- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 383 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 383 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | ISO 75/2Bf |
| Radici Radilon® AHS (dry) Nylon 66 General purposeInformation provided by Radici group. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C @Thickness 3.20 mm |
383 °F @Thickness 0.126 in |
ASTM D648 |
| Covestro Apec® DP9-9373 High-Heat Polycarbonate, General Purpose, UV-Stabilized
(discontinued **) Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® 101F BKB009 Nylon 66
(Unverified Data**) Zytel® 101F BKB009 is an internally lubricated polyamide 66 resin for injection molding. It was developed for fast cycles and high productivity.Information provided by DuPont Performance Polymers |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® 103FHS BKB009 Nylon 66
(Unverified Data**) Zytel® 103FHS BKB009 is a heat stabilized, internally lubricated polyamide 66 resin for injection molding. It was developed for fast cycles and high productivity.Information provided by DuPont Perf.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | ISO 75-1/-2 |
| Lanxess Durethan® BM 25 FN20 700350 Nylon 6, 25% Mineral PA 6, injection molding grade, 25% mineral, UL94V-2 off 0.75 mm, max. temp. glow wire test:960°C off 0.8 mm, free from halogen |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | |
| LATI Latamid 68 H2-V0 PA6/PA66 copolymer, Heat Stabilized, Flame Retardant PA6/PA66 copolymer (PA6/PA66) based compound. Heat stabilized. UL94 V-0 classified, halogens-based flame retardants and red phosphorous free. Good surface appearance.Availability: Africa & Middle Ea.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics Ultem 1010KM PEI (Asia Pacific) Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics Ultem 1010KM PEI (Europe-Africa-Middle East) Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics ULTEM ATX3562R PEI+PCE (Europe-Africa-Middle East) 50% Glass fiber and mineral filled, high flow Polyetherimide blend with internal mold release and enhanced dimensional stability. RoHS compliant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics ULTEM AUT195 PEI+PCE High flow Polyetherimide blend for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperature of 195C (SABIC test method). |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C @Thickness 3.20 mm |
383 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON RX08408 PA 66 LNP* STAT-KON* RX08404 is a compound based on Nylon 66 containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C @Thickness 3.20 mm |
383 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL GTX GTX973 PPE+PA (Europe-Africa-Middle East) NORYL GTX973 is a material especially designed for electrostatic painting and powder coating applications. The material combines high heat resistance with impact and conductivity in a unique way. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics Noryl GTX GTX977 PPE+PA66 (Asia Pacific) Noryl GTX GTX977 resin is a mineral reinforced conductive Noryl GTX with a improved CTE (7) with a balanced performance of Impact and stiffness. (developmental grade : EXNX0074)This data was supplie.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics ULTEM AUT200M PEI (Europe-Africa-Middle East) Transparent high flow Polyetherimide (Tg 217C) with internal mold release.. Very low outgassing and plateout, for automotive lighting applications where highly metallized, reflective surfaces are re.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | >= 195 °C @Thickness 3.20 mm |
>= 383 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 225 30% Glass Fiber Reinforced Ionomer / Nylon Alloy DescriptionFormion® FI 225 is an injection molding grade, 30% glass fiber reinforced Ionomer / Nylon alloy, which has been formulated for high scratch resistance, heat resistance and high stiffness.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | >= 195 °C @Thickness 3.20 mm |
>= 383 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 225 30% Glass Fiber Reinforced Ionomer / Nylon Alloy DescriptionFormion® FI 225 is an injection molding grade, 30% glass fiber reinforced Ionomer / Nylon alloy, which has been formulated for high scratch resistance, heat resistance and high stiffness.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | >= 195 °C @Thickness 3.20 mm |
>= 383 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 225 30% Glass Fiber Reinforced Ionomer / Nylon Alloy DescriptionFormion® FI 225 is an injection molding grade, 30% glass fiber reinforced Ionomer / Nylon alloy, which has been formulated for high scratch resistance, heat resistance and high stiffness.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | ISO 75-1/-2 |
| DSM Arnite® BM4 240 (PBT+PET)-MD20 20% Mineral Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | ISO 75-1/-2 |
| DSM Arnite® TM4 440 (PBT+PET)-MD20 20% Mineral Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | ISO 75-1/2 |
| Eurotec® Tecodur® PB70 GR20 NL IH PBT 20% glass fiber reinforced, impact modified Excellent stiffness and hardnessGood mechanical strengthGood creep and fatigue behaviorVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | ASTM D648 |
| Clariant Renol PA113C Nylon 66, Molybdenum Disulfide Lubricated Data provided by Clariant Masterbatches |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | ISO 75-1/2 |
| Eurotec® Tecomid® NB40 NL XA 20 PA 6 unreinforced, UL94 V0 Excellent stiffness/toughness balanceHigh mechanical strengthVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance and low frictionVery good.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | ISO 75-2 |
| BASF Ultradur® S 4090 GM11 5/5% Glass/Mineral Filled PBT Description: Is a PBT + ASA, injection-molding grades reinforced with 5% glass fiber/mineral, for laminar parts with high demands on dimensional stability and low warpage, e.g. lids, ventilation gri.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | ISO 75 |
| BASF Ultramid® 8260 HS PA6 (Dry) |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | ISO 75-2/B |
| Ascend Performance Materials Vydyne® 66R Nylon 66, General Purpose, high viscosity, DAM Vydyne® 66R is a high-viscosity, heat-stabilized PA66 resin suitable for injection-molding and extrusion applications. It is available in natural color only. Vydyne 66R resin offers high strength, .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | ASTM Test |
| BASF Ultramid® B3M6 30% Mineral Filled PA6 (Dry) Ultramid B3M6 is a 30% mineral reinforced injection molding PA6 grade for industrial items requiring high impact strength and very high dimensional stability, excellent laser markability. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® 103FHS BKB009 Nylon 66
(Unverified Data**) Unreinforced Heat Stabilized Polyamide 66 Zytel 103FHS BKB009 is a heat stabilized internally lubricated polyamide 66 resin for injection molding. It was developed for fast cycles and high productiv.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | >= 195 °C @Thickness 3.20 mm |
>= 383 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 225 30% Glass Fiber Reinforced Ionomer / Nylon Alloy DescriptionFormion® FI 225 is an injection molding grade, 30% glass fiber reinforced Ionomer / Nylon alloy, which has been formulated for high scratch resistance, heat resistance and high stiffness.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | ISO 75 |
| BASF Ultramid® B3M6 BK60564 30% Mineral Filled PA6 (Dry) ultramid B3M6 BK60564 is a 30% mineral reinforced, pigmented black injection molding PA6 grade for industrial items requiring high impact strength and very high dimensional stability, excellent lase.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | |
| LATI Latiblend 6252 H2 G/30 PA6/PP Homopolymer Blend based on Polyamide 6 (PA6) / Polypropylene homopolymer (PPh). Heat stabilized. Glass fibers. Good thermal properties.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; No.. |
|||