkage similar to phenolic molding compounds, low post-shrinkage, good electrical values, excellent heat resistance, good mechanical streng.. |
|||
CTE, linear | -4.00 - 20.0 µm/m-°C @Temperature 55.0 - 260 °C |
-2.22 - 11.1 µin/in-°F @Temperature 131 - 500 °F |
Average value: 8.00 µm/m-°C Grade Count:3 |
Overview of materials for Liquid Crystal Polymer (LCP), Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), Mineral Filled". Each property range of values reported is minimum and max.. |
|||
CTE, linear | -4.00 - 20.0 µm/m-°C @Thickness 2.00 - 4.00 mm |
-2.22 - 11.1 µin/in-°F @Thickness 0.0787 - 0.157 in |
Average value: 8.00 µm/m-°C Grade Count:3 |
Overview of materials for Liquid Crystal Polymer (LCP), Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), Mineral Filled". Each property range of values reported is minimum and max.. |
|||
CTE, linear | 20.0 - 20.0 µm/m-°C @Temperature 100 - 200 °C |
11.1 - 11.1 µin/in-°F @Temperature 212 - 392 °F |
Average value: 20.0 µm/m-°C Grade Count:1 |
Overview of materials for Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler". Specific grades with glass content between 15%.. |
|||
CTE, linear | 12.6 - 20.0 µm/m-°C | 7.00 - 11.1 µin/in-°F | Average value: 17.1 µm/m-°C Grade Count:5 |
Overview of materials for Nylon 66/6, 60% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 60% Glass Fiber Reinforced". Specific grades with glass content between 55% and 64% are incl.. |
|||
CTE, linear | 15.0 - 20.0 µm/m-°C | 8.33 - 11.1 µin/in-°F | VDE 0304T1 |
Bulk Molding Compounds tetra-DUR F 4209 Bulk Molding Compound Highest Arc resistanceTypical Applications - Requiring mechanical strength, abrasion resistance, dimensional stability, electrical insulation, electrostatic dissipation (explosion protection), therm.. |
|||
CTE, linear | 16.2 - 20.0 µm/m-°C | 9.00 - 11.1 µin/in-°F | Average value: 18.3 µm/m-°C Grade Count:7 |
Overview of materials for Polycarbonate, 40% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 40% Glass Filled". Specific grades with glass content between 35% and 44% are included. E.. |
|||
CTE, linear | 20.0 - 20.0 µm/m-°C @Temperature 160 - 249 °C |
11.1 - 11.1 µin/in-°F @Temperature 320 - 480 °F |
Average value: 20.0 µm/m-°C Grade Count:1 |
Overview of materials for Polyphthalamide (PPA), 10% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 10% Glass Fiber Reinforced". Specific grades with glass content between 5% and 14% are .. |
|||
CTE, linear | 12.0 - 20.0 µm/m-°C | 6.67 - 11.1 µin/in-°F | VDE 0304T1 |
Bulk Molding Compounds tetra-DUR N 4203 Bulk Molding Compound Highest dimensional stability under temp. Low profile.Typical Applications - Requiring mechanical strength, abrasion resistance, dimensional stability, electrical insulation, electrostatic dissipat.. |