- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 158 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 158 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C @Thickness 3.18 mm |
158 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Geon™ Vinyl Rigid Extrusion 87180 Polyvinyl Chloride, Rigid (PVC, Rigid) Note: NSF listings are obtained on specific colors. Contact PolyOne for the latest listing of approved colors for this product. Note: The Cell Classification was determined using the notched Izod te.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | STN EN ISO 75-2 (A) |
| Plastcom SLOVAMID® 6/66 FRC 3 TS PA6/66 flame retarded, heat stabilized PA 6 + PA 66 alloy for injection molding, reinforced with 30 % glass fiber, flame retarded with non halogen flame retardant, heat stabilized. Main features: flammability in accordance with UL 94 5 a.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PP CMX8030 VT Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Niche Polymer PA66MIN Nylon 66, Medium Impact Information provided by Niche Polymer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75 |
| Nilit FRIANYL A63 TF10 Nylon 6.6 for injection molding, 10% PTFE lubricated Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75 |
| Nilit FRIANYL B63 TF20 Nylon 6 for injection molding, 20% PTFE lubricated Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | DIN 53461 |
| Qualchem Danamid FEHUV Polyamide 6 Heat and UV stabilized, for long-lasting use at 120-130°C, protected against artificial lightInformation provided by Qualchem Zrt. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPH B8065 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® 103FHS BKB009 Nylon 66
(Unverified Data**) Zytel® 103FHS BKB009 is a heat stabilized, internally lubricated polyamide 66 resin for injection molding. It was developed for fast cycles and high productivity.Information provided by DuPont Perf.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 - 230 °C | 158 - 446 °F | Average value: 191 °C Grade Count:115 |
| Overview of materials for Nylon 6, Glass Fiber Filled, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Glass Fiber Filled, Flame Retardant". Each property range of values reported is minimum and max.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | |
| Malvern Minerals Nylon with Novakup® L-337 Silane-Treated Quartz Filler Product data demonstrates the effect of the Novakup® (lamellar quartz surface treated with A-1100) filler. A separate entry demonstrates the effect of untreated Novacite® filler in nylon. Th.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | |
| Lehmann & Voss LUVOCOM® 1/AR/5/NT Polyamide 66, with aramid reinforcement Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved wear behaviour, low warpage.Isotropic shrinkage characteristics.Control disks, cams, s.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C @Thickness 3.20 mm |
158 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL RN0401 PPE+PS (Asia Pacific) RN0401 is an unfilled Post Consumer Recycle (PCR) based injection moldable modified polyphenylene ether resin comprising at least 20% PCR styrenic series resin content. Available in black only. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Noryl V190 PPE+HIPS (Europe-Africa-Middle East) NORYL V190 is an unfilled flame retardant material with a Vicat B/120 of 90°C according ISO 306. NORYL V190 is V1 at 2.0 mm according UL94 and halogen free according VDE/DIN 472 part 815.This dat.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Valox® 359 PBT (Europe-Africa-Middle East) VALOX 359 is an unreinforced, flame retarded, low warpage PBT injection moulding resin. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-LOY A30009 ABS (Europe-Africa-Middle East) LNP* Stat-Loy* A30009 is a compound based on Acrylonitrile Butadiene resin, containing Proprietary Filler, Flame Retardant. Added features include : Permanent Antistatic, Flame retardant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ASTM Test |
| Styrolution Styrolux 684D SBC Styrolux 684D is a thermoplastic styrene-butadiene block copolymer which is suitable for injection molding, extrusion, and thermoforming. It offers an outstanding combination of crystal clarity and.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75-2 |
| Borealis Daplen™ EF341AE Polypropylene TPO Compound Daplen™ EF341AE is a 30% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has excellent balanced mechanical properties, gives a good surface q.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75-93 |
| Wellman Wellamid® NY1599-BK Unfilled Nylon 66 Description: Unfilled Nylon 66Information provided by Wellman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 MV3H Unreinforced Nylon 6/6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | 120°C/hr; ASTM D 648 |
| Cossa Polimeri ESTAPROP H 1080 T6 T D Polypropylene, 40% Mineral Filled PP homopolymer 40% mineral fillerGood physical and mechanical characteristics, high thermal stability, detergent resistanceInformation provided by Cossa Polimeri S.r.l. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® FG42A NC010 Nylon 66
(Unverified Data**) Unreinforced High Viscosity Polyamide 66 with Developed for Food Contact ApplicationsZytel FG42A NC010 is a high viscosity polyamide 66 resin for injection molding and extrusion. It has been develop.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| Eurostar Starpylen MX06023 PP, 20% Milled Glass Fiber Filled, Injection Molded Starpylen MX06023 is a 20% Milled Glass Fiber Reinforced Polypropylene Injection Molding ResinInformation provided by Eurostar. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Clariant Renol PA123 Nylon 66, Impact Modified, Heat Stabilized, Lubricated Data provided by Clariant Masterbatches |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75-1/2 |
| Eurotec® Tecomid® NA40 NL IL PA 6.6 impact modified Excellent stiffness/toughness balanceHigh mechanical strengthVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance and low frictionVery good.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | |
| BASF Procom® D 1189 Polypropylene Data was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75-1/-2 |
| DSM Akulon® S240-C Nylon 66 (European Grade) (Dry)
(discontinued **) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPHC K8030 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||