- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 280 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 280 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |
| RheTech Products GC20P100-00 15% Glass Fiber Reinforced Polypropylene, Chemically Coupled, Natural Applications: Air Ducts - distributionBracketsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |
| Polymer Resources PC-G10 Polycarbonate, 10% Glass Reinforced Polycarbonate, 10% Glass ReinforcedFeatures: • Flame Retardant • Self ExtinguishingProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-p.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C @Thickness 6.40 mm |
280 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® FL930 PC (Asia Pacific) Various weight reductions at 0.250"" (6.35 mm) wall, 30% GR. Superior flex strength/modulus, good tensile strength. V-0/5VA at 0.250"" (6.35 mm). |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP DFL349 PC LNP LUBRICOMP* DFL349 is a compound based on Polycarbonate resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Flame Retardant, Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP DFL42 PC LNP* Lubricomp* DFL-4042 a compound based on Polycarbonate resin containing 10% Glass Fiber, 20% PTFE. Added features include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |
| Fiberfil® J-60/10/FR Polypropylene Homopolymer, 10% Glass Reinforced, Flame Retardant Information provided by FIBERFIL Engineered Plastics |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON DC10EPFR PC LNP* STAT-KON* Lexan_DC10EPFR is a compound based on Polycarbonate containing Carbon Fiber. Added features of this grade include: Exceptional Processing, Flame Retardant, Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |
| Techmer ES Electrafil® DB-5/SS/10 Polycarbonate, 10% Stainless Steel Fiber (dry blend) |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON DE0049P PC (Asia Pacific) LNP* Stat-kon* DE0049P is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Exceptional Processing, Flame Retardant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GB36 IM1 36% Glass Bead Filler Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Bead, 36% Filler by WeightAdditive: Impact ModifierFeatures: Impact ModifiedInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | |
| Shinil Chemical SHINSTRA PP (SM400) Structural Polymer Household SHINSTRA is the product line of structural polymer compound which exhibits excellent physical, mechanical, and thermal properties. Shinil uses the state-of-the-art dispersion and blending technolog.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP MF741XXH PP LNP* THERMOCOMP* MF741XXH is a compound based on Polypropylene reain containing Glass Fiber and proprietay antimicrobial additives. Designed for touch surfaces in patient critical healthcare applic.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |
| Samyang Trirex® 3030U Polycarbonate, UV Stabilized TRIREX® polycarbonate resins offer superior transparency, mechanical properties, good dimensional stability and high electrical performance, which allows it to be widely used for electrical, elec.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C @Thickness 6.40 mm |
280 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL GFN2 PPE+HIPS (Asia Pacific) PPE+PS blend. 20% Glass reinforced. FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including pump.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL NH7112 PPE+HIPS Noryl* NH7112 resin is a 10% glass reinforced, modified PPE-PS blend. The material offers an exceptional balance of strength and dimensional stability while using non-halogenated flame retardants to.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® TPX-PBT-98010 BN069 Availability: North AmericaForms: PelletsFiller/Reinforcement: Unspecified Filler/ReinforFeatures: High DensityAppearance: Light BeigeProcessing Method: Injection MoldingInformation provided by TP C.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | annealed; ISO 75-A |
| Styron CALIBREâ„¢ 280-15 Polycarbonate CALIBREâ„¢ PC Utility Grade 280-15 is a high flow opaque polycarbonate with an internal mold release system. Applications: Internal parts Electrical Electronics Lightning Information provided b.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | Unannealed; ASTM Data |
| Styron CALIBRE™ 5201 15 Polycarbonate, 20% Glass Reinforced CALIBRE® 5201 is a 20% glass reinforced polycarbonate resin containing mold release for optimal processing. CALIBRE 5201 resin exhibits high modulus and excellent dimensional stability.CALIBRE 52.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | 0.157 in, annealed; ASTM D648 |
| Styron EMERGEâ„¢ 4510-10 Polycarbonate EMERGEâ„¢ PC 4510-10 advanced resin is a general purpose polycarbonate resin offering ignition resistance, heat resistance and excellent toughness. Applications: Consumer Electronics and Inform.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | Heat Distortion temperature |
| Cosmic Plastics 306 Orlon Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |
| A. Schulman SCHULADUR® A GB30 30% Glass Bead Reinforced PBT Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |
| Gromax CCP PBT 6730-104F Glass/Mineral Filled Product Description: PBT glass/mineral reinforced injection molding grade. Characteristics:Excellent electrical property Excellent mechanic and chemical property Excellent weatherability Excellent w.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |
| Ashley Polymers Ashlene® P1081 Polycarbonate A high viscosity resin for blow molding as well as injection molding heavy wall parts requiring maximum impact strength. Also available: P1083, same with UV stabilizer; P1081R, same with release; .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 138 - 288 °C | 280 - 550 °F | Average value: 260 °C Grade Count:23 |
| Overview of materials for Polyphthalamide (PPA), Glass/PTFE This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide + Glass/PTFE". Each property range of values reported is minimum and maximum values of a.. |
|||