- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 142 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 142 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C @Thickness 3.18 mm |
142 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Geon™ Vinyl Rigid Extrusion 87707 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.2 °C @Thickness 3.18 mm |
142 °F @Thickness 0.125 in |
Injection Molded; Annealed; ASTM D648 |
| PolyOne Geon™ Vinyl Rigid Extrusion 87727 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C @Thickness 3.18 mm |
142 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Geon™ Vinyl Rigid Extrusion 87727-0284 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples. Physical property testing was based on the Geon® 87727 Trans 0020.Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | ASTM D648 |
| RheTech Products HP514-182 14% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, 7701 Graphite Applications: Glove box binInterior trimSteering column trimConsolesAir ducts - distributionInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | ASTM D648 |
| RheTech Products HP514-393 14% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, 110D Medium Dark Pewter Applications: Glove box binInterior trimSteering column trimConsolesAir ducts - distributionInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | ASTM D648 |
| RheTech Products HP514-447 14% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, 9902 Very Dark Gray Applications: Interior trimCenter consolesFuse panelsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | ASTM D648 |
| Nylene® 733 Nylon 6 Dry as molded. Injection molding grade. Nylene 733 is a high impact modified nylon suitable for both molding and extrusion. Parts molded from 733 have excellent impact strength right out of the mol.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPH TS15020 D Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | ASTM D648 |
| North Wood Plastics Polypropylene with 20% Wood Fiber, Molding Grade Data provided by North Wood Plastics, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C @Thickness 3.18 mm |
142 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Maxxam™ DP 9052-3-1000 Polyethylene, High Density (HDPE) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | ASTM D648 |
| RheTech Products HP514-00 14% Talc Reinforced High Performance Polypropylene Copolymer, Non-UV Stabilized, Natural Applications: Glove box binInterior trimSteering column trimConsolesAir ducts - distributionInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.1 - 76.7 °C | 142 - 170 °F | Average value: 67.1 °C Grade Count:11 |
| Overview of materials for PVC, Transparent This property data is a summary of similar materials in the MatWeb database for the category "PVC, Transparent". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 - 250 °C | 142 - 482 °F | Average value: 156 °C Grade Count:95 |
| Overview of materials for Nylon 66, Glass Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass Bead Filled". Each property range of values reported is minimum and maximum values of ap.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | ISO 75-1,-2 |
| Gromax BTE70-FN001N1 Nylon 6 (Dry) Information provided by Gromax Enterprises Corp. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | Unannealed; ISO 75A-1, -2 |
| LyondellBasell Hostacomâ„¢ RTA3184 Thermoplastic Polyolefin Elastomer Description: Hostacomâ„¢ RTA3184 medium melt flow, 1,300 MPa flexural modulus, low level glass-reinforced, colorable, interior trim grade thermoplastic elastomeric olefin (TEO) resin is modified .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| SABIC Innovative Plastics SABIC PPCOMPOUND 7985 PP SABIC® PPcompound 7985 is a mineral filled, impact modified polypropylene TPO. This material combines scratch resistance and heat stability with interior automotive UV stability. The IMDS is 2097.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6 IM 7040 MB Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier, Nucleating Agent and LubricantFeatures: Heat Stabilized, Impact Modified, Nucleated and LubricatedInformation pro.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6 IM 7050 Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier, Nucleating Agent and LubricantFeatures: Heat Stabilized, Impact Modified, Nucleated and LubricatedInformation pro.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON MD000I PP (Europe-Africa-Middle East) LNP* Stat-kon* MD000I is a compound based on Polypropylene resin. Added features of this material include: Electrically Conductive, High Impact. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP MB008S PP LNP* THERMOCOMP* MB008S is a compound based on Polypropylene resin containing 40% Glass Bead. Added features of this material include: Heat Stabilized. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Thermocomp MB008S PP (Asia Pacific) LNP* Thermocomp* MB008S is a compound based on Polypropylene resin containing Glass Bead. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Asia Pa.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | ASTM D648 |
| Eastman Tenite 285A2R30018 Cellulose Acetate Butyrate, Natural, Trsp Applications:OphthalmicsOptical safety framesProduct Description: Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, cla.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Eurostar Starpylen HU 30E4 ECR PP, Mineral Filled, Injection Molding Starpylen HU 30E4 ECR is a reinforced Polypropylene with a low carbon footprint renewable mineral filler, Injection Molding Resin (also known as HUS30E4ECR)Information provided by Eurostar. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | |
| Aclo Accutech Polypropylene Homopolymer HP0339C40L Calcium Reinforced |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | ISO 75-2/AF |
| Addiplast Addilene H 490 S Flame Retardant Polypropylene Flame retardant, unreinforced, with halogensInformation provided by Addiplast. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | ISO 75-2/AF |
| Addiplast Addilene J 490 M20S Flame Retardant Polypropylene, 20% Mineral Filled Flame retardant, mineral filled, with halogensInformation provided by Addiplast. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | |
| Aclo Accutech Polypropylene Copolymer CP0436M20L Mica Reinforced |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | |
| Aclo Accutech Polypropylene Copolymer CP0436T40L Talc Reinforced |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | Unannealed; ISO 75-2/Af |
| Styron INSPIRE™ TF7000 ES Natural Performance Polymer INSPIRE* TF7000 ES Natural Performance Polymer DA™ is a very high stiffness (2400 MPa) TPO designed for instrument panel upper and lower components, as well as other interior trim applications wher.. |
|||