Polymer Property : Deflection Temperature at 8.0 MPa = 170 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 8.0 MPa	150 - 170 °C	302 - 338 °F	ISO 75-C
Raschig Group 6551 DAIP Diallyl Phthalate (DAP), Cast, Mineral Filler Glass-fiber reinforced diallyl isophthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensi..
Deflection Temperature at 8.0 MPa	150 - 170 °C	302 - 338 °F	ISO 75-C
Raschig Group EPOXIDUR® 3585 EP Epoxy, Molded, Glass Fiber Filler Glass-fiber reinforced and inorganically filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures, excel..
Deflection Temperature at 8.0 MPa	150 - 170 °C	302 - 338 °F	ISO 75-C
Raschig Group RALUPOL® 4566 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, good electrical values, excellent heat resistance, outstanding pourability. This product meets the allowed u..
Deflection Temperature at 8.0 MPa	75.0 - 170 °C	167 - 338 °F	Average value: 133 °C Grade Count:16
Overview of materials for Nylon 610, Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 610, Glass Reinforced". Each property range of values reported is minimum and maximum values of ap..
Deflection Temperature at 8.0 MPa	155 - 170 °C	311 - 338 °F	ISO 75 C
Vyncolit X658 Novolac Phenolic Glass fiber and mineral filled phenolic molding compound with excellent mechanical and thermal properties and a very good dimensional stability.USES: Complex precision parts.Information provided by ..
Deflection Temperature at 8.0 MPa	150 - 170 °C	302 - 338 °F	ISO 75 C
Vyncolit X681 Novolac Phenolic Glass fiber filled phenolic molding compound with excellent mechanical properties and a low coefficient of friction. Tribological compound with PTFE additive.USES: Water pump seals and self-lubrica..
Deflection Temperature at 8.0 MPa	150 - 170 °C	302 - 338 °F	ISO 75 C
Vyncolit 2950 W Novolac Phenolic Mineral and glass fiber filled phenolic molding compound with a very high strain to failure in flexure. UL listed.USES: Armature insulation.Information provided by Vyncolit, a Sumitomo Bak Group