- HOME
- POLYMER SEARCH
- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 261 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 261 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | ASTM D648-95 |
| Multibase Multi-Pro® 2005 M 20% Mica Filled Polypropylene Multi-Pro 2005 M is a mica reinforced polypropylene compound with high stiffness and flex strength. Its high heat resistance lends itself to replace engineered plastics at moderate cost.Data provid.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C @Thickness 6.35 mm |
261 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| PolyOne LubriOne™ PC-000/10T Polycarbonate (PC) LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics GELOY HRA170D ASA+PC (Europe-Africa-Middle East) GELOY HRA170D resin is a PC-ASA blend with permanent antistatic behavior. It is typically used in applications that require antidust properties and high impact retention. Geloy HRA170D resin is typi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C @Thickness 3.20 mm |
261 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® EX7631T PC EX7631T is a high UVA content homopolymer polycarbonate product intended for use as a cap layer for polycarbonate sheet extrusion. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics Lexan® ML6412 PC Copolymer ML6412 is an impact modified PC resin with non-brominated, non-chlorinated flame retardant system. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | ASTM D648 |
| PolyOne Lubri-Tech™ ATH-000/05M Acetal Homopolymer - 5% MoS2
(discontinued **) Data provided by PolyOne. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C @Thickness 6.40 mm |
261 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical LUPOL HF5157Z PP+Rubber+MF, High Flow and Stiffness, High Impact Description: Injection Molding, PP+Rubber+MF, High Flow and Stiffness, High Impact, Good PaintabilityApplication: Automotive Exterior (Slim wall Bumper Fascia)Information provided by LG Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | Annealed; ASTM D648 |
| Solvay Specialty Polymers Solef® 460/461 Polyvinylidene Fluoride (PVDF) Solef® 460/461 PVDF homopolymer has high melt viscosity and is typically processed by extrusion.Features: High Viscosity; HomopolymerAdditional Properties: Crystallization Heat - ASTM D3418 46.0 .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C @Thickness 3.20 mm |
261 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® IQ357U PBT+PC Valox* Resin IQ357U: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified and UV stabilized resin. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | ASTM D648 |
| SPS Guang Zhou FILLMAâ„¢ 5002F30C Mineral Filled Polypropylene Characteristic: 30%wt of Sulfate Calcium filled, low odor, good glossApplications: Household appliance parts, office suppliesInformation Provided by SPS (Guang Zhou) Ltd. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP Stat-kon ZEL34XXC PPE+PS (Europe-Africa-Middle East) LNP* Stat-kon* ZEL34XXC is a compound based on PPE+PS Blend resin containing Carbon Fiber, PTFE. Added features include : Electrically Conductive , Internally Lubricated.This data was supplied by S.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C @Thickness 3.20 mm |
261 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Thermocomp FF008L PE LNP* Thermocomp* FF008L is a compounding based on Polyethylene containing glass fiber. Added characteristics include Low Extractible.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C @Thickness 6.40 mm |
261 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Infino® WP-1069 PC/ABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | ISO 75-1,-2 |
| Topas Advanced Polymers TOPAS® 5013S-04 Cyclic Olefin Copolymer (COC) TOPAS® 5013S-04 is a high flow injection molding grade with a 130°C heat distortion temperature. It is a glass-clear amorphous polymer with outstanding moisture barrier, chemical resistance, high .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | ASTM D648 |
| Total PPH 3720WZ Polypropylene, Injection Molding Grade High flow reactor injection molding homopolymerHigh Flow - FINA 3720WZ has high flow characteristics that result in ease of filling thin wall parts.Nucleation - FINA 3720WZ is nucleated to provide f.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | ASTM D648 |
| Total PPH 3825WZ Polypropylene, Injection Molding Grade Easy flow injection molding homopolymerNucleation - FINA 3825WZ is engineered with nucleation to provide fast cycle time and improve contact clarity in thin wall multi-cavity molds.Antistat - FINA 3.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | ASTM D648 |
| Total PPH 3925WZ Polypropylene, Injection Molding Grade Easy flow injection molding homopolymerNucleation - FINA 3925WZ is nucleated to provide fast cycle time and improve contact clarity.Antistat - FINA 3925WZ contains an antistat that will help protect.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | ISO 75-1,-2 |
| Covestro Bayblend® M850 XF PC/ABS Blend Main characteristics:• High toughness even at low temperatures• High dimensional accuracy and stability• Good paintability• Good flowabilityGrade characteristics:• Injection molding• Eas.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | ISO 75-1/-2 |
| Covestro Bayblend® T90 MF-20* Polycarbonate + ABS, Mineral Filled Developmental productInjection molding grade20 % mineral filledvery good flowreduced coefficient of thermal dilatationtensile modulus = 5200 MPaVicat/B 120 = 130 °CPreprocessingMax. Water content |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | ISO 75-1/-2 |
| Covestro Bayblend® W85 XF* Polycarbonate + ASA Developmental product(PC+ASA) blendinjection molding grade with improved weather resistanceoptimized heat ageing stabilityhigh heat resistanceVicat/B 120 = 132 °CPreprocessingMax. Water content |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | ASTM D648 |
| Entec Hypro™ PP-HP35NS Homopolymer, 35 Melt Flow, Nucleated, Anti-stat This product is intended for thin-wall injection molding applications such as caps and closures, food containers and consumer products that require high stiffness.Information provided by Entec |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | ISO 75-1,-2 |
| Covestro Makrolon® ET UV130 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• PC/UV absorber concent.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 - 131 °C | 261 - 268 °F | |
| Addcomp PRIEX® Ionomer 42101 PP homopolymer Ionomers will be used toStrengthen rigidity and hardness while maintaining impact resistance in polyolefinsMaintain adhesion even under contaminated conditions especially in fatty substratesReduce t.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | ASTM D648 |
| Aclo Accutech Polypropylene Copolymer HP0334W30L Wollastonite Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | ASTM D648 |
| Adell EQ-14 Homopolymer Polypropylene, 20% Mica Filled Data provided by Adell Plastics, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C @Thickness 3.20 mm |
261 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® CH6410 PC+ABS CH6410 is a high heat, impact modified PC resin, with nonbrominated, nonchlorinated flame retardant system. Limited colors only. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP STAT-KON MFD02 PP LNP* STAT-KON* MFD02 is a compound based on Polypropylene resin containing 10% Glass Fiber. Added features of this material include: Electrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | ASTM D648 |
| Ineos H13Z-00 Polypropylene Homopolymer
(discontinued **) Suggested fabrication methods: Injection moldingFeatures: Nucleated, AntistaticTypical applications: Packaging, Consumer productsComplies with FDA specification, Title 21, CFR 177.1520.Typical prope.. |
|||