Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 55.0 - 90.0 °C | 131 - 194 °F | Average value: 65.1 °C Grade Count:13 |
Overview of materials for PETG Copolyester This property data is a summary of similar materials in the MatWeb database for the category "PETG Copolyester". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 80.0 - 90.0 °C | 176 - 194 °F | TMA |
Solvay Specialty Polymers Hylar® 460 PVDF Polyvinylidene Fluoride
(discontinued **) Data provided by the manufacturer.Hylar® polymers have the characteristic stability of fluoropolymers combined with a unique polarity that influences its solubility and electrical properties. In a.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 85.0 - 90.0 °C | 185 - 194 °F | ASTM D648-98c |
DSM Somos® NanoTool™ Resin for Stereolithography, UV Postcure DescriptionNanoTool produces strong, stiff, high temperature resistant composite parts on conventional stereolithography machines. This third generation of Somos® ProtoComposite materials is heavi.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 80.0 - 90.0 °C | 176 - 194 °F | ASTM D648 |
Arkema Group KYNAR® 460 Polyvinylidene Fluoride Homopolymer - Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. Broad molecular weight distribution. High stability in harsh thermal, chemical and ultraviolet environments. High toughness a.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 80.0 - 90.0 °C | 176 - 194 °F | ASTM D648 |
Arkema Group KYNAR® 460 Red Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion Characteristics: Broad molecular weight distribution, pigmented. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeability, .. |