Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 17.7 µm/m-°C @Temperature 20.0 - 200 °C |
9.83 µin/in-°F @Temperature 68.0 - 392 °F |
|
Materion Brush 1915â„¢ Annealed Temper Rod Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: as suppliedBrush 1915â„¢ is Brush Wellman's new heat-treatable leaded copper alloy. Engineered spe.. |
|||
CTE, linear | 17.7 µm/m-°C @Temperature 20.0 - 200 °C |
9.83 µin/in-°F @Temperature 68.0 - 392 °F |
|
Materion Brush 1915â„¢ Hard Temper Rod, 0.050" - 0.375" Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: as suppliedBrush 1915â„¢ is Brush Wellman's new heat-treatable leaded copper alloy. Engineered spe.. |
|||
CTE, linear | 17.7 µm/m-°C @Temperature 20.0 - 200 °C |
9.83 µin/in-°F @Temperature 68.0 - 392 °F |
|
Materion Brush 1915™ AT Temper Rod Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: 3.5 hrs @ 370°C or Mill HardenedBrush 1915™ is Brush Wellman's new heat-treatable leaded coppe.. |
|||
CTE, linear | 17.7 µm/m-°C @Temperature 20.0 - 200 °C |
9.83 µin/in-°F @Temperature 68.0 - 392 °F |
|
Materion Brush 1915â„¢ Hard Temper Rod, 0.375" - 0.500" Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: as suppliedBrush 1915â„¢ is Brush Wellman's new heat-treatable leaded copper alloy. Engineered spe.. |
|||
CTE, linear | 17.7 µm/m-°C @Temperature 20.0 - 200 °C |
9.83 µin/in-°F @Temperature 68.0 - 392 °F |
|
Materion Brush 1915™ Heat Treated Temper Rod, 0.050" - 0.375" Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: 3.5 hrs @ 370°C or Mill HardenedBrush 1915™ is Brush Wellman's new heat-treatable leaded coppe.. |
|||
CTE, linear | 17.7 µm/m-°C @Temperature 20.0 - 200 °C |
9.83 µin/in-°F @Temperature 68.0 - 392 °F |
|
Materion Brush 1915™ Heat Treated Temper Rod, 0.375" - 0.500" Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: 3.5 hrs @ 370°C or Mill HardenedBrush 1915™ is Brush Wellman's new heat-treatable leaded coppe.. |