- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 129 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 129 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 53.9 °C | 129 °F | Unannealed; ASTM D648 |
| Multibase Nylex™ 2185 HF Polyamide + PP Forms: PelletsProcessing Methods:Injection MoldingInformation provided by Multibase |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ASTM D648 |
| Custom Resins Vexel™ 3250 PBT
(discontinued **) General Purpose Unreinforced; High Flow. Property data for dry as molded samples.Data provided by the manufacturer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Crastin® S610SF BK851 PBT
(Unverified Data**) Crastin® S610SF is an unreinforced, low viscosity polybutylene terephthalate for injection molding. It has high flow characteristics and is specifically suitable for super fast production.Informati.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75 |
| Phillips Sumika Marlex® CHP-370 Thermoplastic Polyolefin
(discontinued **) Thermoplastic Polyolefin, Good Stiffness and Impact PerformanceApplications: Automotive Pillar TrimConditioning after Molding: 48 hr at 23°CNominal Shrinkage: 0.8-1.0%Drying conditionsTemperature: .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ASTM D648 |
| Albis Plastics Cellulose Acetate Butyrate B9024 (UVI, Odor Mask Added), 16% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C @Thickness 6.40 mm |
129 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical Lupox® GP1000M PBT Description: Injection Molding, PBT, High Flow, High ImpactApplication: Automotive (Connector)CAS No. 155123-66-3 and 24968-12-5Information provided by LG Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75-1,-2 |
| Inno-Comp INNOPOL® CS 1-3000 N DEL Polypropylene Homopolymer INNOPOL® CS 1-3000 N DEL is developed for producing injection molded automotive components.All information provided by INNO-COMP. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C @Thickness 3.20 mm |
129 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP PL002 PA 6 LNP* LUBRICOMP* PL002 is a compound based on Nylon 6 base resin containing 10% PTFE. Added feature of this grade is: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C @Thickness 6.40 mm |
129 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP YL003C Polyester Elastomer (Asia Pacific) LUBRICOMP* YL-4030 CCS is a PTFE Lubricated Compound based on Polyester Elastomer resin which has low ionic and low outgassing performance for the Semicon and Internal Hard Disk Drive applications. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C @Thickness 6.40 mm |
129 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® 315 PBT Unreinforced, For extrusion/compounding only (not for injection molding). High viscosity. Melt viscosity between 7500 and 9500 poise. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C @Thickness 6.40 mm |
129 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® 325 PBT (Asia Pacific) General purpose, unreinforced, improved processing. Applications like sprinklers and nozzles, pumps, door handle, tank covers, pens, pencils etc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C @Thickness 3.20 mm |
129 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® V2000DM PBT (Asia Pacific) Unreinforced, directly metallizable PBT injection molding resin with high flow better release characteristics. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Sax Polymers SAXAMID 136Q32 Nylon 6, Injection Molding Grade SAXAMID 136Q32 is a high impact-modified polyamide 6 injection-molding-grade.Information provided by SAX Polymers |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C @Thickness 3.20 mm |
129 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® IQ3001 PBT Valox IQ3001 is an unfilled environmentally responsible iQ-PBT resin modified with elastomer. Targeted for flexible hinge applications. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75-2 |
| Borealis Daplen™ EE158AI Polypropylene TPO Compound Daplen™ EE158AI is a 13% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness, give.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75-2 |
| Borealis Daplen™ EE188HP Polypropylene TPO Compound Daplen™ EE188HP is a 15% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness and g.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75 |
| Unipetrol PP MONSTEN® MA 350 Polypropylene Homopolymer Applications include injection molding. Antistatic stabilization. Homopolymer.Information provided by Unipetrol RPA |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ASTM D648 |
| Formosa Plastics Formolene® 6507N Impact Copolymer Polypropylene Impact Copolymer for Injection Molding Formolene® 6507N is a medium impact copolymer of polypropylene characterized by its easy mold flow, physical property balance and excellent dimensional stabil.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | Plain Cast Resin; ASTM D648 |
| TSE Industries EcoWIND® M110 General Purpose Filament Winding Polyurethane Resin TSE-EcoWIND® resins are “Environmentally-Preferred Products” or EPP’s. They are a pair of polyurethane resins free of Styrene, and are “ultra-low” emitting during application. TSE-EcoWIND® re.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Eurostar Starflam MX06089 PP, Flame Retardant, Injection Molding Starflam MX06089 is an Unfilled Flame Retardant Polypropylene Injection Molding ResinInformation provided by Eurostar. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | dry; ISO 75 |
| Azoty Tarnow™ Tarnamid® T-27 MCS I Polyamide 6 - Impact Modified High impact resistance grade. Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following main properties:H.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75 |
| A.D. Compound Adene NCQAG Copolymer 40% CaCO3 Filled Polypropylene Information provided by A.D. Compound |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75-2 |
| CENTROPLAST CENTROLEN PP-H Polypropylene homopolymer This plastic is a low density, easily machined material that can be welded and has good chemical resistance. Applications include filter housings, chemical pump components and apparatus engineering.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | |
| Ineos ABS Triax® 1180 ABS + Polyamide Blend (DAM)
(discontinued **) Key Features:UnfilledHigh impact or high impact modifiedSuitable processing methods:Injection moldingInformation provided by Bayer Polymers.LANXESS was spun-off from Bayer in early 2005. Business r.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75 |
| Unipetrol PP MONSTEN® EH 501 Polypropylene Impact Copolymer Made for extrusion applications. LHTA stabilization. Impact copolymer.Information provided by Unipetrol RPA |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ASTM D648 |
| Adell RZ-16 Copolymer Polypropylene, 30% Calcium Carbonate Filled Data provided by Adell Plastics, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 53.9 °C | 129 °F | ISO 75-2/A |
| ExxonMobil PP7064L1 Polypropylene Impact Copolymer Product Description: A nucleated impact copolymer resin with medium flow, high stiffness and antistatic properties. It is suitable for molding applications like consumer products, closures, contain.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Crastin® S610SF NC010 PBT
(Unverified Data**) Crastin® S610SF is an unreinforced, low viscosity polybutylene terephthalate for injection molding. It has high flow characteristics and is specifically suitable for super fast production.Informati.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ASTM D648 |
| Braskem CP 286 Injection Molding Polypropylene Heterophasic Copolymer Description: CP 286 is a high melt flow rate, heterophasic copolymer, suitable for injection moulding applications and also as base resin for compound. The resin combines excellent stiffness with g.. |
|||