- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 157 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 157 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C | 315 °F | Unannealed; ISO 75-2/A |
| PolyOne OnForce™ LFT PP-40LGF/001 Natural Polypropylene Homopolymer (PP Homopolymer) PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C | 315 °F | ASTM D648 |
| Oxford Polymers C-Acetal 25GF 25% Glass Fiber Reinforced Copolymer Acetal 25% Glass Fiber Reinforced Copolymer AcetalInformation provided by Oxford Polymers. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C @Thickness 3.20 mm |
315 °F @Thickness 0.126 in |
Annealed; 2 hours at 200°C; ASTM D648 |
| Solvay Specialty Polymers KetaSpire® KT-851 Polyetheretherketone (PEEK)
(Unverified Data**) KetaSpire KT-851 resin is a depth-filtered grade of polyetheretherketone (PEEK) specially designed for use in extruded wire insulation coating. KT-851 offers the needed balance of properties and pro.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C | 315 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP KFL36 Acetal Copolymer (Europe-Africa-Middle East) LNP* Lubricomp* KFL36 is a compound based on Acetal Copolymer resin containing Glass Fiber, PTFE. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C | 315 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| SABIC Innovative Plastics SABIC STAMAX 40YM240 PP SABIC® STAMAX 40YM240 is a 40% long glass fiber reinforced polypropylene. The glass fibers are chemically coupled to the PP matrix, resulting in high stiffness and strength. The IMDS is 16497161... |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C @Thickness 6.40 mm |
315 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM ATX100 PEI+PCE Higher impact, high flow Polyetherimide blend. ECO Conforming, UL94 HB Listing. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C @Thickness 6.40 mm |
315 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Ultem HATX100 PEI+PCE (Asia Pacific) Higher impact, high flow Polyetherimide blend. ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C @Thickness 3.20 mm |
315 °F @Thickness 0.126 in |
Annealed; ASTM D648 |
| Solvay Specialty Polymers KetaSpire® KT-851 NL Polyetheretherketone (PEEK) KetaSpire® KT-851 NL resin is a depth-filtered grade of polyetheretherketone (PEEK) supplied in non-lubricated, natural-color pellet form and is specially designed for use in extruded wire insula.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C @Thickness 3.20 mm |
315 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP VERTON MV008S PP LNP VERTON* MV008S is a compound based on Polypropylene resin containing 40% Long Glass Fiber. Added features of this material include: Chemically Coupled, Heat Stabilized, Structural. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C @Thickness 3.20 mm |
315 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP VERTON MV008S PP (Europe-Africa-Middle East) LNP VERTON* MV008S is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled, Heat Stabilized. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C @Thickness 3.20 mm |
315 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP VERTON MV008SU PP LNP VERTON* MV008SU is a compound based on Polypropylene resin containing 40% Long Glass Fiber. Added features of this material include: Chemically Coupled, Heat Stabilized, UV Stabilized, Structur.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C | 315 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP VERTON MV00ASXC PP (Europe-Africa-Middle East) LNP* VERTON* MV00ASXC is a compound based on PP resin containing Long Glass Fiber. Added features include; Chemically Coupled, Heat Stabilized. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C @Thickness 3.20 mm |
315 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP VERTON MV00ASXP PP (Europe-Africa-Middle East) LNP VERTON* MV00AS is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C | 315 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP VERTON MVL36SX0 PP (Europe-Africa-Middle East) LNP* VERTON* MVL36SX0 is a compound based on PP resin containing Long Glass Fiber and PTFE. Added features include: Chemically coupled, Heat Stabilized, Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C | 315 °F | ASTM D648 |
| Plenco 4548 Phenolic, Granular, Injection Molded PLENCO 04548 is a heat resistant mineral filled phenolic molding compound, offering fast cure rates and hot rigidity. Type ASTM 5948 CFG, and UL recognized under component file E40654. 04548 is avai.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C | 315 °F | ISO 75-1/-2 |
| Covestro Apec® 1897 Polycarbonate Easy flowingeasy to demoldUV-stabilizedsoftening temperature (VST/B 120)=182 °CPreprocessingMax. Water content |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C | 315 °F | ASTM D648 |
| Asahi Kasei Thermylene® P7-40FG-0600 40% Glass Fiber Reinforced, Heat Stabilized Information provided by Asahi Thermofil |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C | 315 °F | ASTM D648 |
| A. Schulman ComAlloy Comtuf® 611 Nylon 6, Glass Reinforced, Impact Modified Data provided by the manufacturer, ComAlloy International Company.13% Glass Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been int.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C | 315 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| SABIC Innovative Plastics SABIC STAMAX 40YM243 PP SABIC® STAMAX 40YM243 is a 40% long glass fiber reinforced UV stabilized polypropylene. The glass fibers are chemically coupled to the PP matrix, resulting in high stiffness and strength. The IMDS .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C | 315 °F | Unannealed; ASTM D648 |