Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 8.0 MPa | 110 - 130 °C | 230 - 266 °F | ISO 75-C |
Raschig Group 2568 AMC Glass fiber-reinforced polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, heat resistant up to 500°C for short time - usable for s.. |
|||
Deflection Temperature at 8.0 MPa | 110 - 130 °C | 230 - 266 °F | ISO 75-C |
Raschig Group MELOPAS® 2010 MF Melamine Organically and inorganically filled Melamine molding compound. Excellent surface hardness, good mechanical strength, good electrical properties. This product meets the allowed upper limits for heav.. |
|||
Deflection Temperature at 8.0 MPa | 110 - 130 °C | 230 - 266 °F | ISO 75-C |
Raschig Group MELOPAS® 6605 MP Melamine Cellulose reinforced Melamine molding compound. Very good electrical properties, excellent surface hardness, good mechanical strength and heat resistance, good wear and UV-stability, good gliding be.. |
|||
Deflection Temperature at 8.0 MPa | 110 - 130 °C | 230 - 266 °F | Injection and Compression; ISO 75 |
Raschig Group MELOPLAS® 150 MF Wood flour-reinforced MF molding compound in dark colors. High surface hardness, high mechanical strength, good electrical properties. Self-extinguishing (V-O/1,6 according to UL 94), UL-listed. Fr.. |
|||
Deflection Temperature at 8.0 MPa | 110 - 130 °C | 230 - 266 °F | Injection and Compression; ISO 75 |
Raschig Group MELOPLAS® 152 MF Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al.. |
|||
Deflection Temperature at 8.0 MPa | 110 - 130 °C | 230 - 266 °F | Injection and Compression; ISO 75-C |
Raschig Group MELOPLAS® 152.7 MF Cellulose-reinforced MF molding compound in white and colored shades. High surface hardness, very good UV stability, very good resistance to chemicals also to foodstuff ingredients, physiologically.. |
|||
Deflection Temperature at 8.0 MPa | 110 - 130 °C | 230 - 266 °F | Injection and Compression; ISO 75-C |
Raschig Group MELOPLAS® 181 MF Cellulose-reinforced, phenol-modified MF molding compound (MPF) in white and colored shades. High surface hardness, good electrical properties, good mechanical strength, high UV and heat resistanc.. |
|||
Deflection Temperature at 8.0 MPa | 110 - 130 °C | 230 - 266 °F | Injection and Compression; ISO 75-C |
Raschig Group MELOPLAS® 181.5 MF Cellulose-reinforced, phenol-modified MF molding compound (MPF) in white and colored shades. Very good electrical properties, high surface hardness, good mechanical strength, high UV and heat resis.. |
|||
Deflection Temperature at 8.0 MPa | 110 - 130 °C | 230 - 266 °F | Injection and Compression; ISO 75-C |
Raschig Group MELOPLAS® 182 MF Wood flour-reinforced and inorganically filled, phenol-modified MF molding compound (MPF) in dark colors. Improved dimensional stability and electrical properties as compared with MP 180, high surf.. |
|||
Deflection Temperature at 8.0 MPa | 110 - 130 °C | 230 - 266 °F | Injection and Compression; ISO 75-C |
Raschig Group MELOPLAS® 183 MF Cellulose-reinforced and inorganically filled, phenol-modified MF molding compound (MPF) in white and colored shades. Improved dimensional stability and electrical properties as compared with MP 18.. |
|||
Deflection Temperature at 8.0 MPa | 70.0 - 130 °C | 158 - 266 °F | Injection; ISO 75-C |
Raschig Group RALUPOL® 8601 UP Glass-fiber reinforced polyester molding compound. Mold shrinkage similar to phenolic moulding compounds, low post-shrinkage, good electrical values, excellent heat resistance, good mechanical stren.. |
|||
Deflection Temperature at 8.0 MPa | 70.0 - 130 °C | 158 - 266 °F | Injection; ISO 75-C |
Raschig Group RALUPOL® 8602 UP Glass-fiber reinforced polyester molding compound. Mold shrinkage similar to phenolic molding compounds, low post-shrinkage, good electrical values, excellent heat resistance, good mechanical streng.. |
|||
Deflection Temperature at 8.0 MPa | 110 - 130 °C | 230 - 266 °F | Injection and Compression; ISO 75-C |
Raschig Group MELOPLAS® 180 MF Wood flour-reinforced, phenol-modified MF molding compound (MPF) in dark colors. High surface hardness, good mechanical strength and electrical properties, good heat resistance. Self-extinguishing .. |