Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | 120°C/h; ISO 75/1 |
Polykemi AB POLYabs SN0 ABS Information provided by Polykemi AB |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | 120°C/h; ISO 75/1 |
Polykemi AB SCANCOMP PP BN140 T5 Polypropylene Information provided by Polykemi AB |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C @Thickness 3.20 mm |
151 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
SABIC Innovative Plastics LNP Konduit MT00EL PP LNP* Konduit* MT00EL is a Polypropylene base resin with thermal fillers. Characteristics of this grade are Thermal Conductivity and it is Low Extraactible.This data was supplied by SABIC-IP for th.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | |
Eastman Eastar DN101 PCTG Copolyester
(discontinued **) ISO data as provided by the manufacturer, Eastman Chemical |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | 120°C/h; ISO 75/1 |
Polykemi AB POLYfill PP CIP6015F VTUV Polypropylene, Mineral Reinforced, Heat and UV Stabilized Information provided by Polykemi AB |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 66.1 - 196 °C | 151 - 385 °F | Average value: 87.9 °C Grade Count:119 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant". Each property range of values rep.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | ASTM D648 |
Ineos Barex® 218 E Acrylonitrile-Methyl Acrylate Copolymer Extrusion Grade. Barex® Resins are available in either natural or blue tint. Barex® 218E is most commonly used for thermoformed sheet applications in which high impact performance is require.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 66.2 °C | 151 °F | unannealed; ASTM D648 |
KYDEX® XD MB 3D Laminate Thermoplastic 3D Laminate for Flat Lamination and Membrane Pressed Uses with Microban® Features:Tough and extremely durableResistant to cracking and chippingSolid, integral color4,000+ custom colorsResistant to a wide range of chemicalsAbrasion resistantFire retardantVery low moisture.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics NORYL WCV063 PPE+SEBS+Polyolefin (Asia Pacific) Flexible, non-halogenated FR, mPPE extrusion grade material for evaluation in automotive wire coating applications requiring ISO6722. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics NORYL WCV063 PPE+SEBS+Polyolefin (Europe-Africa-Middle East) Flexible, non-halogenated FR, mPPE extrusion grade material for evaluation in automotive wire coating applications requiring ISO6722. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP LUBRICOMP RX93237 PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RX93237 is a compound based on Nylon 66 resin containing PTFE, Silicone, MOS2. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | ASTM D 648 |
Shakespeare Isocorâ„¢ SVP6100 Nylon 610 Isocorâ„¢ 6100 is a medium viscosity PA-610. This resin is specifically suited for applications requiring low moisture absorption and greater dimensional stability. Isocorâ„¢ 6100 is also u.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C @Thickness 3.20 mm |
151 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP STAT-KON KEP33 Acetal LNP STAT-KON* KEP33 is a compound based on Acetal resin containing 15% Carbon Fiber, 15% PTFE/Silicone. Added features of this material include: Electrically Conductive, Wear Resistant. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 66.1 °C | 151 °F | unannealed (0.125 in); ASTM D648 |
Styron EMERGEâ„¢ 5710 Acrylonitrile Butadiene Styrene (ABS) EMERGEâ„¢ ABS 5710 advanced resin is an ignition resistant ABS resin with an excellent balance of flow and impact strength. Applications: Monitor Enclosures Surge Protectors and UPS Enclosures .. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | ASTM D648 |
A. Schulman POLYFORT™ FXP 2600-3120 CaC02 Filled Homopolymer Polypropylene DescriptionPolyfort® FXP 2600-3120 is a 20% GAC02 filled homopolymer polypropylene compound.Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | ASTM D648 |
A. Schulman POLYFORT™ FPP 1182 Talc Fortified Impact Resistant Polypropylene DescriptionPolyfort® FPP 1182 is a 20% talc fortified impact resistant polypropylene.Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | ISO 75-2 |
Borealis MS64T20 Polypropylene Compound, Mineral Filled MS64T20 is a 20% mineral filled polypropylene compound intended for injection molding. This material has excellent balanced mechanical properties and is easy to process. Applications: automotive p.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | ASTM D648 |
Eastman DuraStar DS1910HF Polymer, Natural Durastar DS1910HF polymer is a high flow grade of Durastar that contains a mold release. Durastar DS1910HF flow lengths are increased 20-40% relative to Durastar DS1010 as shown by spiral flow testi.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | ASTM D648 |
Eastman DuraStar MN630 Polymer, Natural Durastar Polymer MN630 has excellent appearance and is nearly water-clear. Its most outstanding features are toughness, chemical resistance, and excellent processing characteristics. MN630 has very .. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | ASTM D648 |
Eastman Tenite Acetate 105E1R26029 Clear, Trsp Cellulose Acetate TENITE cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of TENITE cellulosi.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | ASTM D648 |
ExxonMobil PP1222F Mineral-filled Homopolymer Medium melt flow rate homopolymer, 20% filled. Particularly suitable for consumer products and appliance applications requiring long term heat aging resistance. UL continuous service rating of 95°.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 66.1 °C | 151 °F | |
Aclo Accuguard ABS ABS860V0L Flame Retardant |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 66.1 °C | 151 °F | |
Aclo Accutech Polypropylene Homopolymer HP0336W20L1 Wollastonite Reinforced |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | ASTM D648 |
A. Schulman ComAlloy Comtuf® 101 Polypropylene, Mineral Reinforced, Impact Modified Data provided by the manufacturer, ComAlloy International Company.25% Mineral Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been i.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 66.1 °C | 151 °F | ASTM D-648 |
Axiall 7801 Rigid PVC, Extrusion, White, High Impact Profile Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 66.1 °C | 151 °F | ASTM D-648 |
Axiall 7803 Rigid PVC, Extrusion High Impact Profile Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | Dry; ASTM D648 |
Asahi Kasei Leona® FR200 Nylon 66 UL94 V-0; halogen-free and phosphor-free.Applications:Connectors, switches, and other electrical and electronic parts Information provided by Asahi Kasei |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | 120°C/h; ISO 75/1 |
Polykemi AB POLYfill PPH TS8030 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | Unannealed; ISO 75-2A |
Total Lacqrene® 2901 Medium Impact Polystyrene
(discontinued **) LACQRENE® 2901 is a very easy flowing, medium impact polystyrene for injection molding. The very high flow of this grade allows for the production of thin wall section or long flow path molding on.. |