- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 96.0 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 96.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | ISO.75 DIN.53461 |
| Omnia Plastica Omniamid PA6 GHR HR - Dry Cast nylon 6 produced with the addition of graphite and a special lubricator which gives to this product better properties than natural PA6G. Whilst retaining the general features of OMNIAMID G it i.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | ASTM D648 |
| PTS PCA-3015 Low Temperature Impact PC/PBT Alloy Information provided by Polymer Technology and Services, LLC (PTS). |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C @Thickness 3.20 mm |
205 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP FARADEX NS0031 PC+ABS (Asia Pacific) Faradex NS0031 is a compound based on PC+ABS blend resin containing non-brominated and non-chlorinated flame retardant system, Stainless Steel. Added features of this material include: EMI/RFI Shiel.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP FARADEX NX07344 PC+ABS (Asia Pacific) Faradex NX07344 is a compound based on PC+ABS blend resin containing non-brominated and non-chlorinated flame retardant system, Stainless Steel and glass fiber. Added features of this material incl.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | |
| Ineos ABS TRIAX® 1408 GF ABS/Nylon Blend, Injection Grade, As Conditioned
(discontinued **) Standard injection molding grade, easy flow, easy mold release, fast setting.Applications: Thin walled engineering parts. Automotive sector: air filters, switch and connector parts for car electric... |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | |
| Ineos ABS Lustran® H607AS Contains antistatic additives,Property data per ISO test methods. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP KL001 Acetal Copolymer (Asia Pacific) LNP* Lubricomp* KL001 is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C @Thickness 3.20 mm |
205 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Lubricomp OP005XXC PPS LNP LUBRICOMP* OP005XXC is a compound based on Polyphenylene Sulfide resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON DE0021E PC (Asia Pacific) LNP STAT-KON* DE0021E is a compound based on Polycarbonate resin containing Carbon Fiber, Flame Retardant. Added features of this material include: Easy Molding. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | |
| Spartech Royalite R84 Proprietary Polymer Weather Resistant Sheet Data provided by the manufacturer. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Thermocomp FF008L PE LNP* Thermocomp* FF008L is a compounding based on Polyethylene containing glass fiber. Added characteristics include Low Extractible.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | ISO 75-1/-2 |
| Styrolution Luran® S 757 G UV White 37019 ASA Description: Particularly easy flowing injection molding grade for difficult moldings with large flow path/wall thickness ratios.Information provided by STYROLUTION, which is a joint venture between.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | ISO 75 |
| Styrolution Terluran® HI-10 ABS Terluran HI-10 is an injection molding and extrusion grade of ABS with very high toughness and medium flow.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C @Thickness 6.40 mm |
205 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® V3900WX PBT+PC (Asia Pacific) PBT/PC blend - Unreinforced - Flame Retardant. This is a UV-stabilized grade designed for outdoor enclosure applications requiring UL 746C F1 weatherability performance. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | 0.25 inch; ASTM D648 |
| PlastxWorld CEVIAN® B14E0 PBT/ABS Alloy Excellent flowability, high impact strength and toughness. These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWo.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | DIN 53461 |
| Polyram RamShine PAS701 ASA, UV Stabilized UV stabilized general purpose injection molding ASAInformation provided by Polyram Ram On Ind. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | annealed; ISO 75 |
| Chi Mei Kibilac® PW-997S ASA Polymer Extrusion |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | annealed; ISO 75 |
| Chi Mei Polylac® PA-726 ABS Electro-plating |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | annealed; ISO 75 |
| Chi Mei Polylac® PA-746 ABS - High Flow High flow, medium impact |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | annealed; ISO 75 |
| Chi Mei Polylac® PA-747 ABS High impact |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Delrin® 500SC NC010 Acetal (POM)
(Unverified Data**) Silicone Lubricated Medium Viscosity Acetal Homopolymer Concentrate Developed for Enhancing LubricityInformation provided by DuPont Performance Polymers |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | annealed; ISO 75 |
| Chi Mei Polylac® PA-747S ABS - Extrusion High Impact Extrusion |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | ASTM D648 |
| Ashley Polymers Ashlene® ABS Resin 223 Medium impact, medium flow, matte finish. Suitable for general purpose injection molding.Data provided by the manufacturer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | Method A - Annealed; ASTM D-648 |
| Bhansali Engineering Abstron HCR-15 M ABS Heat Resistant Chemical Resistant GradeInformation provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPC GF5020 Polypropylene Copolymer, Glass Fiber Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C @Thickness 0.125 mm |
205 °F @Thickness 0.00492 in |
ASTM D648 |
| Proto3000 PC-ABS Fused Deposition Modeling Polymer Description: PC-ABS (polycarbonate-ABS) is one of the most widely used industrial thermoplastics. PC-ABS offers the most desirable properties of both materials - the superior strength and heat resis.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | Method A - Annealed; ASTM D-648 |
| Bhansali Engineering Abstron IMC-45 FR V2 Flame Retardant PC/ABS Grade Information provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | |
| Arkema Group Oroglas® V 920 T Acrylic, Injection Molding Grade
(discontinued **) OROGLAS V 920 T is an injection molding grade with an improved thermal resistance HDT A ( 1.82 MPa ) = 96°c without any adverse effect on mechanical and optical properties.The processing of OROGLAS.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | ISO 75-1/-2 |
| Styrolution Luran® S KR 2867 C WU Colored ASA+PC Description: Easy flowing injection molding grade containing bromine-, chlorine- and antimony-free flame retardant.Information provided by STYROLUTION, which is a joint venture between BASF and INEO.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C @Thickness 3.20 mm |
205 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP AX06472 ABS LNP* Thermocomp* AX06472 is a compound based on ABS containing a clay blend. |
|||