- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 401 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 401 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | 120°C/h; ISO 75/1 |
| Polykemi AB SCANAMID 66 A12^ Nylon 66 Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | DIN 53461; ASTM D648 |
| Kolon SPESIN® KP213G15HI Multi Reinforced PBT Resin
(discontinued **) SPESIN® is a thermoplastic PBT resin with excellent thermal, mechanical and electrical properties. SPESIN® is widely used in industrial parts and especially in electrical-electronic parts.High hea.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ISO 75, ASTM D648 |
| Nilit Nilamid B G4 FR HF 20% Glass Fiber Reinforced, Flame Retardant PA6 Description: Nilamid B G4 FR HF is a NYLON 6 based flame retardant compound that does not contain any halogen or red phosphorous. It has a good overall mechanical performance, has an excellent price.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | DAM; ASTM D648 |
| DuPont Performance Polymers Zytel® 77G33L BK031 Nylon 612
(Unverified Data**) Zytel® 77G33L BK031 is a 33% glass fiber reinforced, black polyamide 612 resin for injection molding.Information provided by DuPont Performance Polymers |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ISO 75-1/-2 |
| Lanxess Durethan® BKV 215 W1 902176 Copolyamide, 15% Glass Fiber CoPA, injection molding grade, 15% glass fibers, elastomer-modified, weather-stabilized |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | DIN 53461; ASTM D648 |
| Kolon KOPA® KN133G15 G/F Reinforced Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ISO 75-1/-2 |
| Lanxess Durethan® BKV 115 000000 Copolyamide, 15% Glass Fiber CoPA, injection molding grade, 15% glass fibers, elastomer-modified, electroplateable, higher notched impact strength and also higher energy absorption under biaxial impact load than BKV 15, even in.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ISO 75-1/-2 |
| Lanxess Pocan® BF 4409 000000 PBT, 7% Glass Fiber PBT, 7% glass fibers, injection molding, flame retardant |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ISO 75/Bf |
| Solvay TECHNYL® C 52G4 MZ25 PA6, 25% mineral filler, DRY Description: TECHNYL® C 52G4 MZ25 is a 25% mineral reinforced melamine cyanurate flame retarded polyamide 6.This product is heat stabilized and is suitable for injection molding. This product is .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ISO 75-2 |
| Solvay Technyl® C216V15 15% Glass Filled Nylon 6 Information provided by Rhodia; Rhodia has been acquired by Solvay. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C @Thickness 3.20 mm |
401 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Ultem 1010A PEI (Asia Pacific) Transparent, high flow Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C @Thickness 3.20 mm |
401 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM 1010K PEI (Asia Pacific) Transparent, high flow Polyetherimide (Tg 217C). ECO Conforming. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C @Thickness 3.20 mm |
401 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM 2310EPR PEI (Europe-Africa-Middle East) 30% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. Resin is RoHS compliant. UL94 V0 listing. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics ULTEM AUR200G6 PEI (Europe-Africa-Middle East) The data listed in this data sheet are the lower specification limits, apart from the MFR, CTE, HDT at 1.8 MPa, Density, Tensile strain, Water Absorption, Thermal Conductivity and Shrinkage which ar.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics ULTEM HU1004 PEI High Temperature, Transparent, Polyetherimide Blend with Improved Ductility and Enhanced Hydrostability. For medical devices and pharmaceutical applications. Healthcare management of change, biocomp.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C @Thickness 3.20 mm |
401 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® 815F PBT+PET (Europe-Africa-Middle East) PBT+PET, 15% Glass, Mold Release, Heat Stabilized, For food contact applications |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C @Thickness 3.20 mm |
401 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON EX11402 PEI LNP* STAT-KON* EX11402 is a compound based on Polyetherimide resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics Noryl GTX GTX8110P PPE+PA (Europe-Africa-Middle East) GTX8110P is a glass filled extrudable Noryl GTX with low thermal conductivity, suitable for thermal breaksThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C @Thickness 3.20 mm |
401 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Noryl GTX GTX880 PPE+PA6 (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | 0.25 inch; ASTM D648 |
| PlastxWorld CEVIAN® B6528 40% GF PBT/ABS Alloy Glass fiber and mineral filled, low warpage and flame retarded PBT/ABS.Information provided by PlastxWorld Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 MK30HI 30% Mineral Reinforced, Impact Modified Nylon 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ISO 75 |
| Polyram RamLloy PFS301G6 ASA/PBT Alloy, 30% Glass Fiber 30% Glass fiber reinforced ASA/PBT alloy for injection molding applications.Information provided by Polyram. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ISO 75 |
| Polyram RamLloy PFS302G14 ASA/PBT Alloy, 14% Glass Fiber 14% Glass fiber reinforced ASA/PBT alloy for injection molding applications.Information provided by Polyram. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® E53 NC010 Nylon 66 Unreinforced High Viscosity Polyamide 66 Information provided by DuPont Performance Polymers |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Be |
| Eurostar Starflam BFR430A PA6, Glass Fiber Filled, Flame Retardant, Injection Molded Starflam BFR430A is a Flame Retardant, Glass Fiber Reinforced Polyamide 6, Injection Molding ResinInformation provided by Eurostar. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ISO 75-2/B |
| Cathay PA56 Renewable Engineering Polyamide, DAM Cathay engineering polyamides contain 26-100% renewably sourced material. Advantages: Operates at similar conditions to PA66; Suitable for injection, compounding and extrusion; Stable mechanical pr.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ISO 75 |
| BASF Ultramid® 1310-11 NF2001 PA66 (Dry) Ultramid 1310-11 NF2001 is a controlled crystallization, fast cycling PA6/6 which provides extremely fast cycle times and improved productivity over Ultramid 1000. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ISO 75 |
| BASF Ultramid® NBX-0025 NF2001 PA66 (Dry) Ultramid NBX-0025 NF2001 is a specialty, unfilled PA6/6. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ISO 75 |
| BASF Ultramid® 1003-2 NF2002 PA66 (Dry) Ultramid 1003-2 NF2002 is a general purpose, heat stabilized nylon 6/6. |
|||