Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 8.0 MPa | 120 - 140 °C | 248 - 284 °F | ISO 75-C |
Raschig Group 5553 DAP Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona.. |
|||
Deflection Temperature at 8.0 MPa | 120 - 140 °C | 248 - 284 °F | Injection; ISO 75-C |
Raschig Group 5563 DAP Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona.. |
|||
Deflection Temperature at 8.0 MPa | 120 - 140 °C | 248 - 284 °F | Injection and Compression; ISO 75-C |
Raschig Group MELOPLAS® 2500 MF Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al.. |
|||
Deflection Temperature at 8.0 MPa | 120 - 140 °C | 248 - 284 °F | Injection and Compression; ISO 75-C |
Raschig Group MELOPLAS® 3025 MF Cellulose-reinforced and inorganically filled MF molding compound in white and colored shades. High surface hardness, good UV and heat stability, very good resistance to chemicals - also to foodstu.. |
|||
Deflection Temperature at 8.0 MPa | 120 - 200 °C | 248 - 392 °F | Average value: 165 °C Grade Count:8 |
Overview of materials for Diallyl Phthalate (DAP) Molding Compound, Short Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Diallyl Phthalate (DAP) Molding Compound, Short Glass Fiber Filled". Each property range of values repor.. |
|||
Deflection Temperature at 8.0 MPa | 120 °C | 248 °F | ISO 75-2 |
Hexion Bakelite™ 151733 Phenolic Formaldehyde Resin
(discontinued **) Phenolic molding compound, mainly organically filled, standard molding compound for normal stress.Application areas: Contact strips.Information provided by Bak AGBak AG became a part of Hexion in 20.. |
|||
Deflection Temperature at 8.0 MPa | 120 °C | 248 °F | ISO 75-1/-2 |
Lanxess Durethan® BKV 25 H2.0 LT 904040 Nylon 6, 25% Glass Fiber PA 6, injection molding grade, 25% glass fibers, good heat-ageing resistance, laser-weldable |
|||
Deflection Temperature at 8.0 MPa | 120 °C | 248 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® 2SV-30H black 9992 PA610-GF30 Product Description: GRILAMID XE 3976 black 9992 is a 30% glass fiber reinforced, heat stabilized polyamide 610 injection molding grade. This product is to a large extent based on renewable raw mate.. |
|||
Deflection Temperature at 8.0 MPa | 120 °C | 248 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® 2SV-30H nat PA610-GF30 Product Description: GRILAMID XE3976 natural 9992 is a 30% glass fiber reinforced, heat stabilized polyamide 610 injection molding grade. This product is to a large extent based on renewable raw mat.. |
|||
Deflection Temperature at 8.0 MPa | 120 °C | 248 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® BGZ-15 PA6-GF15 Information provided by EMS Grivory |
|||
Deflection Temperature at 8.0 MPa | 120 °C | 248 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® XE 4108 black 9992 PA612-GF50 Product description: Grilamid XE 4108 black 9992 is a 50% glass fiber reinforced, heat stabilized polyamide 612 injection molding grade. The main features of Grilamid XE 4108 are: low water absorpti.. |
|||
Deflection Temperature at 8.0 MPa | 120 °C | 248 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® XE 4108 nat PA612-GF50 Product description: Grilamid XE 4108 natural is a 50% glass fiber reinforced, heat stabilized polyamide 612 injection molding grade. The main features of Grilamid XE 4108 are: low water absorptiong.. |
|||
Deflection Temperature at 8.0 MPa | 120 °C | 248 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® BGZ-40 PA6-GF40 Product description: Grilon BGZ-40 is a normal viscosity, heat stabilized and impact modified PA 6 injection molding type with 40% glass fibers. Grilon BGZ-40 has the following important properties:.. |
|||
Deflection Temperature at 8.0 MPa | 120 °C | 248 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® XE 5051 (BGZ-40 FC) PA6-GF40 Product description: Grilon XE 5051 is a impact modified, heat stabilized PA 6 injection molding grade with 40% glass fiber reinforcement. Grilon XE 5051 has the following important properties: High.. |
|||
Deflection Temperature at 8.0 MPa | 120 °C | 248 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® XE 4192 black 9992 PA610-GF30 Information provided by EMS Grivory |
|||
Deflection Temperature at 8.0 MPa | 120 °C | 248 °F | ISO 75-1/-2 |
Lanxess Pocan® TP 740-201 000000 PBT + ASA, 20% Glass Fiber
(discontinued **) PBT+ASA, 20% glass fibers, injection molding, low tendency to warp, improved surface finish |
|||
Deflection Temperature at 8.0 MPa | 120 °C | 248 °F | ISO 75-2 |
Hexion Bakelite™ PF 2560 Phenolic Formaldehyde Resin, High Surface Quality, For Electrostatic Coating, UL Listed
&n Phenolic molding compound, inorganically/organically filled, average heat resistant, high surface quality, lower water absorption than PF 31, minimal distortion, UL listed molding compound 1.5 mm/V-.. |