- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 338 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 338 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ISO 75, ASTM D648 |
| Nilit Nilitop BT FR C3 Unfilled, Flame Retardant PBT Description: Nilitop BT FR C3 is an unfilled, flame retardant PBT with halogens. The flame retardant does not contain PBB and PBDE, so it is compliant with the WEEE directive.Key characteristics: Go.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ISO 75 |
| Nilit FRIANYL B63 K Nylon 6 for injection molding Nylon 6 for injection molding, specially formulated for knobs.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ISO 75 |
| Nilit FRIANYL B63 KLZ Nylon 6 for injection molding Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | DIN 53461 |
| Qualchem Danamid FE Polyamide 6 Standard type polyamide with good flowing propertiesInformation provided by Qualchem Zrt. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | DIN 53461 |
| Qualchem Danamid FEL0 Polyamide 6 Flame retardant, with halogens (V-0)Information provided by Qualchem Zrt. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | Unannealed; ISO 75-2/B |
| PolyOne Bergamid™ B700 UF V2 Polyamide 6 (Nylon 6) Information provided by PolyOne |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ISO 75/Method Bf |
| Premix Thermoplastics PRE-ELEC® PPE 1462
(discontinued **) PRE-ELEC PPE 1462 is a conductive thermoplastic compound based on modified polyphenylene ether (PPE). Conductivity is achieved by using special conductive carbon black. In addition to a low electric.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ASTM D648 |
| Asahi Kasei Tenac® FA405 Acetal Homopolymer, Low Friction Grade
(discontinued **) Contains fluoropolymer and lubricant; excellent friction and wear on plastics.Applications: Bearings for printers, cams, gears.This product is not a part of the standard product line dated 2003. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ASTM D648 |
| LG Chemical Lupox® GP-1006F General Purpose PBT, Unreinforced, Flame Retardant, Non-Bleed LUPOX semi-crystalline thermoplastic PBT resins exhibit properties including high strength, rigidity and good resistance to fatigue and creep at elevated temperatures. Furthermore, LUPOX resins sho.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ISO 75-1, -2 |
| Lanxess Pocan® B 5220 XF 000000 PBT, 20% Glass Spheres PBT, 20% glass spheres, injection molding, improved flowability, improved impact strength, low tendency to warpInformation provided by LANXESS. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | |
| LATI Latamid 66 H2PX-V0 PA 66, Heat Stabilized, Flame Retardant Polyamide 66 (PA66) based compound. Heat stabilized. Toughened. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free. Availability: Africa & Middle East; Asia Pacific; Europe; Latin .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | |
| LATI Latan 13 K/30 POM, 30% Carbon Fiber Reinforced Polyoxymethylene (POM) based compound. Carbon fiber. Medium viscosity. Good tribological properties.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | |
| LATI Laticonther 82 CP1/800 PA12 High thermal conductivity product based on Polyamide 12 (PA12). Special fillerAvailability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Indus.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C @Thickness 3.20 mm |
338 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP IBP34 PA6.12 LNP* LUBRICOMP* IBP34 is a compound based on Nylon 6/12 containing 20% Glass Bead, 15% PTFE/Silicone. Added features include: Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C @Thickness 6.40 mm |
338 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Infino® GP-5000 PBT, Unreinforced General PBT material that can be used for connectorsInformation provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP Thermocomp WB006 PBT LNP* Thermocomp* WB006 is a compound based on Polybutylene Terephalate resin containing Glass Bead.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ISO 75-1/-2 |
| Unitika A1025NO PA6, Flame Retardant, Dry Information provided by Unitika Ltd. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ISO 75-1,-2 |
| Topas Advanced Polymers TOPAS® 6017S-04 Cyclic Olefin Copolymer (COC) TOPAS® 6017S-04 is an injection molding grade with a high heat distortion temperature (170°C) and exceptional dimensional stability. It is a glass-clear amorphous polymer with outstanding moisture.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | DIN 53461 |
| Polyram RamSter PF100 PBT, General Purpose General purpose, high viscosity PBT for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ISO 75-1/-2 |
| Unitika A1030JR PA6, Dry Information provided by Unitika Ltd. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ISO 75-1/-2 |
| DSM Akulon® K240-HP (Dry) Impact Modified Nylon 6 (North America) Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ISO 75-1/-2 |
| DSM Akulon® K240-HP Impact Modified Nylon 6 (European Grade) (Dry) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ISO 179 |
| CP-Polymer-Technik Wellamid® 6000 GS 20 HWCP 20% Glass Sphere Filled Nylon 6, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® BS V0 PA6 Product description: Grilon BS V0 is an unreinforced, normal viscosity, self-extinguishing PA6 injection molding grade. Grilon BS V0 has the following important properties: Halogen and phosphorous-f.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ASTM D648 |
| Beijing Chemical Industry KAIFA® 301-G0F PBT Resin Flame retardant, good flow, low bleedingInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ASTM D648 |
| Beijing Chemical Industry KAIFA® 201-G0R PBT Resin Good flow and toughnessInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C @Thickness 3.20 mm |
338 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Ultem ATX103R PEI+PCE (Asia Pacific) 30% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing in recognized colors.This data was supplied by SABIC-IP for the Asia Pacif.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ISO 75-1/-2 |
| DSM Arnite® T06 204 XL PBT Low Viscosity, Injection Molding, Low outgassing |
|||