Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 57.2 °C @Thickness 3.18 mm |
135 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
PolyOne Geon™ Vinyl Packaging 2121 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 57.2 °C | 135 °F | ASTM D648 |
RheTech Products HP521-187 15% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, 9779 Medium Grey Applications: Interior trimIP structural componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 57.2 °C | 135 °F | ASTM D648 |
RheTech Products M12P250-01 12% Mica Reinforced Polypropylene Copolymer, Black Applications: Filler panelsHVAC ductsFan shroudsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 57.2 °C | 135 °F | ASTM D648 |
RheTech Products T20P252-00 20% Talc Reinforced Polypropylene, Natural Applications: IP Structural componentsGlove box binWire troughInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C @Thickness 3.20 mm |
135 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP COLORCOMP PX99848 PA 6 (Asia Pacific) LNP* Colorcomp* PX99848 is a compound based on Nylon 6 resin containing Unfilled Custom Color. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 57.2 °C | 135 °F | ASTM D648 |
RheTech Products HP522-473 15% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, ZU5A Dark Graphite Applications: ConsolesClose out panelInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C | 135 °F | 120°C/h; ISO 75/1 |
Polykemi AB POLYfill PPC K5040 E30 Polypropylene Copolymer, Mineral Reinforced, Elastomer Modified Information provided by Polykemi AB |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 57.2 °C | 135 °F | Unannealed; ISO 75A-1, -2 |
LyondellBasell Hostacomâ„¢ CB275FC Thermoplastic Polyolefin Elastomer Description: Hostacomâ„¢ CB275FC high melt flow, 1,900 MPa flexural modulus, precolored, UV-stabilized, mineral-filled thermoplastic elastomeric olefin (TEO) resin has an excellent balance of pro.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 57.2 °C | 135 °F | Unannealed; ISO 75A-1, -2 |
LyondellBasell Hostacomâ„¢ TKS708D Thermoplastic Polyolefin Elastomer Description: Hostacomâ„¢ TKS708D medium high melt flow, 1,300 MPa flexural modulus, UV-stabilized, high impact thermoplastic elastomeric olefin (TEO) resin has an excellent combination of propert.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C @Thickness 3.20 mm |
135 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP LUBRICOMP ML003S PP LNP* LUBRICOMP* ML003S is a compound based on Polypropylene resin containing 15% PTFE. Added features include: Heat Stabilized, Wear Resistant. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C | 135 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics Xenoy® X6125 PBT+PC Unreinforced, impact modified, thermoplastic alloy (PBT+PC). High impact strength while retaining mechanical and thermal properties.This data was supplied by SABIC-IP for the Americas region. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 57.2 °C | 135 °F | Unannealed; ASTM D648 |
Techmer ES Luriblend® PA6 TS15 BK Nylon 6 Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Silicone Lubricant and PTFE LubricantFeatures: Heat Stabilized and LubricatedAppearance: BlackInformation provided by TP Composite.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 57.2 °C | 135 °F | Unannealed; ASTM D648 |
Techmer ES HiFill FR® PP CO FR HS Availability: North AmericaForms: PelletsAdditive: Heat StabilizerFeatures: Flame Retardant, Heat Stabilized and CopolymerUL File Number: E157318Processing Method: Injection MoldingInformation provi.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C | 135 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP THERMOCOMP WX02869H Polyester, TP LNP THERMOCOMP* WX02869H is a compound based on Polyester, TP resin containing High Specific Gravity. Added features of this material include: High Impact. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 57.2 °C | 135 °F | ASTM D648 |
A. Schulman PP 1259 Polypropylene Medium Impact Polypropylene DescriptionPolypropylene PP 1259 is a medium impact polypropylene with easier molding characteristics for thinner parts and longer flow distances. Lower molding pressures and heats often reduce war.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C | 135 °F | ISO 75 |
Unipetrol PP MONSTEN® TL 003 Polypropylene Homopolymer Made for tape applications. UV stabilized. Homopolymer.Information provided by Unipetrol RPA |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 57.2 °C | 135 °F | ASTM D648 |
A. Schulman PP 1259 Polypropylene Medium Impact Polypropylene DescriptionPolypropylene PP 1259 is a medium impact polypropylene with easier molding characteristics for thinner parts and longer flow distances. Lower molding pressures and heats often reduce war.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C | 135 °F | 120°C per hour; ISO 75-2 |
Total PPH 5042 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 5042 is homopolymer.ApplicationATOFINA Polypropylene PPH 5042 has been specially designed for extrusion-thermoforming, where it gives improved rigidity and impact resistanc.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C | 135 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
Eurostar Starflam M10009A PP, Flame Retardant, Injection Molding Starflam M10009A is an Unfilled Flame Retardant Polypropylene (Homo) Injection Molding ResinInformation provided by Eurostar. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C | 135 °F | ASTM D648 |
E-Polymers TEKASTER® F100 low-mid viscosity PBT Polyester Resin: TEKASTER is thermoplastic polyester resins (PBT, PET) mostly injection molding. PBT has excellent mechanical properties and well balanced engineering plastics with an electrical pe.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C | 135 °F | ASTM D648 |
Braskem H 103 Injection Molding Polypropylene Applications: Thin-walled parts and easy mould filling; food and cosmetic packing; toys and household; sealed closures. Information provided by Braskem |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C | 135 °F | ASTM D648 |
Braskem H 107 Injection Molding Polypropylene Applications: Thin-walled parts and easy mould filling. Information provided by Braskem |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C | 135 °F | ASTM Test |
BASF Ultramid® 8281 HS PA6 (Dry) |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C | 135 °F | dry; ISO 75 |
Azoty Tarnow™ Tarnamid® T-30 MHLS Polyamide 6 - Colored High viscosity heat and UV light stabilized grade for injection molding.Tarnamid® has the following main properties:High mechanical strength, rigidity and hardnessHigh impact strengthHigh vibration.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C | 135 °F | ASTM D648 |
Albis Plastics Cellulose Acetate CA700 , Unreinforced, 35% Plasticizer
(discontinued **) Amorphous Cellulose Acetate (CA)Characteristics: Chemical Resistance, Toughness, Strength, Hardness, Gloss, Clarity and "Feel"Applications: Tool Handles, Optical Products, Toys and Sheet ProductsPro.. |