- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 338 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 338 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75 |
| Nilit FRIANYL B63 KV15 Nylon 6 for injection molding, 15% glass ball reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75 |
| Nilit FRIANYL B63 KV20 Nylon 6 for injection molding, 20% glass ball reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75 |
| Nilit FRIANYL B63 KV25 Nylon 6 for injection molding, 25% glass ball reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ASTM D648 |
| Ravago Manufacturing Americas Enviramid™ N2315HL Post Consumer Recycle Nylon 6, 15% Glass Filled Heat Stabilized, Lubricated, Black and made from EnViramid™ Post Consumer Recycled NylonInformation provided by Ravago. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Minlon® 10B140 BK061 Nylon 66
(Unverified Data**) Minlon® 10B140 BK061 is a 40% mineral reinforced, black polyamide 66 resin for injection molding. It has very low warpage.Information provided by DuPont Performance Polymers |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ASTM D648 |
| Plenco Valite 1246-18X Novolac Phenolic, Granular, Injection Molded
(discontinued **) This Valite product has been replaced by Plenco 4246. Data provided by Plenco.VALITE 1246-18X is a black two-stage, medium heat resistant phenolic molding compound. It has excellent electrical, mol.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75/Af |
| Solvay TECHNYL® C 52G1 V20 PA6, DRY Description: Halogen and Red Phosphorous free fire resistant polyamide PA6 Glass reinforced for injection molding of thin walled partsAvailable in: Asia Pacific, Europe, Latin America and North Amer.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Valox® VX5121 PBT (Europe-Africa-Middle East) VALOX VX5121 is a 15 % glass reinforced PBT+PC blend with low warpage characteristics.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP ZFM3314 PPE (Europe-Africa-Middle East) glas, mineral filled PPE |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C @Thickness 6.40 mm |
338 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL GTX GTX9400W PPE+PS+PA (Asia Pacific) High flow PPO+PA. Power distribution box applications. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C @Thickness 3.20 mm |
338 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL PX500 PPE (Asia Pacific) Noryl PX500 is an unfilled modified polyphenylene ether resin capable of multiple conversion routes. This resin is designed for lower odor during conversion than many standard modified PPE resins. .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | As Molded; ASTM D648A |
| Sumitomo Bakelite North America XB-22 Fiberglass Reinforced Phenolic Novolac XB-22 is a fiberglass reinforced phenolic novolac molding compound, with excellent dimensional stability and good strength at elevated temperatures. This material is formulated for low thermal condu.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75-93 |
| Wellman EcoLon® MR1660-BK1 Nylon 66, 40% Mineral Reinforced All information provided by Wellman Engineered Resins. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75-93 |
| Wellman Wellamid® GFT1699-WBK1 13% Glass Fiber Reinforced, Weatherable Black Nylon 66 Description: Glass Fiber Reinforced, Weatherable Black Nylon 66Information provided by Wellman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | DIN EN ISO 75 |
| Wolf Kunststoff ZEDEX® ZX-324V1T A3H PEEK Polymer, Reinforced Main Characteristics: High resilience; High elasticity; Low permanent deformation; Stress resistant; High strength at temperatures above 140 ° CApplications: Shipbuilding; Chemical Engineering; Aut.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | dry; ISO 75-1/-2 |
| DSM Akulon® K222-KGV4 /A PA6-GF20 FR(30) 20% Glass Reinforced, Heat Stabilized, Flame Retardant (Halogen-phosphorous-free) |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® LV-65H FWA black 9225 PA12-GF65 Product description: Grilamid LV-65H FWA black 9225 is a 65 % glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following special features: High stiffness combine.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® LV-65H FWA nat PA12-GF65 Product description: Grilamid LV-65H FWA natural is a 65 % glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following special features: High stiffness combined w.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Crastin® LW9020FR BK851 PBT+ASA
(Unverified Data**) 20% Glass Reinforced Flame Retardant Polybutylene Terephthalate Blend with Low Warpage Characteristics Crastin LW9020FR BK851 is a 20% glass fiber reinforced flame retardant black polybutylene tere.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| Eurostar Staramide AK8 PA66, 40% Mineral Reinforced, Injection Molding Staramide AK8 is a 40% Mineral Filled Polyamide 66, Injection Molding ResinInformation provided by Eurostar. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ASTM Test |
| BASF Ultramid® NBX-0025 NF2001 PA66 (Dry) Ultramid NBX-0025 NF2001 is a specialty, unfilled PA6/6. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75-2 |
| CENTROPLAST CENTRO HPM Polysulfone This plastic has good hydrolysis, chemical and radiation resistance, and can operate at high temperatures. It is used in food processing industry, pumps and valves, and medical equipment.Informatio.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C @Thickness 3.20 mm |
338 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP SF008 PA 12 (Asia Pacific) LNP* Thermocomp* SF008 is a compound based on Nylon 12 resin containing Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | |
| LATI Latilub 95-25GR CE/10 PSU, Mineral Fiber Reinforced, Graphite Filled Self-lubricating product based on Polysulfone (PSU). Graphite. Mineral filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Indu.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Crastin® LW9030 BK851 PBT
(Unverified Data**) Crastin® LW9030 BK851 is a 30% glass fiber reinforced, black polybutylene terephthalate alloy for injection molding. It has improved surface aesthetics, excellent dimensional stability and low warp.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75-1/-2 |
| Quadrant EPP Quadrant PSU unfilled, extruded (ISO Data) Quadrant 1000 PSU is a slightly yellow, translucent (non-optical quality) amorphous thermoplastic material, offering a combination of excellent mechanical, thermal and electrical properties. It ofte.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Valox® VX4915 ASA+PBT (Europe-Africa-Middle East) 15% Glass reinforced nucleated PBT/ASA with excellent mechanical properties high dimensional stability, and low density.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||