- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 227 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 227 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C @Thickness 6.35 mm |
441 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| PolyOne LubriOne™ SF-30CF/15T Polyphenylene Sulfide (PPS) LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 441 °F | Annealed; ISO 75-2/A |
| PolyOne Nymax™ GF 924 33 UV Black 108 Polyamide 66 (Nylon 66) Property data for molded test bars: Dry as MoldedInformation provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 440 °F | ASTM D648 |
| Niche Polymer PA66GF13N Nylon 66, 13% Glass Fiber Filled Information provided by Niche Polymer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 441 °F | Unannealed; ASTM Data |
| Dow Questra® EA503 High Heat Syndiotactic Polystyrene, 30% Glass Filled
(discontinued **) QUESTRA® Crystalline Polymers are semi-crystalline engineering thermoplastic resins produced from styrene monomer using a proprietary metallocene catalyst system. These syndiotactic polymers are ve.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 440 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PET GF45 X 45% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 45% Filler by WeightInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 440 °F | Unannealed; ASTM D648 |
| Techmer ES Statiblend® PA6/6 GF20 AS BK 20% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 20% Filler by WeightAdditive: Lubricant, Antistatic and Heat StabilizerFeatures: Antistatic, Heat Stabilized and Lubricate.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 441 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP RF0069SZ PA 66 LNP* THERMOCOMP* RF0069SZ is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of th is grade include: Flame Retardant, Heat Stabilized. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 441 °F | Unannealed; ISO 75-2/A |
| Solvay Specialty Polymers Ixef® 1524 Polyarylamide (PARA), 50% Glass Fiber (Dry) Ixef® 1524 is a 50% glass-fiber reinforced, halogen-free flame retardant polyarylamide which exhibits high strength and stiffness, good surface gloss, and excellent creep resistance.Features: Bro.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 441 °F | ASTM D648 |
| Sumitomo Bakelite Sumikon® PM-6430 Glass-Filled Phenolic, Injection Grade Sumikon PM-6430 black Phenolic is a two stage glass fiber and mineral filled special purpose molding compound. It is especially designed for applications requiring high strength and dimensional s.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 441 °F | DIN 53461 |
| Polyram PlusTek PA4801G6 Nylon 6.6, 30% Glass Fiber Reinforced, PTFE lubricated 30% glass fiber reinforced, PTFE lubricated polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 440 °F | ASTM D648 |
| Clariant PA123G20 Nylon 66, 20% Glass Fiber, Impact Modified, Heat Stabilized Data provided by Clariant Masterbatches |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 440 °F | ASTM D648 |
| Clariant PA123G25 Nylon 66, 25% Glass Fiber, Impact Modified, Heat Stabilized Data provided by Clariant Masterbatches |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 440 °F | ASTM D648 |
| Clariant Renol PA123G13 Nylon 66, 13% Glass Fiber, Impact Modified, Heat Stabilized, Lubricated Data provided by Clariant Masterbatches |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 441 °F | ASTM D648 |
| Adell AR-13 Nylon 66, 15% Glass Reinforced Data provided by Adell Plastics, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 441 °F | ASTM D648 |
| Adell AR-33 Nylon 66, 15% Glass Reinforced Data provided by Adell Plastics, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 441 °F | ASTM Test |
| BASF Ultramid® 7423-2 NF3001 13% Glass Filled PA66 (Dry) Ultramid 7423-2 NF3001 is an impact modified, 13% glass reinforced, heat stabilized injection molding PA6/6. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 440 °F | ASTM D648 |
| Asahi Kasei Thermofil N5-15FG-1103 15% Glass Fiber Reinforced, Lubricated Information provided by Asahi Thermofil |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 441 °F | ASTM D648 |
| Sumitomo Bakelite Sumikon® PM-6430 Glass-Filled Phenolic, Compression Grade Sumikon PM-6430 black Phenolic is a two stage glass fiber and mineral filled special purpose molding compound. It is especially designed for applications requiring high strength and dimensional sta.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 441 °F | ASTM D648 |
| Plenco 50030 PET, Pellet, Injection Molded, Natural Color
(discontinued **) PLENCO 50030 is an engineering grade glass reinforced polyethylene terephthalate resin designed for good physical strength. It is UL listed and available in white, natural, and black.Information sup.. |
|||