- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 92.0 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 92.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | |
| Eastman Eastalloy DA003 PC+PCTG Copolyester/Polycarbonate
(discontinued **) ISO data as provided by the manufacturer, Eastman Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C @Thickness 6.40 mm |
198 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical LG703W ABS, Low Gloss, Heat Resistance Feature: Injection Molding, Low Gloss, Heat ResistanceApplication: Automobiles Interior Housing (Column Cover, Filllar Etc)CAS No. 25120-20-1, 9003-56-9, 25747-74-7 and 9003-54-7Information provided.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | ASTM D648 |
| Kolon KOCETAL® EL302 Toughened Grade Acetal Resin Flexible grade. Applications: Flexible products. Information provided by API-Kolon. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | ASTM D648 |
| LG Chemical LUPOY GP-5000FQ General Purpose PC/ABS Alloy, Unreinforced, Excellent Flow Among the characteristics of LUPOY polycarbonate resins are excellent mechanical properties, high heat resistance, high impact strength, and dimensional stability.Applications:Automotive: Automotive.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | ISO 75-1,-2 |
| Ineos ABS Triax® 3158 ABS + Polyamide Blend (DAM), PA66/ABS Pellets (filled) Triax® 3158 is a PA+ABS-Blend and on-line paintable (195°C). It has very high heat resistance, reduced moisture, improved impact strength, and a low coefficient of linear thermal expansion. It.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP IAL12 PA6.12 LNP* LUBRICOMP* IAL12 is a compound based on Nylon 6/12 resin containing 5% PTFE, 10% Aramid Fiber. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP KA000M POM (Europe-Africa-Middle East) LNP* LUBRICOMP* KA000M is a compound based on Acetal Copolymer resin containg Aramide and Proprietary Lubricant. Added features include Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL WCV072 PPE+PP (Europe-Africa-Middle East) Flexible, halogen free mPPE extrusion grade material for applications such as automotive wire insulation. Low specific gravity with good flame retardant and very good scrape abrasion resistance. De.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP KL002 Acetal Copoly LNP* LUBRICOMP* KL002 is a compound based on Acetal Copolymer resin containing 10% PTFE. Added feature of this material is: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP KP002 Acetal Copoly (Asia Pacific) LNP* Lubricomp* KP002 is a compound based on Acetal Copolymer resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRILOY DF2041 PC LNP LUBRILOY* DF2041 is a compound based on Polycarbonate resin containing 20% Glass Fiber, Proprietary Lubricant. Added features include: Flame Retardant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics XYLEX X7300CL PC+POLYESTER PC+ POLYESTER unreinforced alloy developed for optical or lense market. Chemical resistance. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics XYLEX X7300CL PC+POLYESTER (Asia Pacific) PC+ POLYESTER unreinforced alloy developed for optical or lense market. Chemical resistance. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics XYLEX X7300CL PC+POLYESTER (Europe-Africa-Middle East) PC+ POLYESTER unreinforced alloy developed for optical or lense market. Chemical resistance. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP AX90213 ABS LNP* THERMOCOMP* AX90213 is a compound based on ABS resin containing Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | ASTM D648 |
| Samyang Tramid® 210P Polyamide, High Productivity Strong with excellent thermal resistance. Abrasion resistance, chemical resistance and oil resistance are excellent.210P is a high productivity grade.Applications:ConnectorsCable tiesHarness clipsT.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOTUF CF007IXP PS LNP* Thermotuf* CF007IXP is a compound based on Polystyrene containing glass fiber. Characteristics of this grade are: High Impact. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics NORYL FP6130 PPE+PS (Asia Pacific) Noryl* FP6130 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and high flow , this resin also uses non-chlorinated, non-brominated FR a.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | ASTM D648 |
| Eastman Tritan LX201 Copolyester Eastman Tritan LX201 is an amorphous copolyester with excellent appearance and clarity. Tritan LX201 contains a mold release derived from vegetable based sources. Its most outstanding features are.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | ASTM D648 |
| Eastman Tritan MX810 Copolyester Applications:Blood TherapyDialyzer HousingsIV ComponentsKey Attributes:Ease of processingExcellent clarityExcellent hydrolytic stabilityFast drying timesGood chemical resistanceOutstanding impact re.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | ASTM D648 |
| Eastman Tritan TX2000 Copolyester Eastman Tritan TX2000 is an amorphous copolyester with excellent appearance and clarity. Its most outstanding features are excellent toughness, hydrolytic stability, and heat and chemical resistanc.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | Method A - Annealed; ASTM D-648 |
| Bhansali Engineering Abstron IM-11BM ABS Injection Molding Grade High Impact Strength, Medium Flow, High Fatigue ResistanceInformation provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | Method A - Annealed; ASTM D-648 |
| Bhansali Engineering Abstron IM-17A(HF) ABS Injection Molding Grade Very High Flow, Medium Impact GradeInformation provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C @Thickness 6.40 mm |
198 °F @Thickness 0.252 in |
Method A; ASTM D648 |
| Bhansali Engineering Abstron SE32 FR IS15061 Flame Retardant ABS Flame Retardant- IS 15061 conformedInformation provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C @Thickness 6.40 mm |
198 °F @Thickness 0.252 in |
Method A; ASTM D648 |
| Bhansali Engineering Abstron IPM2000 PMMA- ABS Alloy High Gloss, High scratch resistanceInformation provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | Method A - Annealed; ASTM D-648 |
| Bhansali Engineering Abstron SE-32 ABS Sheet Extrusion Grade Super high and Very High Impact Sheeting grades for Automobile & Luggage ApplicationsInformation provided by Bhansali |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C @Thickness 6.35 mm |
198 °F @Thickness 0.250 in |
ASTM D-648 |
| Chevron Phillips EA3025 Crystal Polystyrene
(discontinued **) High heat crystal polystyrene.Applications:Foam egg cartonsFoam meat traysInsulation boardBi-axially oriented sheetFeatures:Ultra-high molecular weight homopolymerHigh Vicat softening temperatureNar.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | ISO 75-1, 2 |
| Polyplastics Duracon® CP-15X Acetal Co-polymer (POM), Creep resistant, Creep resistant DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O).. |
|||