Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 10.0 - 20.0 µm/m-°C @Temperature 50.0 - 100 °C |
5.56 - 11.1 µin/in-°F @Temperature 122 - 212 °F |
ISO 11359-2 |
Raschig Group 2567 AMC Glass fiber-reinforced and inorganically filled polyester molding compound (UP) in various colors. Outstanding mechanical strength similar to BMC/SMC, very good electrical isolation properties and .. |
|||
CTE, linear | 10.0 - 20.0 µm/m-°C @Temperature 50.0 - 100 °C |
5.56 - 11.1 µin/in-°F @Temperature 122 - 212 °F |
ISO 11359-2 |
Raschig Group RALUPOL® 4385 UP Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, very high arc resistance, very high mechanical values. This product meets the allowed upper limits for heavy.. |
|||
CTE, linear | 10.0 - 52.0 µm/m-°C @Temperature 100 - 200 °C |
5.56 - 28.9 µin/in-°F @Temperature 212 - 392 °F |
Average value: 31.0 µm/m-°C Grade Count:2 |
Overview of materials for Polyphenylene Sulfide (PPS) with 30% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 30% Glass Fiber Filler". Specific grades with glass content between 25%.. |
|||
CTE, linear | 10.0 - 100 µm/m-°C | 5.56 - 55.6 µin/in-°F | Average value: 63.3 µm/m-°C Grade Count:8 |
Overview of materials for Nylon 66, Extruded This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Extruded". Each property range of values reported is minimum and maximum values of appropriate.. |
|||
CTE, linear | 10.0 - 500 µm/m-°C | 5.56 - 278 µin/in-°F | Average value: 55.8 µm/m-°C Grade Count:37 |
Overview of materials for Nylon 66, Glass/Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass/Mineral Filled". Each property range of values reported is minimum and maximum values of.. |
|||
CTE, linear | 10.0 - 500 µm/m-°C | 5.56 - 278 µin/in-°F | Average value: 70.1 µm/m-°C Grade Count:46 |
Overview of materials for Nylon 612, Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Nylon 612, Glass Fiber Filler". Each property range of values reported is minimum and maximum values of .. |
|||
CTE, linear | 10.0 - 48.6 µm/m-°C | 5.56 - 27.0 µin/in-°F | Average value: 29.1 µm/m-°C Grade Count:7 |
Overview of materials for Nylon 12, Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, Carbon Fiber Filled". Each property range of values reported is minimum and maximum values of .. |
|||
CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | |
Mateck Lanthanum Aluminate Substrate, LaAlO3 rhombohedral Substrate single crystals for superconductivity |
|||
CTE, linear | 10.0 µm/m-°C @Temperature 20.0 °C |
5.56 µin/in-°F @Temperature 68.0 °F |
x-axis |
Industrial Laminates/Norplex ES-2 Engraving Stock Description: Composed of black phenolic paper core, sub surfaces of white melamine, and various pigmented cover plies. |
|||
CTE, linear | 10.0 µm/m-°C @Thickness 1.57 mm, Temperature 20.0 °C |
5.56 µin/in-°F @Thickness 0.0620 in, Temperature 68.0 °F |
x-axis; IPC-TM 650-2.4.24 |
Industrial Laminates/Norplex NP510A Glass Fabric Description: Woven glass fabric epoxy laminate. Engineered to provide NEMA grade FR-4 properties. This material contains bromine on the epoxy resin backbone. Certifiable to MIL-I-24768/27, Type GEE-.. |
|||
CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-2 |
Menzolit Menzolit® BMC 0200 Unsaturated Polyester UP BMC 0200 is a standard BMC for general purpose applications. The glass content is on a level that combines good mouldability with good strength and stiffness properties. Even without a specific fire.. |
|||
CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-2 |
Menzolit Menzolit® BMC 0800 Unsaturated Polyester UP BMC 0800 is a special SMC for applications within household and kitchenware. The glass level has been selected to combine good mould ability with good strength and stiffness properties. The product .. |
|||
CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-2 |
Menzolit Menzolit® BMC 1650 Unsaturated Polyester UP BMC 1650 is a specially designed anti-microbial polyester moulding compound which incorporates a "germ killer" . It has been tested and found to be compliant for resistance to fungal defacement in .. |
|||
CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-2 |
Menzolit Menzolit® BMC 2500 Unsaturated Polyester UP BMC 2500 is a special BMC for high voltage isolating applications. The glass content is set to a level that combines good mouldability with good strength and stiffness properties. The fire retardanc.. |
|||
CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-2 |
Menzolit Menzolit® SMC 0400 Unsaturated Polyester UP SMC 0400 is a Class-A SMC for exterior body applications on cars, LCV´s and trucks. These compounds mould to parts with good up to excellent surface quality for medium bake in-line and off-line p.. |
|||
CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-2 |
Menzolit Menzolit® BMC 0300 Unsaturated Polyester UP BMC 0300 is a low shrink standard material for general-purpose applications, which require a higher level on surface quality and better dimensional stability. The glass content is on a level that co.. |
|||
CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-2 |
Menzolit Menzolit® BMC 1400 Unsaturated Polyester UP BMC 1400 is a special BMC for the use on an engine. The glass content is set to a level that combines good mouldability with good strength and stiffness properties. The product has been developped f.. |
|||
CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-2 |
Menzolit Menzolit® BMC 2600 Unsaturated Polyester UP BMC 2600 is a special BMC with reduced electrical properties. The glass content is set to a level that combines good mouldability with good strength and stiffness properties. Because of its improved.. |
|||
CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-2 |
Menzolit Menzolit® BMC 3000 Unsaturated Polyester UP BMC 3000 is a special BMC suitable for the use in microwave and cookware applications.It has high temperature resistance, and meets requirements for food contact applications. It has a high gloss fi.. |
|||
CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-2 |
Menzolit Menzolit® SMC 2400 Unsaturated Polyester UP SMC 2400 is a SMC with fire retardancy. The glass level has been selected to combine mouldability with strength and stiffness properties. The fire retardancy is especially high, and the material is .. |
|||
CTE, linear | 10.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
5.56 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-2 |
Polyplastics Duracon® CH-20 Acetal Co-polymer (POM), Conductive, CF reinforced, Wear resistance DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O).. |
|||
CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | |
CoorsTek StatSafe™ ZDC-W Static Dissipative Zirconia Specialized StatSafe™ ESD-safe zirconia combines static-dissipation characteristics with the mechanical properties of advanced ceramics: tailorable volume resistivity, surface finish, high stiffne.. |
|||
CTE, linear | 10.0 µm/m-°C @Temperature 20.0 °C |
5.56 µin/in-°F @Temperature 68.0 °F |
Parallel DOM |
Alliance S-28B Samarium Cobalt Magnetic Material |
|||
CTE, linear | 10.0 µm/m-°C @Temperature 20.0 °C |
5.56 µin/in-°F @Temperature 68.0 °F |
Parallel DOM |
Alliance S-30A Samarium Cobalt Magnetic Material |
|||
CTE, linear | 10.0 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C |
5.56 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F |
ISO 11359-2 |
Ascend Performance Materials Vydyne® 21SPF Nylon 66, General Purpose, High Productivity, DAM Vydyne® 21SPF is general-purpose PA66 resin. Available in natural, it is designed principally for injection-molding fabrication. This grade offers a well-balanced combination of engineering propert.. |
|||
CTE, linear | 10.0 - 30.0 µm/m-°C @Temperature 20.0 °C |
5.56 - 16.7 µin/in-°F @Temperature 68.0 °F |
Parallel DOM |
Alliance BCN-12 Bonded (Composite) Magnetic Material |
|||
CTE, linear | 10.0 - 77.4 µm/m-°C @Temperature 37.8 - 150 °C |
5.56 - 43.0 µin/in-°F @Temperature 100 - 302 °F |
Average value: 33.3 µm/m-°C Grade Count:11 |
Overview of materials for Epoxy, Molded, Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Epoxy, Molded, Glass Fiber Filler". Each property range of values reported is minimum and maximum values.. |