Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Strip General Elgiloy® information: High strength, ductility, fatigue life, and good mechanical properties. Corrosion resistant in numerous environments. Available in strip (currently 0.0015" to 0.075".. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Strip, 10% Cold Reduction The strength, elongation, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, fati.. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Strip, 20% Cold Reduction The strength, elongation, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, fati.. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Strip, 20% Cold Reduction, Heat Treated Heat Treatment 5 hours at 482°C. The strength, elongation, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High .. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Strip, 30% Cold Reduction The strength, elongation, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, fati.. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Strip, 40% Cold Reduction The strength, elongation, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, fati.. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Strip, 40% Cold Reduction, Heat Treated Heat Treatment 5 hours at 482°C. The strength, elongation, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High .. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Strip, 50% Cold Reduction The strength, elongation, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, fati.. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Strip, 50% Cold Reduction, Heat Treated Heat Treatment 5 hours at 482°C. The strength, elongation, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High .. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Strip, 65% Cold Reduction The strength, elongation, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, fati.. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Strip, 65% Cold Reduction, Heat Treated Heat Treatment 5 hours at 482°C. The strength, elongation, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High .. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Strip, 85% Cold Reduction The strength, elongation, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, fati.. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Strip, 85% Cold Reduction, Heat Treated Heat Treatment 5 hours at 482°C. The strength, elongation, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High .. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Strip, Heat Treated Heat Treatment 5 hours at 482°C. The strength and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, duc.. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Wire, 10% Cold Reduction The strength, shear modulus, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, f.. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Wire, 20% Cold Reduction, Heat Treated Heat Treatment 5 hours at 527°C. The strength, shear modulus, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: Hi.. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Wire, 30% Cold Reduction The strength, shear modulus, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, f.. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Wire, 30% Cold Reduction, Heat Treated Heat Treatment 5 hours at 527°C. The strength, shear modulus, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: Hi.. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Strip, 10% Cold Reduction, Heat Treated Heat Treatment 5 hours at 482°C. The strength, elongation, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High .. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Strip, 30% Cold Reduction, Heat Treated Heat Treatment 5 hours at 482°C. The strength, elongation, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High .. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Wire, 10% Cold Reduction, Heat Treated Heat Treatment 5 hours at 527°C. The strength, shear modulus, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: Hi.. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Wire, 20% Cold Reduction The strength, shear modulus, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, f.. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Wire, 40% Cold Reduction The strength, shear modulus, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, f.. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Wire, 40% Cold Reduction, Heat Treated Heat Treatment 5 hours at 527°C. The strength, shear modulus, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: Hi.. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Wire, 47% Cold Reduction (Coil Spring Range) 45-48% cold reduction is the normal coil spring range. The strength, shear modulus, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.Ge.. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Wire, 47% Cold Reduction (Coil Spring Range), Heat Treated Heat Treatment 5 hours at 527°C. 45-48% cold reduction is the normal coil spring range. The strength, shear modulus, and hardness values are specific to this heat treatment; other values below ar.. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Wire, 65% Cold Reduction The strength, shear modulus, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, f.. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Wire, 65% Cold Reduction, Heat Treated Heat Treatment 5 hours at 527°C. The strength, shear modulus, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: Hi.. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Wire, Heat Treated Heat Treatment 5 hours at 527°C. The strength and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, duc.. |
|||
CTE, linear | 15.17 µm/m-°C @Temperature 0.000 - 500 °C |
8.428 µin/in-°F @Temperature 32.0 - 932 °F |
|
Elgiloy® Co-Cr-Ni Alloy, Wire The strength and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, fatigue life, and.. |