- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 84.0 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 84.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | |
| Polimeri Europa KOSTIL B266 Styrene Acrylonitrile Symbol according to ISO 1043-1: SAN Grade designation according to ISO 4894-SAN 2,M,105-15 Standard injection moulding grade with good chemical resistance Application fields: household and small .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C @Thickness 3.20 mm |
183 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Cycolac® INP562 ABS SABIC INP562 provides compatibility with a wider range of ABS grades than many color concentrate bases; allows better dispersion than pellets; allows concentrate manufacturers to produce both pellet.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYasa 2410F High Flow ASA Information provided by Polykemi AB |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C @Thickness 3.20 mm |
183 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® CX2142ME PC+ABS Cycoloy* resin grade CX2142ME is an injection moldable PC/ABS blend with Br- and Cl-free flame retardant systems. Key features of good flow, good impact, UL-94 V0 rating at 1.2 mm, and improved chem.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C @Thickness 3.20 mm |
183 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Cycoloy® CX7110 PC+ABS (Europe-Africa-Middle East) Cycoloy* resin grade CX7110 is an injection moldable PC/ABS blend with non-brominated and non-chlorinated flame retardant systems. Excellent impact/flow balance together with a UL-94 V0 rating at 1... |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C @Thickness 3.20 mm |
183 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Geloy FXTW26SK ASA Next generation Geloy XTW ASA for high heat exterior applications. Outstanding weatherability and toughness. Metallic sparkle VisualFx.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C @Thickness 3.20 mm |
183 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Geloy XTWM206 ASA (Asia Pacific) Next generation ASA optimized for outstanding weatherability, colorability and higher heat applications requiring UV exposure resistance.This data was supplied by SABIC-IP for the Asia Pacific regio.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C @Thickness 3.20 mm |
183 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Geloy XTWM206 ASA (Europe-Africa-Middle East) Next generation ASA optimized for outstanding weatherability, colorability and higher heat applications requiring UV exposure resistance.This data was supplied by SABIC-IP for the Europe-Africa-Midd.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP AL002 ABS (Asia Pacific) LNP* LUBRICOMP* AL002 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C @Thickness 6.35 mm |
183 °F @Thickness 0.250 in |
ASTM D-648 |
| Chevron Phillips MA5350 HIPS - High Impact Polystyrene
(discontinued **) Rubber modified high impact polystyrene.Applications:Floppy diskettesDurable household applicationsThin to medium parts that require a combination of high gloss and good toughnessFeatures:Low coeffi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP AL002 ABS (Europe-Africa-Middle East) LNP* LUBRICOMP* AL002 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | ASTM D648 |
| Albis Plastics ASA 02A 811 Unreinforced
(discontinued **) Acrylonitrile/Styrene/AcrylateCharacteristics: Excellent UV, Good Rigidity, Good Dimensional StabilityApplications: Sunglasses, Boat Shells, Roofs for Campers & RVsProcessing: Injection Molding (Mel.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C @Thickness 6.35 mm |
183 °F @Thickness 0.250 in |
ASTM D648 |
| IRPC Polimaxx Porene SP100 Acrylonitrile Butadiene Styrene Applications:injection moldinghelmetsautomotive |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C @Thickness 3.20 mm |
183 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON DD0001I PC LNP* STAT-KON* DD0001I is a compound based on Polycarbonate resin containing Carbon Powder. Added features include: ECO FR rating of 94V-0 @ 3.0mm and 94V-1 @ 1.5mm, High Impact. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Valox® IQ357U PBT+PC Valox* Resin IQ357U: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified and UV stabilized resin. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C @Thickness 3.20 mm |
183 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP HH0420A PA11 LNP* THERMOCOMP* HH0420A is a compound based on Nylon 11 containing proprietary fillers. Added features of this material are High Specific Gravity. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C @Thickness 6.40 mm |
183 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Starex® SF-0505H MABS, Unreinforced Scratch Resistant Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C @Thickness 6.40 mm |
183 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Starex® LX-0981 ABS, Unreinforced Metallic-Look Luminous Grade - gives aesthetics of a painted surface without painting. Reduces time, cost, and environmental hazards (such as soilvents).Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C @Thickness 6.40 mm |
183 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Starex® NH-1907 HIPS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C @Thickness 6.40 mm |
183 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Starex® SF-0505H MABS, Unreinforced Scratch Resistant Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics NORYL PPX PPX7112 PPE+PP (Europe-Africa-Middle East) PPE+PP blend. Suitable for painted exterior automotive applications. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Sax Polymers SAXLAC 310A Acrylonitrile Butadiene Styrene Saxalac 310A is a medium viscosity, impact resistant ABS injection molding grade, characterized by good processability and high stiffness.Mechanical property data tested at 50% RH.Information provid.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C @Thickness 3.20 mm |
183 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Noryl FXN2090H PPE+HIPS Noryl* FXN2090H resin is an unfilled, injection moldable grade. Designed for exceptionally high gloss and improved pencil hardness vs. standard Noryl grades, FXN2090H resin uses non-halogenated FR a.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C @Thickness 3.20 mm |
183 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Noryl FXN2090H PPE+HIPS (Europe-Africa-Middle East) Noryl* FXN2090H resin is an unfilled, injection moldable grade. Designed for exceptionally high gloss and improved pencil hardness vs. standard Noryl grades, FXN2090H resin uses non-halogenated FR a.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | DIN 53461 |
| Polyram RamShine PV1003 ABS, General Purpose General purpose ABS for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 3702 Clarified Copolymer Polypropylene DescriptionPolyfort® PP 3702 is a clarified copolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1068-32 Black40% Mineral Filled Polypropylene DescriptionPolyfort® FPP 1068-32 Black is a 40% mineral filled polypropylene designed for use when improved heat resistance, dimensional stability and high stiffness is needed. ApplicationApplicati.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | ISO 75 |
| Ecomass® 706BI76 Filled ABS, Injection Molding Grade Moderate Specific Gravity, Filled ABS, Plating Grade, Product Form - PelletsProcessing Method: Injection MoldingNontoxic alternative to traditional materialsInformation provided by Technical Polyme.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Cycolac® DL100LG ABS (Europe-Africa-Middle East) Cycolac DL100LG is a low gloss, high heat, high impact ABS/PC blend with low emission |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | |
| Polimeri Europa SINKRAL PD G120 ABS
(discontinued **) Symbol according to ISO 1043-1: ABS Grade designation according to ISO 2580-ABS 1,MG,095-15-09-30 General purpose injection moulding grade. Characteristics: outstanding rigidity very high surface.. |
|||