- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 246 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 246 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C @Thickness 3.20 mm |
246 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® EXCY0025 PC+ABS Recyle Material with PC+ABS+EXL recycle for good low temperature impact performance. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 246 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPHC T8040 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 246 °F | unannealed; ASTM D648 |
| Phillips 66 COPYLENE® CH120LN Polypropylene, Homopolymer, Injection Molding, Antistat/Lube COPYLENE™ CH120LN is designed for general purpose injection molding applications with anti-static and nucleation. Applications: Food Containers, Housewares, Closures.Information provided by Phillip.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 246 °F | unannealed; ASTM D648 |
| Phillips 66 COPYLENE® CH350LN Polypropylene, Homopolymer, High Flow, Nucleated, Lube, Injection Molding COPYLENE™ CH350LN is designed for general purpose injection molding applications with anti-static, nucleation and controlled rheology. Applications: Food Containers, Housewares, Closures.Informatio.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 246 °F | ASTM D648-97 |
| Ipiranga Petrochem PH 3515 Polypropylene The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 246 °F | ASTM D648 |
| LyondellBasell Astryn 75F4-4 Polypropylene Copolymer, 40% Talc Key Features: conventional melt flow, high modulus, mineral-filled polypropylene copolymer, high strength, high stiffness, good aestheticsApplications: small appliances, electrical components, house.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C @Thickness 6.40 mm |
246 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical LUPOY GN5007FL PC/ABS, Halogen Free Flame Retardant, Heat Resistance Description: Injection Molding, PC/ABS, Halogen Free Flame Retardant, Heat Resistance, High FlowApplication: IT/OA, Electric & Electronic Housing and ComponentsCAS: 103598-77-2, 9003-56-9 and 181028.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 246 °F | ISO 75-1,-2 |
| Inno-Comp INNOPOL® CS 1-1240 42% Chalk-Filled Polypropylene Homopolymer INNOPOL® CS 1-1240 is a 42% chalk –filled polypropylene homopolymer compound /PP-H KD42 (ISO 1043)/. This grade is available in natural and custom colored form.INNOPOL® CS 1-1240 is devel.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 246 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics Xenoy® X4830 PBT+PC Xenoy X4830 is a hydrostable, high modulus, low temperature ductile PC/PBT blend. Furthermore, this resin provides high chemical resistance, very low creep, low CTE, excellent fatique and high heat .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 246 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics Xenoy® X4830 PBT+PC (Asia Pacific) Xenoy X4830 is a hydrostable, high modulus, low temperature ductile PC/PBT blend. Furthermore, this resin provides high chemical resistance, very low creep, low CTE, excellent fatique and high heat .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 246 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics Xenoy® X4830 PBT+PC (Europe-Africa-Middle East) Xenoy X4830 is a hydrostable, high modulus, low temperature ductile PC/PBT blend. Furthermore, this resin provides high chemical resistance, very low creep, low CTE, excellent fatique and high heat .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C @Thickness 3.20 mm |
246 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics XYLEX HX7509HP PC+POLYESTER Medium flow, polycarbonate/Polyester alloy; contains mold release. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), fo.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C @Thickness 3.20 mm |
246 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics XYLEX X7509HP PC+POLYESTER PC+Polyester alloy. Houseware applications. USA/Europe Food contact. this grade will no longer be supported with biocompatibility information and should not be used for medical applications which r.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C @Thickness 3.20 mm |
246 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics XYLEX X7509HP PC+POLYESTER (Asia Pacific) PC+Polyester alloy. Houseware applications. USA/Europe Food contact. this grade will no longer be supported with biocompatibility information and should not be used for medical applications which r.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C @Thickness 3.20 mm |
246 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP AX04518 ABS LNP* THERMOCOMP* AX04518 is a compound based on ABS resin containing proprietary filler(s). |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C @Thickness 6.40 mm |
246 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® V3900WX PBT+PC PBT/PC blend - Unreinforced - Flame Retardant. This is a UV-stabilized grade designed for outdoor enclosure applications requiring UL 746C F1 weatherability performance. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C @Thickness 3.20 mm |
246 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Xylex X7529 PC+POLYESTER (Europe-Africa-Middle East) PC+ POLYESTER unreinforced alloy developed for optical or lense market. Good flow with good impact and excellent optical quality. UV 400nm block.This data was supplied by SABIC-IP for the Europe-Afr.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C @Thickness 3.20 mm |
246 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Xylex X7529OQ PC+POLYESTER (Europe-Africa-Middle East) PC+ POLYESTER unreinforced alloy developed for optical or lense market. Good flow with good impact and excellent optical qualityThis data was supplied by SABIC-IP for the Europe-Africa-Middle East r.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 246 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 3726 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 246 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 3726 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 246 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 3726 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 246 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 3726 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 246 °F | ASTM D648 |
| Aclo Accutech Polypropylene Homopolymer HP0334M30L Mica Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 246 °F | ASTM D648 |
| Ashley Polymers Ashlene® 525 Nylon 66 High impact Nylon 66 with good stiffness for injection molding.Data provided by the manufacturer |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 246 °F | ASTM D648 |
| Ashley Polymers Ashlene® 525-B2 Nylon 66 A high impact modified lubricated nylon resin containing well dispersed carbon black for maximum resistance to weathering.Data provided by the manufacturer |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 246 °F | ASTM D648 |
| Ashley Polymers Ashlene® D870, D870L, Transparent Amorphous Nylon D870 = Transparent Amorphous Nylon for Injection Molding, Unlubricated. D870L = Transparent Amorphous Nylon for Injection Molding, Lubricated.Data provided by the manufacturer |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 246 °F | ASTM D648 |
| A. Schulman ComAlloy Hiloy® 243 SAN, Glass Reinforced Data provided by the manufacturer, ComAlloy International Company.30% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 246 °F | ASTM D648 |
| Aclo Accutech Polyethylene HD0234G10UVL High Density Glass Reinforced UV Stabilized |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 246 °F | ASTM D-648 |
| Bapolene® 4012F Polypropylene, Compounding/Extrusion Grade Bapolene PP4012F is a homopolymer polypropylene (flake) that meets US FDA 21CFR177.1520.Applications: Compounding, and filled or color concentrate applications.Bapolene® and Bapolan® are registere.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C @Thickness 3.20 mm |
246 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Xylex X7529OQ PC+POLYESTER (Asia Pacific) PC+ POLYESTER unreinforced alloy developed for optical or lense market. Good flow with good impact and excellent optical qualityThis data was supplied by SABIC-IP for the Asia Pacific region. |
|||