Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 40.0 - 130 µm/m-°C | 22.2 - 72.2 µin/in-°F | Average value: 99.8 µm/m-°C Grade Count:22 |
Overview of materials for Polybutylene Terephthalate (PBT), Extrusion Grade This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Extrusion Grade". Each property range of values reported is minimum an.. |
|||
CTE, linear | 0.920 - 130 µm/m-°C | 0.511 - 72.0 µin/in-°F | Average value: 102 µm/m-°C Grade Count:66 |
Overview of materials for Acetal Homopolymer, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Acetal Homopolymer, Unreinforced". Each property range of values reported is minimum and maximum values .. |
|||
CTE, linear | 100 - 130 µm/m-°C | 55.6 - 72.2 µin/in-°F | Average value: 120 µm/m-°C Grade Count:28 |
Overview of materials for Acetal Homopolymer, Unreinforced, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Acetal Homopolymer, Unreinforced, Impact Grade". Each property range of values reported is minimum and m.. |
|||
CTE, linear | 110 - 130 µm/m-°C @Temperature 20.0 °C |
61.1 - 72.2 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Kolon Kocetal® EC701 Modified Grade Acetal Copolymer
(discontinued **) Thermal properties: Kocetal has excellent heat stability; heat degradation is little under long term and high temperature application, compared to other POM. Maximum applicable temperature of produ.. |
|||
CTE, linear | 110 - 130 µm/m-°C @Temperature 20.0 °C |
61.1 - 72.2 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Kolon Kocetal® DP301 Modified Grade Acetal Copolymer
(discontinued **) Thermal properties: Kocetal has excellent heat stability; heat degradation is little under long term and high temperature application, compared to other POM. Maximum applicable temperature of produ.. |
|||
CTE, linear | 110 - 130 µm/m-°C @Temperature 20.0 °C |
61.1 - 72.2 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Kolon Kocetal® VT701 Modified Grade Acetal Copolymer
(discontinued **) Thermal properties: Kocetal has excellent heat stability; heat degradation is little under long term and high temperature application, compared to other POM. Maximum applicable temperature of produ.. |
|||
CTE, linear | 40.0 - 130 µm/m-°C | 22.2 - 72.2 µin/in-°F | Average value: 87.5 µm/m-°C Grade Count:15 |
Overview of materials for Ethylene Vinyl Alcohol (EVOH) This property data is a summary of similar materials in the MatWeb database for the category "Ethylene Vinyl Alcohol". Each property range of values reported is minimum and maximum values of appropr.. |
|||
CTE, linear | 110 - 130 µm/m-°C @Temperature 100 - 100 °C |
61.1 - 72.2 µin/in-°F @Temperature 212 - 212 °F |
Average value: 120 µm/m-°C Grade Count:3 |
Overview of materials for Ethylene Vinyl Alcohol (EVOH) This property data is a summary of similar materials in the MatWeb database for the category "Ethylene Vinyl Alcohol". Each property range of values reported is minimum and maximum values of appropr.. |
|||
CTE, linear | 70.0 - 130 µm/m-°C @Temperature 30.0 - 300 °C |
38.9 - 72.2 µin/in-°F @Temperature 86.0 - 572 °F |
Average value: 100 µm/m-°C Grade Count:2 |
Overview of materials for Polytetrafluoroethylene (PTFE), Bronze Filled This property data is a summary of similar materials in the MatWeb database for the category "Polytetrafluoroethylene (PTFE), Bronze Filled". Each property range of values reported is minimum and ma.. |
|||
CTE, linear | 94.0 - 130 µm/m-°C | 52.2 - 72.2 µin/in-°F | Average value: 108 µm/m-°C Grade Count:6 |
Overview of materials for Fluorocarbon ETFE/ECTFE, Molded/Extruded This property data is a summary of similar materials in the MatWeb database for the category "Fluorocarbon ETFE/ECTFE, Molded/Extruded". Each property range of values reported is minimum and maximum.. |
|||
CTE, linear | 20.0 - 130 µm/m-°C | 11.1 - 72.2 µin/in-°F | Average value: 57.4 µm/m-°C Grade Count:11 |
Overview of materials for Nylon 12, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, 20% Glass Fiber Filled". Specific grades with glass content between 15% and 24% are included. .. |
|||
CTE, linear | 110 - 130 µm/m-°C @Temperature 20.0 °C |
61.1 - 72.2 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Kolon Kocetal® K700 General Purpose Grade Acetal Copolymer Thermal properties: Kocetal has excellent heat stability; heat degradation is little under long term and high temperature application, compared to other POM. Maximum applicable temperature of produ.. |
|||
CTE, linear | 120 - 130 µm/m-°C | 66.7 - 72.2 µin/in-°F | ASTM D696 |
Guarniflon PTFE G400 Polytetrafluoroethylene A virgin PTFE with low coefficient of friction, excellent chemical inertness, non-adhesive surface, wide service temperature range, and excellent dielectric propertiesInformation provided by Guarnif.. |
|||
CTE, linear | 120 - 130 µm/m-°C | 66.7 - 72.2 µin/in-°F | ASTM D696 |
Guarniflon PTFE G415 Polytetrafluoroethylene 25% Soft Carbon PTFE G Standard Compound with carbon..Properties: Good thermal and electrical conductivity. Good resistance to deformation. Excellent resistance to load with low coefficient of friction and high .. |
|||
CTE, linear | 110 - 130 µm/m-°C | 61.1 - 72.2 µin/in-°F | |
Master Bond EP21TDC-4 Two Component, Highly Flexible Epoxy System Master Bond Polymer System EP21TDC-4 is a two component, flexible epoxy resin system for high performance bonding, sealing and coating. It is formulated to cure at ambient temperatures or more quick.. |
|||
CTE, linear | 110 - 130 µm/m-°C | 61.1 - 72.2 µin/in-°F | |
Master Bond EP21TDC-4ND Two component, highly flexibilized epoxy for bonding, sealing and coating Product Description: Master Bond EP21TDC-4ND is a two component, very flexible epoxy system for high performance bonding, sealing and coating with a non-drip consistency. It has a one to four mix ra.. |
|||
CTE, linear | 15.0 - 130 µm/m-°C @Temperature >=143 °C |
8.33 - 72.2 µin/in-°F @Temperature >=289 °F |
Average value: 66.2 µm/m-°C Grade Count:12 |
Overview of materials for Polyetheretherketone, Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, Glass Fiber Filled". Each property range of values reported is minimum and maximum.. |
|||
CTE, linear | 120 - 130 µm/m-°C | 66.7 - 72.2 µin/in-°F | ASTM D696 |
Guarniflon PTFE G412 Polytetrafluoroethylene 15% Graphite PTFE G Standard Compound with graphite.Properties: Extremely low coefficient of friction. Fairly good compressive strength. Enhanced chemical resistance. Good wear resistance. Good thermal diss.. |
|||
CTE, linear | 110 - 130 µm/m-°C | 61.1 - 72.2 µin/in-°F | ASTM D696 |
Guarniflon PTFE G403 Polytetrafluoroethylene 15% Glass Fiber PTFE G Standard Compound with glass fiberProperties: Enhanced wear resistance. Enhanced chemical resistance (except for alkali and hydrofluoric acid).Applications: Valve seats, seals, bearings, re.. |
|||
CTE, linear | 16.2 - 130 µm/m-°C | 9.00 - 72.2 µin/in-°F | Average value: 35.9 µm/m-°C Grade Count:17 |
Overview of materials for Polybutylene Terephthalate (PBT), Glass Filled, Impact Modified This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Glass Filled, Impact Modified". Each property range of values reported.. |